Filament Atlas
Open in the selectorSelector

PETG

72 products from 35 makers. Most documented first. Select a column to sort, a product to see its values, print settings and documents.

Key

How the numbers are worked out

Bambu Lab PETG HFStrength XY, MPa34Strength Z, MPa23Modulus XY, GPa1.81Charpy notched, kJ/m²6.2HDT 0.45, °C69HDT 1.8, °C62Price, CAD/kg26Nozzle, °C230–260Bed, °C65–75Chamber, °C35–50Drying, °C, h658 h

Bambu Lab PETG HFBambu Lab

Published values

PropertyAs publishedConditionsOn the Overview
Bambu Lab, Bambu Filament Technical Data Sheet - PETG HF21 valuesUnless a row says otherwise: printed specimen
dryDried before testing (see preparation)
annealed at 75 °C for 8 hAll the specimens were annealed and dried at 75 °C for 8 h before testing
print settingsSpecimen Printing Conditions Subjects Data Nozzle Temperature 255 °C Bed Temperature 70 °C Printing Speed 200 mm/s InfillDensity 100% * All the specimens were printed at the following settings: Nozzle Temperature = 255 °C, Printing Speed = 200 mm/s, Bed Temperature = 70 °C,InfillDensity = 100%. All the specimens were annealed and dried at 75 °C for 8 h before testing. It'snot
Tensile modulus XY1810 ±190 MPap. 2: Young's Modulus (X-Y)ISO 527, GB/T 1040in the median
Tensile modulus Z1540 ±130 MPap. 2: Young's Modulus (Z)ISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) XY34 ±4 MPap. 2: Tensile Strength (X-Y)ISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) Z23 ±4 MPap. 2: Tensile Strength (Z)ISO 527, GB/T 1040in the median
Elongation at break XY8.6 ± 1.2 %p. 2: Breaking Elongation Rate (X-Y)ISO 527, GB/T 1040in the median
Elongation at break Z5.1 ± 0.8 %p. 2: Breaking Elongation Rate (Z)ISO 527, GB/T 1040in the median
Flexural modulus XY2050 ±120 MPap. 2: Bending Modulus (X-Y)ISO 178, GB/T 9341in the median
Flexural modulus Z1810 ±140 MPap. 2: Bending Modulus (Z)ISO 178, GB/T 9341in the median
Flexural strength XY64 ±3 MPap. 2: Bending Strength (X-Y)ISO 178, GB/T 9341in the median
Flexural strength Z48 ±4 MPap. 2: Bending Strength (Z)ISO 178, GB/T 9341in the median
Charpy impact strength XY31.5 ± 2.2 kJ/m²p. 2: Impact Strength (X-Y)ISO 179, GB/T 1043unnotchednot in the median: unnotched
Charpy impact strength XY6.2 ± 1.8 kJ/m² (notched)p. 2: Impact Strength (X-Y) (notched)ISO 179, GB/T 1043in the median
Charpy impact strength Z10.6 ± 1.2 kJ/m²p. 2: Impact Strength (Z)ISO 179, GB/T 1043not in the median: notch not stated
HDT at 0.45 MPa69 °Cp. 2: Heat Deflection Temperature
ISO 75As the sheet prints it: ISO 75 0.45 MPa
in the median
HDT at 1.8 MPa62 °Cp. 2: Heat Deflection Temperature
ISO 75As the sheet prints it: ISO 75 1.8 MPa
in the median
Glass transition temperature66 °Cp. 2: Glass Transition Temperature
DSCAs the sheet prints it: DSC, 10 °C/min
in the median
Vicat softening temperature70 °Cp. 2: Vicar Softening TemperatureISO 306, GB/T 1633
Melting temperature214 °Cp. 2: Melting Temperature
DSCAs the sheet prints it: DSC, 10 °C/min
Density1.28 g/cm³p. 2: Densityspecimen not stated, ISO 1183
Water absorption0.40 %p. 2: Saturated Water
no standard namedAs the sheet prints it: ter Absorption Rate 25 °C, 55% RH
tested at 25°C
Melt mass-flow rate28.2 ± 2.7 g/10 minp. 2: Melt Indexspecimen not stated,
no standard namedAs the sheet prints it: 210 °C, 2.16 kg
tested at 210°Cmoisture state not statedtreatment not stated
Also named without a value: crystallization temperature.

Print settings

Nozzle
230–260 °Cown data sheet
Bed
65–75 °Cown data sheet
Heated chamber
35–50 °Cown data sheet
Drying
65 °C for 8 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Annealing
75 °C for 8 hown data sheet
Its print profile, in the documents' words

Price

26 CAD/kgthe median of its 3 regular prices in the sample

7 listings: 3 in its price, 4 with no regular price per kilogram recorded
  • Bambu Lab Canada: 30 per kg, sale pricePETG HF - Red (33200) / Filament with spool / 1 kgnot used: no regular price per kilogram recorded; seen 10 Sep 2026
  • Bambu Lab Canada: 26 per kg, sale pricePETG HF - Black (33102) / Refill / 1 kgnot used: no regular price per kilogram recorded; seen 10 Sep 2026
  • Bambu Lab Canada: 30 per kg, sale pricePETG HF - Gray (33101) / Filament with spool / 1 kgnot used: no regular price per kilogram recorded; seen 10 Sep 2026
  • 3D Printing Canada: 30 per kg, sale priceWhite - Bambu Lab PETG HF Filament - 1.75mm,1kg / Filament with spoolnot used: no regular price per kilogram recorded; seen 10 Sep 2026
  • Shop3D.ca: 26 CAD/kgBambu Lab - PETG HF REFILL (1.75mm) 1kg / Black (SKU G02-K0-1.75-1000-SPLFREE)in its price; seen 30 Sep 2026
  • DigitMakers: 19 CAD/kgBambu Lab PETG HF 1.75mm Refill - 1 kg (Various Colors) / Green (33500) (SKU G02-G0-1.75-1000-SPLFREE)in its price; seen 30 Sep 2026
  • MakerWiz: 26 CAD/kgBambu Lab Bambu PETG HF 1kg / Black / Refill / 1kgin its price; seen 30 Sep 2026

Its 3 documents

What the maker says (9)
Specimen preparation (1)
Chemicals and environment (7)
Bambu Lab PETG TranslucentStrength XY, MPa33Strength Z, MPa29Modulus XY, GPa1.42Charpy notched, kJ/m²8.6HDT 0.45, °C74HDT 1.8, °C68Price, CAD/kg26Nozzle, °C230–270Bed, °C65–75Chamber, °C35–50Drying, °C, h658 h

