OBC

3 products from 3 makers. Most documented first. Select a column to sort, a product to see its values, print settings and documents.

Key

How the numbers are worked out

Kexcelled THE K8 OBCStrength XY, MPa10Strength Z, MPa10Modulus XY, GPa0.2Charpy notched, kJ/m²15Nozzle, °C210–250Bed, °C90–110Chamber, °C—Drying, °C, h—

Kexcelled THE K8 OBCKexcelled

Published values

PropertyAs publishedConditionsOn the Overview
Kexcelled, THE K8 OBC Technical Data Sheet21 valuesUnless a row says otherwise: printed specimen
print settingsinfill=100%; printer=BambuLab X1C; nozzle=220℃; bed=55℃; speed=100mm/s; shell=1.2mm; infill angle=45°
Tensile modulus XY200~400 Mpap. 2: Emodulus (Mpa), X,Y-axisISO 527in the median
Tensile modulus Z200~300 Mpap. 2: Emodulus(Mpa) (MECHANICAL PROPERTIES|TENSILE TEST / Printed horizontal Z,X-axis)
ISO 527As the sheet prints it: ISO 527; stress range=1~3MPa; reference only
in the median
Tensile modulus XZ200~400 Mpap. 2: Emodulus(Mpa) (MECHANICAL PROPERTIES|TENSILE TEST / Printed horizontal X,Z-axis)ISO 527not in the median: measured on a bar in another orientation
Tensile strength (yield or break not stated) XY10~15 Mpap. 2: Tensile strength (Mpa), X,Y-axisISO 527in the median
Tensile strength (yield or break not stated) Z10~14 Mpap. 2: Tensile strength(Mpa) (MECHANICAL PROPERTIES|TENSILE TEST / Printed horizontal Z,X-axis)ISO 527in the median
Tensile strength (yield or break not stated) XZ11~15 Mpap. 2: Tensile strength(Mpa) (MECHANICAL PROPERTIES|TENSILE TEST / Printed horizontal X,Z-axis)ISO 527not in the median: measured on a bar in another orientation
Elongation at break XY210~220 %p. 2: Elongation at break (%), X,Y-axisISO 527in the median
Elongation at break Z50~160 %p. 2: Elongation at break(%)ISO 527in the median
Flexural modulus XY300~400 Mpap. 2: Flexural modulus (Mpa), X,Y-axisISO 178in the median
Flexural modulus Z200~300 Mpap. 2: Flexural modulus(Mpa) (MECHANICAL PROPERTIES |FLEXURAL TEST / Printed horizontal Z,X-axis)ISO 178in the median
Flexural modulus XZ300~400 Mpap. 2: Flexural modulus(Mpa) (MECHANICAL PROPERTIES |FLEXURAL TEST / Printed horizontal X,Z-axis)ISO 178not in the median: measured on a bar in another orientation
Flexural strength XY11~16 MPap. 2: Maximum force (Mpa), X,Y-axisISO 178in the median
Flexural strength Z9~13 MPap. 2: Maximum force (Mpa), Z,X-axisISO 178in the median
Flexural strength XZ13~16 MPap. 2: Maximum force (Mpa), X,Z-axisISO 178not in the median: measured on a bar in another orientation
Charpy impact strength XY15~20 KJ/m2p. 2: Notch impact strength (KJ/m2), X,Y-axisISO 179notchednot in the median: the only value of its test, shown as published
Charpy impact strength Z3~6 KJ/m2p. 2: Notch impact strength (KJ/m2), Z,X-axisISO 179notchednot in the median: measured on a bar in another orientation
Charpy impact strength XZ34~48 KJ/m2p. 2: Notch impact strength (KJ/m2), X,Z-axisISO 179notchednot in the median: measured on a bar in another orientation
HDT at 0.45 MPa58℃p. 1: Heat deflection temperature(HDT)specimen not stated,
ISO 75As the sheet prints it: ISO 75; 0.45MPa; heating=120℃/h
print settings not stated
Vicat softening temperature98℃p. 1: Vicat softening temperature(VST)specimen not stated,
ISO 306As the sheet prints it: ISO 306; 10N; heating=120℃/h
print settings not stated
Density0.9~0.92g/cm3p. 1: densityspecimen not stated, ISO 1183print settings not stated
Melt mass-flow rate2~8g/10minp. 1: Melt flow rate (MFR)specimen not stated,
ISO 1133As the sheet prints it: ISO 1133; mass=2.16kg
tested at 190℃print settings not stated