Bambu Lab PETG TranslucentBambu Lab

Published values

PropertyAs publishedConditionsOn the Overview
Bambu Lab, Bambu Filament Technical Data Sheet - PETG Translucent21 valuesThe same values also in Bambu Lab, Technical Data Sheet V1.0 PETG Translucent.Unless a row says otherwise: printed specimen
dryDried before testing (see preparation)
annealed at 65 °C for 8 hAll the specimens were annealed and dried at 65 °C for 8 h before testing
print settingsSpecimen Printing Conditions Subjects Data Nozzle Temperature 255 °C Bed Temperature 70 °C Printing Speed 150 mm/s Infill Density 100% * All the specimens were printed at the following settings: Nozzle Temperature = 255 °C, Printing Speed = 150 mm/s, Bed Temperature = 70 °C, Infill Density = 100%. All the specimens were annealed and dried at 65 °C for 8 h before testing. It's
Tensile modulus XY1420 ± 160 MPap. 2: Young's Modulus (X-Y)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 527, GB/T 1040in the median
Tensile modulus Z1230 ± 140 MPap. 2: Young's Modulus (Z)ISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) XY33 ± 4 MPap. 2: Tensile Strength (X-Y)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) Z29 ± 3 MPap. 2: Tensile Strength (Z)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 527, GB/T 1040in the median
Elongation at break XY8.2 ± 1.3 %p. 2: Breaking Elongation Rate (X-Y)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 527, GB/T 1040in the median
Elongation at break Z5.2 ± 0.9 %p. 2: Breaking Elongation Rate (Z)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 527, GB/T 1040in the median
Flexural modulus XY1610 ± 130 MPap. 2: Bending Modulus (X-Y)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 178, GB/T 9341in the median
Flexural modulus Z1520 ± 110 MPap. 2: Bending Modulus (Z)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 178, GB/T 9341in the median
Flexural strength XY68 ± 3 MPap. 2: Bending Strength (X-Y)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 178, GB/T 9341in the median
Flexural strength Z55 ± 4 MPap. 2: Bending Strength (Z)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 178, GB/T 9341in the median
Charpy impact strength XY37.4 ± 3.3 kJ/m²;p. 2: Impact Strength (X-Y) — unnotchedISO 179, GB/T 1043not in the median: unnotched
Charpy impact strength XY8.6 ± 2.1 kJ/m²p. 2: Impact Strength (X-Y) — notchedalso in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 179, GB/T 1043in the median
Charpy impact strength Z7.2 ± 1.8 kJ/m²p. 2: Impact Strength (Z)also in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 179, GB/T 1043not in the median: notch not stated
HDT at 0.45 MPa74 °Cp. 2: Heat Deflection Temperaturealso in Bambu Lab, Technical Data Sheet V1.0 PETG Translucent
ISO 75As the sheet prints it: ISO 75 0.45 MPa
in the median
HDT at 1.8 MPa68 °Cp. 2: Heat Deflection Temperaturealso in Bambu Lab, Technical Data Sheet V1.0 PETG Translucent
ISO 75As the sheet prints it: ISO 75 1.8 MPa
in the median
Glass transition temperature70 °Cp. 2: Glass Transition Temperaturealso in Bambu Lab, Technical Data Sheet V1.0 PETG Translucent
DSCAs the sheet prints it: DSC, 10 °C/min
in the median
Vicat softening temperature79 °Cp. 2: Vicar Softening Temperaturealso in Bambu Lab, Technical Data Sheet V1.0 PETG TranslucentISO 306, GB/T 1633
Melting temperature228 °Cp. 2: Melting Temperaturealso in Bambu Lab, Technical Data Sheet V1.0 PETG Translucent
DSCAs the sheet prints it: DSC, 10 °C/min
Density1.25 g/cm³p. 2: Densityalso in Bambu Lab, Technical Data Sheet V1.0 PETG Translucentspecimen not stated, ISO 1183
Water absorption0.30 %p. 2: Saturated Water Absorption Ratealso in Bambu Lab, Technical Data Sheet V1.0 PETG Translucent
no standard namedAs the sheet prints it: te 25 °C, 55% RH
tested at 25°C
Melt mass-flow rate11.7 ± 1.5 g/10 minp. 2: Melt Indexalso in Bambu Lab, Technical Data Sheet V1.0 PETG Translucentspecimen not stated,
no standard namedAs the sheet prints it: 230 °C, 2.16 kg
tested at 230°Cmoisture state not statedtreatment not stated
Also named without a value: crystallization temperature.
Bambu Lab, Technical Data Sheet V1.0 PETG Translucent1 value
Tensile modulus Z1230 ± 1430 MPap. 2: Young's Modulus (Z) ISO 527, GB/T 1040ISO 527, GB/T 1040
dryDried before testing (see preparation)
annealed at 65 °C for 8 hAll the specimens were annealed and dried at 65 °C for 8 h before testing
not in the median: another value of this product is in it

Print settings

Nozzle
230–270 °Cown data sheet
Bed
65–75 °Cown data sheet
Heated chamber
35–50 °Cown data sheet
Drying
65 °C for 8 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Annealing
65 °C for 8 hown data sheet
Its 2 print profiles, in the documents' words

Price

26 CAD/kgits one regular price in the sample

2 listings: 1 in its price, 1 with no regular price per kilogram recorded
  • Bambu Lab Canada: 30 per kg, sale pricePETG Translucent - Light Blue (32600) / Filament with spool / 1 kgnot used: no regular price per kilogram recorded; seen 10 Sep 2026
  • Bambu Lab Canada: 26 CAD/kgPETG Translucent - Clear (32101) / Refill / 1 kgin its price; seen 10 Sep 2026

Its 4 documents

What the maker says (6)
  • BenefitsThis specially tuned filament minimizes common issues like nozzle sticking, leakage, and clumping during the printing process, providing a hassle-free experience compared to ordinary PETG materials.Bambu Lab, Technical Data Sheet V1.0 PETG Translucentp. 1
  • BenefitsThe filament also exhibits water resistance, UV resistance, and resistance to temperature changes, making it an excellent choice for outdoor applications.Bambu Lab, Technical Data Sheet V1.0 PETG Translucentp. 1
  • Pitfalls and limitationsIt's not recommended to anneal prints of PETG Translucent, because only very limited promotion of properties can obtain while prints with not very simple shape and structure may deform obviously.Bambu Lab, Technical Data Sheet V1.0 PETG Translucentp. 3
  • Odour and emissionsOdor OdorlessBambu Lab, Technical Data Sheet V1.0 PETG Translucentp. 3
  • Good forOptimized for exceptional light transmittance, Bambu PETG Translucent provides unmatched levels of translucency. * Please note that the transparency of the prints may vary depending on factors such as size and structure, as well as printing parameters (including speed, nozzle temperature, and infill density).Bambu Lab, PETG Translucent official maker product pagep. 1: exact product features/description/application tips, source text line 135
  • Printing advicePrinting PETG Translucent with the appropriate print parameters can achieve an appearance ranging from tinted translucent to tinted transparent. Learn more about Printing tips for transparent PETG on WIKI.Bambu Lab, PETG Translucent official maker product pagep. 1: exact product features/description/application tips, source text line 157
Specimen preparation (1)
Chemicals and environment (7)
Kingroon PETG BasicStrength XY, MPa33Strength Z, MPa29Modulus XY, GPa1.42Charpy notched, kJ/m²8.6HDT 0.45, °C74HDT 1.8, °C68Price, CAD/kg—Nozzle, °C230–270Bed, °C65–75Chamber, °C35–50Drying, °C, h658 h

Kingroon PETG BasicKingroon

Published values

PropertyAs publishedConditionsOn the Overview
Kingroon, KINGROON Filament Technical Data Sheet V1.0 PETG Basic20 valuesUnless a row says otherwise: printed specimen
dryAll the specimens were annealed and dried at 65 °C for 8 h before testing
annealed at 65 °C for 8 hAll the specimens were annealed and dried at 65 °C for 8 h before testing
print settingsNozzle Temperature = 255 °C; Printing Speed = 150 mm/s; Bed Temperature = 70 °C; Infill Density = 100%
Tensile modulus XY1420 ± 160 MPap. 2: Young's Modulus(X-Y)ISO 527, GB/T 1040in the median
Tensile modulus Z1230 ± 140 MPap. 2: Young's Modulus (Z)ISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) XY33 ± 4 MPap. 2: Tensile Strength (X-Y)ISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) Z29 ± 3 MPap. 2: Tensile Strength (Z)ISO 527, GB/T 1040in the median
Elongation at break XY8.2 ± 1.3 %p. 2: Breaking Elongation Rate (X-Y)ISO 527, GB/T 1040in the median
Elongation at break Z5.2 ± 0.9 %p. 2: Breaking Elongation Rate (Z)ISO 527, GB/T 1040in the median
Flexural modulus XY1610 ± 130 MPap. 2: Bending Modulus (X-Y)ISO 178, GB/T 9341in the median
Flexural modulus Z1520 ± 110 MPap. 2: Bending Modulus (Z)ISO 178, GB/T 9341in the median
Flexural strength XY68 ± 3 MPap. 2: Bending Strength (X-Y)ISO 178, GB/T 9341in the median
Flexural strength Z55 ± 4 MPap. 2: Bending Strength (Z)ISO 178, GB/T 9341in the median
Charpy impact strength XY8.6 ± 2.1 kJ/m²p. 2: Impact Strength (X-Y) (notched)ISO 179, GB/T 1043in the median
Charpy impact strength XY37.4 ± 3.3 kJ/m²;p. 2: Impact Strength (X-Y) (unnotched, the first of the cell's two values)ISO 179, GB/T 1043not in the median: unnotched
Charpy impact strength Z7.2 ± 1.8 kJ/m²p. 2: Impact Strength (Z)ISO 179, GB/T 1043not in the median: notch not stated
HDT at 0.45 MPa74 °Cp. 2: Heat Deflection Temperature (74 °C)
ISO 75As the sheet prints it: ISO 75; 0.45 Mpa
in the median
HDT at 1.8 MPa68 °Cp. 2: Heat Deflection Temperature (68 °C)
ISO 75As the sheet prints it: ISO 75; 1.8 Mpa
in the median
Glass transition temperature70 °Cp. 2: Glass Transition Temperaturespecimen not stated,
DSCAs the sheet prints it: DSC; rate=10 °C/min
moisture state not statedtreatment not statedprint settings not stated		in the median
Vicat softening temperature79 °Cp. 2: Vicar Softening TemperatureISO 306, GB/T 1633
Melting temperature228 °Cp. 2: Melting Temperaturespecimen not stated,
DSCAs the sheet prints it: DSC; rate=10 °C/min
moisture state not statedtreatment not statedprint settings not stated
Density1.25 g/cm³p. 2: Densityspecimen not stated, ISO 1183moisture state not statedtreatment not statedprint settings not stated
Melt mass-flow rate11.7 ± 1.5 g/10 minp. 2: Melt Indexspecimen not stated,
no standard namedAs the sheet prints it: 2.16 kg
tested at 230 °Cmoisture state not statedtreatment not statedprint settings not stated

Print settings

Nozzle
230–270 °Cown data sheet
Bed
65–75 °Cown data sheet
Heated chamber
35–50 °Cown data sheet
Drying
65 °C for 8 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Annealing
65 °C for 8 hown data sheet
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (4)
Polymaker PETGStrength XY, MPa48Strength Z, MPa45.7Modulus XY, GPa2.31Charpy notched, kJ/m²4.95HDT 0.45, °C69HDT 1.8, °C65Price, CAD/kg30Nozzle, °C240–260Bed, °C60–70Chamber, °CnoneDrying, °C, h556 h

Polymaker PETGPolymaker

Published values

PropertyAs publishedConditionsOn the Overview
Polymaker, Polymaker™ PETG Technical Data Sheet21 values
Tensile modulus XY2311.11 ± 92.41 MPap. 1: Young’s modulus (X-Y)ISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Tensile modulus Z2202.91 ± 52.34 MPap. 1: Young’s modulus (Z)no standard stated
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Tensile strength (yield or break not stated) XY47.96 ± 4.88 MPap. 1: Tensile strength (X-Y)ISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Tensile strength (yield or break not stated) Z45.71 ± 1.76 MPap. 1: Tensile strength (Z)no standard stated
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Elongation at break XY9.33 ± 6.57 %p. 1: Elongation at break (X-Y)ISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Elongation at break Z3.54 ± 2.35 %p. 1: Elongation at break (Z)no standard stated
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Flexural modulus XY2277.34 ± 198.09 MPap. 1: Bending modulus (X-Y)ISO 178, GB/T 9341
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Flexural modulus Z1958.74 ± 126.39 MPap. 1: Bending modulus (Z)no standard stated
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Flexural strength XY80.08 ± 3.53 MPap. 1: Bending strength (X-Y)ISO 178, GB/T 9341
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Flexural strength Z57.65 ± 5.63 MPap. 1: Bending strength (Z)no standard stated
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
in the median
Charpy impact strength XY20.24 ± 3.95 kJ/m2p. 1: Charpy impact strength (X-Y) ISO 179, GB/T 1043ISO 179, GB/T 1043
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
not in the median: notch not stated
Charpy impact strength XY4.95 ± 0.55 kJ/m²p. 1: Charpy impact strength (X-Y) notchedISO 179, GB/T 1043in the median
Charpy impact strength Z15.74 ± 3.91 kJ/m²p. 1: Charpy impact strength (Z)ISO 179, GB/T 1043not in the median: notch not stated
HDT at 0.45 MPa69°Cp. 1: Heat deflection temp. 0.45MPa
ISO 75As the sheet prints it: ISO 75; 0.45 MPa
in the median
HDT at 1.8 MPa65°Cp. 1: Heat deflection temp. 1.8MPa
ISO 75As the sheet prints it: ISO 75; 1.8 MPa
in the median
Glass transition temperature71.24 °Cp. 1: Glass transition temp. DSC, 10°C/minDSCin the median
Vicat softening temperature75 °Cp. 1: Vicat softening temp.no standard stated
Decomposition temperature405.49°Cp. 1: Decomposition temp.
TGAAs the sheet prints it: TGA, 20°C/min; rate=20 °C/min
Density1.30 g/cm3p. 1: Density ISO1183, GB/T1033
ISO 1183, GB/T 1033As the sheet prints it: 1183 ISO1183 GB/T1033
Water absorption0.51%p. 1: Max Water Absorption Rate
no standard namedAs the sheet prints it: RH=70%
after moisture conditioning70% RH 23°C
tested at 23 °C
Melt mass-flow rate16.3 g/10minp. 1: Melt index 230°C, 2.16 kg
no standard namedAs the sheet prints it: 230°C 2.16 kg
tested at 230°C