Print settings

Nozzle
210–250 °Cown data sheet
Bed
90–110 °Cown data sheet
Heated chamber
not stated
Drying
not stated
Hardened nozzle
not stated
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

Fillamentum OBC 905Data sheet shared with Dow EVOLV3D OBCStrength XY, MPa14Strength Z, MPa11Modulus XY, GPa—Charpy notched, kJ/m²—Nozzle, °C195–215Bed, °C90–105Chamber, °CnoneDrying, °C, h80≥ 2 h

Fillamentum OBC 905Fillamentum

Data sheet shared with Dow EVOLV3D OBC: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Fillamentum, OBC 90521 valuesUnless a row says otherwise: printed specimen
Tensile yield strength XY14 MPap. 1: Tensile strength at yieldASTM D1708in the median
Tensile yield strength Z11 MPap. 1: Tensile strength atASTM D1708in the median
Tensile break strength XY14 MPap. 1: Tensile strength at breakASTM D1708not in the median: another value of this product is in it
Tensile break strength Z12 MPap. 1: Tensile strength at break (Z-axis)ASTM D1708not in the median: another value of this product is in it
Elongation at break XY700 %p. 1: Elongation at breakASTM D1708in the median
Elongation at break Z480 %p. 1: Elongation at break (Z-axis)ASTM D1708in the median
Elongation at yield XY10 %p. 1: Elongation at yieldASTM D1708listed under other properties
Elongation at yield Z24 %p. 1: Elongation at yield (Z-axis)ASTM D1708listed under other properties
Flexural modulus XY244 MPap. 1: Flexural modulusASTM D790in the median
Flexural modulus Z217 MPap. 1: Flexural modulus (Z-axis)
ASTM D790As the sheet prints it: ASTM D790; strain=1%
in the median
Flexural strength XY7.8 MPap. 1: Flexural strengthASTM D790in the median
Flexural strength Z6.8 MPap. 1: Flexural strength (Z-axis)
ASTM D790As the sheet prints it: ASTM D790; strain=5%
in the median
Izod impact strength XY347 J/mp. 1: Izod impact strengthASTM D256notchednot in the median: in J/m
Izod impact strength XY34.3 kJ/m2p. 1: Izod impact energyASTM D256notchednot in the median: to another standard
Izod impact strength Z352 J/mp. 1: Izod impact strength (Z-axis)
ASTM D256As the sheet prints it: ASTM D256; notched
notched		not in the median: in J/m
Izod impact strength Z43.1 kJ/m2 kJ/m²p. 1: Izod impact energy (Z-axis)ASTM D256notchednot in the median: to another standard
Hardness53 Shore Dp. 1: HardnessISO 7619in the median
Glass transition temperature-13 °Cp. 1: Glass transition temperatureISO 11357
Vicat softening temperatureheld back: the sheet's unit or table layout is unclearheld backp. 1: Vicat softening temperature - ISO 306 Temperature resistance Chemical properties Typical Valueno standard stated
Melting temperature130 °Cp. 1: Melting temperatureISO 11357
Density0.905 g/cm3p. 1: Material densityISO 1183
Dow, EVOLV3D OBC1 value
Melt mass-flow rate9.5 g/10 minp. 1: Melt Flow Rate
ASTM D1238As the sheet prints it: ASTM D1238; 2.16 kg
tested at 230 C

Print settings

Nozzle
195–215 °Cown data sheet
Bed
90–105 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
optional: 80 °C for ≥ 2 hown data sheet
Hardened nozzle
not stated
Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 5 documents