Print settings

Nozzle
240–260 °Cown data sheet
Bed
60–70 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
55 °C for 6 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 240-260°C; Bed 60-70°C; Drying 55°C/6HPolymaker, Polymaker™ PETG Technical Data Sheetp. 1: Recommended printing settings: Nozzle temperature; p. 1: Drying temp. and time; p. 1: Closure chamber; p. 1: Build surface treatment; p. 1: Based on 0.4mm nozzle

Price

30 CAD/kgits one regular price in the sample

1 listing
  • DigitMakers: 30 CAD/kgPolymaker™ PETG - 1.75mm 1000g / Black (SKU PLMK-FL-PETG-1.75-1000G-BLK)in its price; seen 30 Sep 2026

Its 2 documents

What the maker says (2)
Chemicals and environment (5)
Bambu Lab PETG BasicStrength XY, MPa51Strength Z, MPa35Modulus XY, GPa2.78Charpy notched, kJ/m²—HDT 0.45, °C71HDT 1.8, °C68Price, CAD/kg25Nozzle, °C230–260Bed, °C65–75Chamber, °C35–50Drying, °C, h658 h

Bambu Lab PETG BasicBambu Lab

Published values

PropertyAs publishedConditionsOn the Overview
Bambu Lab, Bambu Filament Technical Data Sheet - PETG Basic19 valuesUnless a row says otherwise: printed specimen
print settingsSpecimen Printing Conditions Subjects Data Nozzle Temperature 255 °C Bed Temperature 70 °C Printing Speed 150 mm/s Infill Density 100% All the specimens were printed at the following settings: X1-Carbon, Nozzle Temperature = 255 °C, Printing Speed = 150 mm/s, Bed Temperature = 70 °C, Infill Density = 100%. It's not recommended to anneal prints of PETG Basic, because only very
Tensile modulus XY2780 ± 65 MPap. 2: Young's Modulus (X-Y)ISO 527, GB/T 1040in the median
Tensile modulus Z2550 ± 100 MPap. 2: Young's Modulus (Z)ISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) XY51 ± 1 MPap. 2: Tensile Strength (X-Y)ISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) Z35 ± 6 MPap. 2: Tensile Strength (Z)ISO 527, GB/T 1040in the median
Elongation at break XY9.5 ± 0.7 %p. 2: Breaking Elongation Rate (X-Y)ISO 527, GB/T 1040in the median
Elongation at break Z5.2 ± 1.4 %p. 2: Breaking Elongation Rate (Z)ISO 527, GB/T 1040in the median
Flexural modulus XY1950 ± 50 MPap. 2: Bending Modulus (X-Y)ISO 178, GB/T 9341in the median
Flexural modulus Z1740 ± 40 MPap. 2: Bending Modulus (Z)ISO 178, GB/T 9341in the median
Flexural strength XY75 ± 3 MPap. 2: Bending Strength (X-Y)ISO 178, GB/T 9341in the median
Flexural strength Z56 ± 4 MPap. 2: Bending Strength (Z)ISO 178, GB/T 9341in the median
Charpy impact strength XY34.2 ± 4.1 kJ/m²p. 2: Impact Strength (X-Y)ISO 179, GB/T 1043not in the median: notch not stated
Charpy impact strength Z10.5 ± 1.8 kJ/m²p. 2: Impact Strength (Z)ISO 179, GB/T 1043not in the median: notch not stated
HDT at 0.45 MPa71 °Cp. 2: Heat Deflection Temperature
ISO 75As the sheet prints it: ISO 75 0.45 MPa
in the median
HDT at 1.8 MPa68 °Cp. 2: Heat Deflection Temperature
ISO 75As the sheet prints it: ISO 75 1.8 MPa
in the median
Glass transition temperature69 °Cp. 2: Glass Transition Temperature
DSCAs the sheet prints it: DSC, 10 °C/min
in the median
Vicat softening temperature69 °Cp. 2: Vicat Softening TemperatureISO 306, GB/T 1633
Density1.25 g/cm³p. 2: Densityspecimen not stated, ISO 1183
Water absorption0.45 %p. 2: Saturated Water Absorption Rate
no standard namedAs the sheet prints it: ate 25 °C, 55% RH
tested at 25°C
Melt mass-flow rate22.9 ± 2.4 g/10 minp. 2: Melt Indexspecimen not stated,
no standard namedAs the sheet prints it: 245 °C, 2.16 kg
tested at 245°C
Also named without a value: melting temperature, crystallization temperature.

Print settings

Nozzle
230–260 °Cown data sheet
Bed
65–75 °Cown data sheet
Heated chamber
35–50 °Cown data sheet
Drying
65 °C for 8 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

25 CAD/kgits one regular price in the sample

2 listings: 1 in its price, 1 with no regular price per kilogram recorded
  • Bambu Lab Canada: 25 CAD/kgPETG Basic - Black(30105) / Refill / 1kgin its price; seen 10 Sep 2026
  • Bambu Lab Canada: 29 per kg, sale pricePETG Basic - Black(30105) / Filament with spool / 1kgnot used: no regular price per kilogram recorded; seen 10 Sep 2026

Its 3 documents

What the maker says (9)
Chemicals and environment (7)
Polymaker PolyMax PETGSold as toughened (the maker's statement)Strength XY, MPa37.9Strength Z, MPa29.4Modulus XY, GPa1.68Charpy notched, kJ/m²11.6HDT 0.45, °C76HDT 1.8, °C72Price, CAD/kg—Nozzle, °C230–260Bed, °C70–80Chamber, °CnoneDrying, °C, h656 h

Polymaker PolyMax PETGPolymaker

Sold as toughened or impact-modified: "Our PolyMax™ PETG is a modified PETG with enhanced fracture toughness which makes it more ductile and impact resistance." (Polymaker, Polymaker PolyMax PETG official product page, p. 1). The maker's statement, not a test result.

Published values

PropertyAs publishedConditionsOn the Overview
Polymaker, PolyMax™ PETG Technical Data Sheet19 valuesThe same values also in Polymaker, Nov. 2018 Technical Data Sheet Version 4.0 PolyMax™ PETG.
Tensile modulus XY1684 ± 135 MPap. 1: Young’s modulus (X-Y)ISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Tensile modulus Z1603 ± 40 MPap. 1: Young’s modulus (Z)also in Polymaker, Nov. 2018 Technical Data Sheet Version 4.0 PolyMax™ PETGISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Tensile strength (yield or break not stated) XY37.9 ± 1.4 MPap. 1: Tensile strength (X-Y)ISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Tensile strength (yield or break not stated) Z29.4 ± 1.0 MPap. 1: Tensile strength (Z)also in Polymaker, Nov. 2018 Technical Data Sheet Version 4.0 PolyMax™ PETGISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Elongation at break XY5.22 ± 1.5 %p. 1: Elongation at break (X-Y)ISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Elongation at break Z3.10 ± 0.51 %p. 1: Elongation at break (Z)ISO 527, GB/T 1040
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Flexural modulus XY1068 ± 94 MPap. 1: Bending modulus (X-Y)ISO 178, GB/T 9341
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Flexural strength XY58.3 ± 0.38 MPap. 1: Bending strength (X-Y)ISO 178, GB/T 9341
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Flexural strength Z55.1 ± 4.9 MPap. 1: Bending strength (Z)also in Polymaker, Nov. 2018 Technical Data Sheet Version 4.0 PolyMax™ PETGISO 178, GB/T 9341
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
in the median
Charpy impact strength XY11.6 ± 0.8 kJ/m2p. 1: Notched charpy impact strength (X-Y)ISO 179, GB/T 1043
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
not in the median: sold as toughened, set apart
Charpy impact strength Z2.4 ± 0.6 kJ/m2p. 1: Notched charpy impact strength (Z)ISO 179, GB/T 1043
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient temp.
not in the median: measured on a bar in another orientation
HDT at 0.45 MPa76°Cp. 1: Heat deflection temp. 0.45MPa
ISO 75As the sheet prints it: ISO 75; 0.45 MPa
in the median
HDT at 1.8 MPa72°Cp. 1: Heat deflection temp. 1.8MPa
ISO 75As the sheet prints it: ISO 75; 1.8 MPa
in the median
Glass transition temperature79 °Cp. 1: Glass transition temp. DSC, 10°C/minalso in Polymaker, Nov. 2018 Technical Data Sheet Version 4.0 PolyMax™ PETGDSCin the median
Vicat softening temperature82 °Cp. 1: Vicat softening temp. ISO 306, GB/T 1633
ISO 306, GB/T 1633As the sheet prints it: 306 ISO 306 GB/T 1633
Decomposition temperature373°Cp. 1: Decomposition temp.
TGAAs the sheet prints it: TGA, 20°C/min; rate=20 °C/min
Density1.24 g/cm3p. 1: Density ISO1183, GB/T 1033
ISO 1183, GB/T 1033As the sheet prints it: 1183 ISO1183 GB/T 1033
Water absorption0.542 %p. 1: Equilibrium water absorption (%)=
no standard namedAs the sheet prints it: Equilibrium water absorption
Melt mass-flow rate9 g/10minp. 1: Melt index 210°C, 2.16 kg
no standard namedAs the sheet prints it: 210°C 2.16 kg
tested at 210°C
Polymaker, Nov. 2018 Technical Data Sheet Version 4.0 PolyMax™ PETG10 valuesUnless a row says otherwise: printed specimen
print settingsnozzle temperature = 240 °C, printing speed = 45 mm/s, build plate temperature = 80 °C, infill = 100%
Tensile modulus XY1523 ± 50 MPap. 1: Young’s modulus (X-Y) ASTM D638 (ISO 527, GB/T 1040)ASTM D638, ISO 527, GB/T 1040not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Tensile strength (yield or break not stated) XY31.7 ± 0.1 MPap. 1: Tensile strength (X-Y) ASTM D638 (ISO 527, GB/T 1040)ASTM D638, ISO 527, GB/T 1040not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Elongation at break XY4.4 ± 0.6 %p. 1: Elongation at break (X-Y) ASTM D638 (ISO 527, GB/T 1040)ASTM D638, ISO 527, GB/T 1040not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Elongation at break Z3.1 ± 0.5 %p. 1: Elongation at break (Z) ASTM D638 (ISO 527, GB/T 1040)ASTM D638, ISO 527, GB/T 1040not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Flexural strength XY58.3 ± 0.4 MPap. 1: Bending strength (X-Y) ASTMD790 (ISO 178, GB/T 9341)ASTM D790, ISO 178, GB/T 9341not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Impact strength, test unclear XY9.7 ± 2.6 kJ/m2p. 1: Charpy impact strength (X-Y) ASTM D256 (ISO 179, GB/T 1043)ASTM D256, ISO 179, GB/T 1043notchedWhich test: probably Charpylisted under other properties
Impact strength, test unclear Z2.4 ± 0.5 kJ/m2p. 1: Charpy impact strength (Z) ASTM D256 (ISO 179, GB/T 1043)ASTM D256, ISO 179, GB/T 1043notchedWhich test: probably Charpylisted under other properties
Density1.25 g/cm3p. 1: Density ASTM D792 (ISO 1183, GB/T 1033)
ASTM D792, ISO 1183, GB/T 1033As the sheet prints it: 792 ASTM D792 ISO 1183 GB/T 1033
print settings not stated
Melt mass-flow rate3.9 (g/10 min)p. 1: Melt index (220 °C)specimen not stated,
no standard namedAs the sheet prints it: 2.16 kg
tested at 220 °Cprint settings not stated
Melt mass-flow rate17.1 (g/10 min)p. 1: Melt index (240 °C)specimen not stated,
no standard namedAs the sheet prints it: 2.16 kg
tested at 240 °Cprint settings not stated

Print settings

Nozzle
230–260 °Cown data sheet
Bed
70–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 6 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): nozzle in Polymaker, Nov. 2018 Technical Data Sheet Version 4.0 PolyMax™ PETG; heated chamber in Polymaker, Nov. 2018 Technical Data Sheet Version 4.0 PolyMax™ PETG; drying in Polymaker, Polymaker PolyMax PETG official product page.

Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (6)
Chemicals and environment (5)
Polymaker PolyLite PETGStrength XY, MPa50.8Strength Z, MPa42.8Modulus XY, GPa2.12Charpy notched, kJ/m²2.6HDT 0.45, °C78HDT 1.8, °C75Price, CAD/kg38Nozzle, °C230–240Bed, °C70–80Chamber, °CnoneDrying, °C, h656 h

Polymaker PolyLite PETGPolymaker

Published values

PropertyAs publishedConditionsOn the Overview
Polymaker, PolyLite PETG7 valuesThe same values also in Polymaker, PolyLite PETG, Polymaker, PolyLite™ PETG Technical Data Sheet and Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETG.Unless a row says otherwise: printed specimen
print settingsPrinting temperature 240 °C Bed temperature 80 °C Shell 2 Top & bottom layer 4 Infill 100% Environmental temperature 25 °C Cooling fan OFF DISCLAIMER: The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality con
Charpy impact strength XY2.6 ± 0.2 kJ/m2p. 4: Charpy impact strength (X-Y)ISO 179, GB/T 1043
moistureAll specimens were conditioned at room temperature for 24h prior to testing
notched		in the median
HDT at 0.45 MPa78.4 °Cp. 3: Heat deflection temperaturealso in Polymaker, PolyLite PETG
ISO 75As the sheet prints it: ISO 75 0.45MPa
in the median
HDT at 1.8 MPa74.8 °Cp. 3: Heat deflection temperaturealso in Polymaker, PolyLite PETG
ISO 75As the sheet prints it: ISO 75 1.8MPa
in the median
Glass transition temperature81 °Cp. 3: Glass transition temperaturealso in Polymaker, PolyLite™ PETG Technical Data Sheetalso in Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETGalso in Polymaker, PolyLite PETG
DSCAs the sheet prints it: DSC, 10°C/min
in the median
Vicat softening temperature84 °Cp. 3: Vicat softening temperaturealso in Polymaker, PolyLite™ PETG Technical Data Sheetalso in Polymaker, PolyLite PETGISO 306, GB/T 1633
Density1.25 g/cm3p. 2: Densityalso in Polymaker, PolyLite™ PETG Technical Data Sheetalso in Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETGalso in Polymaker, PolyLite PETGspecimen not stated, ISO 1183, GB/T 1033
Water absorption0.54 %p. 2: Equilibrium water absorption (%)also in Polymaker, PolyLite™ PETG Technical Data Sheetalso in Polymaker, PolyLite PETGspecimen not stated,
no standard namedAs the sheet prints it: Equilibrium water absorption
Also named without a value: flexural modulus, flexural strength, charpy impact strength, melting temperature, crystallization temperature, thermal conductivity.
Polymaker, PolyLite PETG10 valuesThe same values also in Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETG and Polymaker, PolyLite™ PETG Technical Data Sheet.Unless a row says otherwise: printed specimen
print settingsPrinting temperature 240 °C; Bed temperature 80 °C; Shell 2; Top & bottom layer 4; Infill 100%; Environmental temperature 25 °C; Cooling fan OFF
Tensile modulus XY1472 ± 270 MPap. 4: Young’s modulus (X-Y)also in Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETGISO 527, GB/T 1040not in the median: another value of this product is in it
Tensile modulus Z1087 ± 79 MPap. 4: Young’s modulus (Z)ISO 527, GB/T 1040not in the median: another value of this product is in it
Tensile strength (yield or break not stated) XY31.9 ± 1.1 MPap. 4: Tensile strength (X-Y)also in Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETGISO 527, GB/T 1040not in the median: another value of this product is in it
Tensile strength (yield or break not stated) Z13.4 ± 2.0 MPap. 4: Tensile strength (Z)ISO 527, GB/T 1040not in the median: another value of this product is in it
Elongation at break XY6.8 ± 0.9 %p. 4: Elongation at break (X-Y)also in Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETGISO 527, GB/T 1040not in the median: another value of this product is in it
Elongation at break Z1.3 ± 0.2 %p. 4: Elongation at break (Z)ISO 527, GB/T 1040not in the median: another value of this product is in it
Flexural modulus XY1174 ± 64 MPap. 4: Bending modulus (X-Y)ISO 178, GB/T 9341not in the median: another value of this product is in it
Flexural strength XY53.7 ± 2.4 MPap. 4: Bending strength (X-Y)ISO 178, GB/T 9341not in the median: another value of this product is in it
Charpy impact strength XY5.1 ± 0.3 kJ/m2p. 4: Charpy impact strength (X-Y)ISO 179, GB/T 1043notchednot in the median: another value of this product is in it
Melt mass-flow rate10.8 g/10minp. 2: Melt index 240°C, 2.16kgalso in Polymaker, PolyLite™ PETG Technical Data Sheetalso in Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETGspecimen not stated,
no standard namedAs the sheet prints it: 240°C 2.16kg
tested at 240°Cprint settings not stated
Polymaker, PolyLite™ PETG Technical Data Sheet8 valuesThe same values also in Polymaker, PolyLite PETG.Unless a row says otherwise: printed specimen
print settingsPrinting temperature 240°C; Infill 100%; Bed temperature 80°C; Shell 2; Top & bottom layer 3; Cooling fan OFF; Environmental Temperature Ambient
Tensile modulus XY2116.8 ± 68.1 MPap. 1: Young’s modulus (X-Y)also in Polymaker, PolyLite PETGISO 527, GB/T 1040in the median
Tensile modulus Z1898.7 ± 98.5 MPap. 1: Young’s modulus (Z)also in Polymaker, PolyLite PETGISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) XY50.8 ± 0.9 MPap. 1: Tensile strength (X-Y)also in Polymaker, PolyLite PETGISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) Z42.8 ± 2.8 MPap. 1: Tensile strength (Z)also in Polymaker, PolyLite PETGISO 527, GB/T 1040in the median
Elongation at break XY8.4 ± 1.7 %p. 1: Elongation at break (X-Y)also in Polymaker, PolyLite PETGISO 527, GB/T 1040in the median
Elongation at break Z3.3 ± 0.2 %p. 1: Elongation at break (Z)also in Polymaker, PolyLite PETGISO 527, GB/T 1040in the median
Flexural modulus XY1898.5 ± 35.5 MPap. 1: Bending modulus (X-Y)also in Polymaker, PolyLite PETGISO 178, GB/T 9341in the median
Flexural strength XY69.6 ± 0.8 MPap. 1: Bending strength (X-Y)also in Polymaker, PolyLite PETGISO 178, GB/T 9341in the median
Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETG4 valuesUnless a row says otherwise: printed specimen
moistureAll specimens were conditioned at room temperature for 24h prior to testing
print settingsnozzle temperature = 240 °C, printing speed = 45 mm/s, build plate temperature = 80 °C, infill = 100%
Flexural modulus orientation not stated1174 ± 64 MPap. 1: Bending modulus ASTMD790 (ISO 178, GB/T 9341)
ASTM D790, ISO 178, GB/T 9341As the sheet prints it: 790 ASTMD790 ISO 178 GB/T 9341
not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Flexural strength orientation not stated53.7 ± 2.4 MPap. 1: Bending strength ASTMD790 (ISO 178, GB/T 9341)
ASTM D790, ISO 178, GB/T 9341As the sheet prints it: 790 ASTMD790 ISO 178 GB/T 9341
not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Impact strength, test unclear5.1 ± 0.3 kJ/m2p. 1: Charpy impact strength ASTM D256 (ISO 179, GB/T 1043)
ASTM D256, ISO 179, GB/T 1043As the sheet prints it: 256 ASTM D256 ISO 179 GB/T 1043
notchedWhich test: probably Charpy		listed under other properties
Melt mass-flow rate3.9 g/10 minp. 1: Melt index 220 °C, 2.16 kgspecimen not stated,
no standard namedAs the sheet prints it: 220 °C 2.16 kg
tested at 220°Cmoisture state not statedprint settings not stated