What the maker says (3)
Chemicals and environment (1)
Dow EVOLV3D OBCData sheet shared with Fillamentum OBC 905Strength XY, MPa14Strength Z, MPa11Modulus XY, GPa—Charpy notched, kJ/m²—Nozzle, °C160–200Bed, °C60–100Chamber, °CnoneDrying, °C, h80≥ 2 h

Dow EVOLV3D OBCDow

Data sheet shared with Fillamentum OBC 905: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Dow, EVOLV3D OBC6 valuesUnless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated14 MPap. 1: Tensile yield strengthASTM D1708not in the median: set apart (never used to pass), test bar not described as printed
Tensile break strength orientation not stated14 MPap. 1: Tensile break strengthASTM D1708not in the median: another value of this product is in it
Elongation at break orientation not stated>700 %p. 1: Elongation at breakASTM D1708not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated10 %p. 1: Elongation at yieldASTM D1708listed under other properties
Melting temperature130 °Cp. 1: Melting temperatureprinted specimen, DSC
Density0.905 g/ccp. 1: DensityASTM D792

Print settings

Nozzle
160–200 °Cown data sheet
Bed
60–100 °Cown data sheet
Heated chamber
not requiredFillamentum OBC 905's data sheet, shared
Drying
optional: 80 °C for ≥ 2 hFillamentum OBC 905's data sheet, shared
Hardened nozzle
not stated
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (5)
  • BenefitsChemical resistant – Resistant to common solvents enabling new applicationsDow, EVOLV3D OBCp. 1
  • BenefitsLow Density – enabling light weight, durable partsDow, EVOLV3D OBCp. 1
  • Warping and shrinkageThis material demonstrates significantly improved warpage and printability for a polyolefin, enabling lightweight, durable parts with excellent chemical resistance.Dow, EVOLV3D OBCp. 1
  • Warping and shrinkageLow warpage – faster startup and less fine tuningDow, EVOLV3D OBCp. 1
  • Odour and emissionsRecommended to be printed in ventilated areaDow, EVOLV3D OBCp. 1
Chemicals and environment (13)
  • Organic solvent resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Acetone · Acetone · specificDow, EVOLV3D OBCAcetone
  • Organic solvent resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Ethanol · Ethanol · specificDow, EVOLV3D OBCEthanol
  • Organic solvent resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Ethanol (60°C) · Ethanol at 60 C · specificDow, EVOLV3D OBCEthanol (60°C)
  • Organic solvent resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Isopropanol · Isopropanol · specificDow, EVOLV3D OBCIsopropanol
  • Organic solvent resistance: described in wordsLittle/no appearance change; slight mechanical-property decrease. Source rating +.Limonene · Limonene · specificDow, EVOLV3D OBCLimonene
  • Organic solvent resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Methanol · Methanol · specificDow, EVOLV3D OBCMethanol
  • Organic solvent resistance: described in wordsLittle/no appearance change; slight mechanical-property decrease. Source rating +.Methyl ethyl ketone · Methyl ethyl ketone · specificDow, EVOLV3D OBCMethyl ethyl ketone
  • Oil and grease resistance: described in wordsLittle/no appearance change; slight mechanical-property decrease. Source rating +.Petroleum · Petroleum · specificDow, EVOLV3D OBCPetroleum
  • Organic solvent resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Propylene glycol · Propylene glycol · specificDow, EVOLV3D OBCPropylene glycol
  • Acid resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Acetic acid80% · Acetic acid 80% · specificDow, EVOLV3D OBCAcetic acid80%
  • Acid resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Nitric acid10% · Nitric acid 10% · specificDow, EVOLV3D OBCNitric acid10%
  • Acid resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Phosphoric acid40% · Phosphoric acid 40% · specificDow, EVOLV3D OBCPhosphoric acid40%
  • Acid resistance: described in wordsNo appearance change; mechanical properties retained. Source rating ++.Sulfuric acid70% · Sulfuric acid 70% · specificDow, EVOLV3D OBCSulfuric acid70%

Not published by any product: price.

Values are for the colour each sheet tested; pigment can change them.