Print settings

Nozzle
230–240 °Cown data sheet
Bed
70–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 6 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): nozzle in Polymaker, PolyLite PETG official product page; bed in Polymaker, Jun. 2017 Technical Data Sheet Version 3.0 PolyLite™ PETG; drying in Polymaker, PolyLite PETG official product page.

Its 5 print profiles, in the documents' words

Price

38 CAD/kgthe median of its 2 regular prices in the sample

2 listings
  • DigitMakers: 30 CAD/kgPolyLite™ PETG Various Colors (1.75mm 1000g) / White (SKU PLMK-FL-PLITE-PETG-1.75-1000G-WHT)in its price; seen 30 Sep 2026
  • MakerWiz: 46 CAD/kgPolymaker PolyLite™ PETG Filament - 1.75 mm, 1 kg (11 Colours) / Black / 1.75 mm (SKU 61000401)in its price; seen 30 Sep 2026

Its 6 documents

What the maker says (9)
Chemicals and environment (11)
QIDI ToughPETG-HFSold as toughened (the maker's statement)Strength XY, MPa44.2Strength Z, MPa42.7Modulus XY, GPa1.82Charpy notched, kJ/m²16.4HDT 0.45, °C70HDT 1.8, °C65Price, CAD/kg—Nozzle, °C230–260Bed, °C70–80Chamber, °CnoneDrying, °C, h658 h

QIDI ToughPETG-HFQIDI

Sold as toughened or impact-modified: "QIDI has improved the notch impact strength of QIDI ToughPETG-HF to more than twice that of ordinary PETG without affecting the interlayer bonding strength in the Z-axis direction through toughness improvement technology." (QIDI, Technical Data Sheet QIDI ToughPETG-HF, p. 1). The maker's statement, not a test result.

Published values

PropertyAs publishedConditionsOn the Overview
QIDI, Technical Data Sheet QIDI ToughPETG-HF15 valuesUnless a row says otherwise: printed specimen
Tensile modulus XY1821.82 ± 49.41 MPap. 2: 杨氏模量(X-Y) Young's modulus(X-Y)no standard statedin the median
Tensile modulus Z1955.67 ± 179.30 MPap. 2: 杨氏模量(Z) Young's modulus(Z)no standard statedin the median
Tensile yield strength XY44.23 ± 0.64 MPap. 2: 拉伸屈服强度(X-Y) Tensile yield strength(X-Y)no standard statedin the median
Tensile break strength Z42.70 ± 0.51 MPap. 2: 拉伸断裂强度(Z) Tensile breaking strength(Z)no standard statedin the median
Elongation at break XY14.04 ± 7.77 %p. 2: 断裂伸长率(X-Y) Elongation at break(X-Y)no standard statedin the median
Elongation at break Z4.51 ± 0.82 %p. 2: 断裂伸长率(Z)no standard statedin the median
Elongation at yield XY4.19 ± 0.06 %p. 2: 屈服伸长率(X-Y) Yield elongation(X-Y)no standard statedlisted under other properties
Flexural modulus XY1895.07 ± 36.19 MPap. 3: Bending modulus(X-Y)no standard statedin the median
Flexural strength XY71.40 ± 0.74 MPap. 3: 弯曲强度(X-Y) Bending strength(X-Y)no standard statedin the median
Charpy impact strength XY16.39 ± 2.16 KJ/㎡p. 3: Charpy impact strength(X-Y)
ISO 179As the sheet prints it: ISO 179; notched
notched		not in the median: sold as toughened, set apart
HDT at 0.45 MPa70 °Cp. 2: Determination of temperature
no standard namedAs the sheet prints it: 0.45MPa
in the median
HDT at 1.8 MPa65 °Cp. 2: 热变形温度 ISO 75:Method A
ISO 75As the sheet prints it: 1.8MPa ISO 75
in the median
Glass transition temperature80 °Cp. 2: Density 玻璃化转变温度 ISO 11357 Glass transition temperaturespecimen not stated, ISO 11357in the median
Density1.27 g/cm³p. 2: 密度 ISO 1183 Densityspecimen not stated, ISO 1183
Melt mass-flow rate7 g/10minp. 2: Glass transition temperature 熔融指数 220℃,2.16kg Melt indexspecimen not stated,
no standard namedAs the sheet prints it: 220℃,2.16kg
tested at 220°C

Print settings

Nozzle
230–260 °Cown data sheet
Bed
70–80 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (5)
  • BenefitsQIDI ToughPETG-HF is a toughness modified PETG developed specifically for FDM, which provides excellent high speed printability by improving material flow and have better mechanical strength and heat resistance compared to PLA.QIDI, Technical Data Sheet QIDI ToughPETG-HFp. 1
  • BenefitsQIDI has improved the notch impact strength of QIDI ToughPETG-HF to more than twice that of ordinary PETG without affecting the interlayer bonding strength in the Z-axis direction through toughness improvement technology.QIDI, Technical Data Sheet QIDI ToughPETG-HFp. 1
  • BenefitsQIDI ToughPETG-HF has excellent material flow and good modeling effect, which can achieve perfect printing results in most printers.QIDI, Technical Data Sheet QIDI ToughPETG-HFp. 1
  • Supports and removalS-White Quick-Remove Support MaterialQIDI, Technical Data Sheet QIDI ToughPETG-HFp. 3
  • Printing adviceSince the bonding between ToughPETG-HF and PC material base plate is very strong, it is recommended to increase the spacing between the first layer of the model and the base plate when printing a larger subface.QIDI, Technical Data Sheet QIDI ToughPETG-HFp. 4
Eryone Hyper Speed PETGStrength XY, MPa50.1Strength Z, MPa21.7Modulus XY, GPa1.33Charpy notched, kJ/m²1.25HDT 0.45, °C69HDT 1.8, °C—Price, CAD/kg—Nozzle, °C240–280Bed, °C75–80Chamber, °CnoneDrying, °C, h65–756–8 h

Eryone Hyper Speed PETGEryone

Published values

PropertyAs publishedConditionsOn the Overview
Eryone, Technical Data Sheet (TDS) Hyper Speed PETG13 valuesUnless a row says otherwise: printed specimen
print settingsprinting temperature=240 ° C, printing speed=100mm/s, base plate 80 ° C, filling=100%, nozzle diameter=0.4mm
Tensile modulus XY1332.1 MPap. 2: Elastic modulus X-Y 50mm/min GB/T 1040.1-2006 MPa
GB/T 1040As the sheet prints it: 50mm/min GB/T 1040.1-2006
in the median
Tensile modulus Z (X-Z)1034.2 MPap. 2: Elastic modulus X-Z MPano standard statedin the median
Tensile strength (yield or break not stated) XY50.1 MPap. 2: Tensile strength X-Y 50mm/min GB/T 1040.4 MPa
GB/T 1040As the sheet prints it: 50mm/min GB/T 1040.4
in the median
Tensile strength (yield or break not stated) Z (X-Z)21.7 ± 2 MPap. 2: Tensile strength X-Z 50mm/min GB/T 1843 MPa
GB/T 1843As the sheet prints it: 50mm/min GB/T 1843
in the median
Elongation at break XY4.1 %p. 2: Elongation at break X-Y 50mm/min GB/T 1040.4 %
GB/T 1040As the sheet prints it: 50mm/min GB/T 1040.4
in the median
Elongation at break Z (X-Z)2.7 %p. 2: Elongation at break X-Z 50mm/min GB/T 1040.2 %
GB/T 1040.2As the sheet prints it: 50mm/min GB/T 1040.2
in the median
Flexural modulus orientation not stated1742.3 MPap. 2: Bending modulus 2mm/min GB/T 9341 MPa
GB/T 9341As the sheet prints it: 2mm/min GB/T 9341
in the median
Flexural strength orientation not stated66.1 MPap. 2: Bending strength 2mm/min GB/T 9341 MPa
GB/T 9341As the sheet prints it: 2mm/min GB/T 9341
in the median
Charpy impact strength1.25 kJ/m2p. 2: Charpy Impact strenght 2.75J GB/T 1043.1-2008 kJ/m2
GB/T 1043.1As the sheet prints it: 2.75J GB/T 1043.1-2008
notched		in the median
HDT at 0.45 MPa69 ℃p. 1: Heat distortion temperature(° C) ASTM D648 0.45MPa ℃specimen not stated; its document points to a moulded or resin bar,
ASTM D648As the sheet prints it: 0.45MPa ASTM D648
print settings not stated		not in the median: set apart (never used to pass), test bar not described as printed
Vicat softening temperature70 ℃p. 1: Vicat Softening Temperature(° C) ASTM D1525 (ISO 306 GB/T 1633) ℃specimen not stated, ASTM D1525, ISO 306, GB/T 1633print settings not stated
Density1.28 g/cm³p. 1: Density(g/cm³ at 21.5 ° C) ASTM D792 (ISO 1183, GB/T 1033) g/cm³specimen not stated,
ASTM D792, ISO 1183, GB/T 1033As the sheet prints it: g/cm³ at 21.5 ° C) ASTM D792 ISO 1183 GB/T 1033
tested at 21.5°Cprint settings not stated
Melt mass-flow rate28.2 ± 2.7 g/10minp. 1: Melt Index(g/10 min) 220 ° C, 10kg 240 ° C, 2.16 kg g/10minspecimen not stated,
no standard namedAs the sheet prints it: g/10 min 220 ° C 10kg 240 ° C 2.16 kg
tested at 220°Cprint settings not stated

Print settings

Nozzle
240–280 °Cown data sheet
Bed
75–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65–75 °C for 6–8 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (7)
Eryone Standard PETGStrength XY, MPa47.5Strength Z, MPa25.7Modulus XY, GPa1.24Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C67Price, CAD/kg—Nozzle, °C230–250Bed, °C75–80Chamber, °CnoneDrying, °C, h8012 h

Eryone Standard PETGEryone

Published values

PropertyAs publishedConditionsOn the Overview
Eryone, Technical Data Sheet (TDS) Standard PETG15 valuesUnless a row says otherwise: printed specimen
Tensile modulus XY1242.5 MPap. 2: Elastic modulus X-Y MPano standard stated
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
in the median
Tensile modulus Z (X-Z)852.1 MPap. 2: Elastic modulus X-Z MPano standard stated
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
in the median
Tensile strength (yield or break not stated) XY47.5 MPap. 2: Tensile strength X-Y 50mm/min GB/T 1040.4 MPa
GB/T 1040As the sheet prints it: 50mm/min GB/T 1040.4
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
in the median
Tensile strength (yield or break not stated) Z (X-Z)25.7 MPap. 2: Tensile strength X-Z 50mm/min GB/T 1843 MPa
GB/T 1843As the sheet prints it: 50mm/min GB/T 1843
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
in the median
Elongation at break XY4.8 %p. 2: Elongation at break X-Y 50mm/min GB/T 1040.4 %
GB/T 1040As the sheet prints it: 50mm/min GB/T 1040.4
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
in the median
Elongation at break Z (X-Z)2.9 %p. 2: Elongation at break X-Z 50mm/min GB/T 1040.4 %
GB/T 1040As the sheet prints it: 50mm/min GB/T 1040.4
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
in the median
Flexural modulus orientation not stated2073.2 MPap. 2: Bending modulus 2mm/min GB/T 9341 MPa
GB/T 9341As the sheet prints it: 2mm/min GB/T 9341
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
in the median
Flexural strength orientation not stated77.1 MPap. 2: Bending strength 2mm/min GB/T 9341 MPa
GB/T 9341As the sheet prints it: 2mm/min GB/T 9341
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
in the median
Charpy impact strength orientation not stated2.63 kJ/m2p. 2: Charpy Impact strenght
GB/T 1843As the sheet prints it: GB/T 1843; energy=2.75J
not in the median: notch not stated
Impact strength, test unclear2.63 kJ/m2p. 2: Charpy Impact strenght 2.75J GB/T 1843 kJ/m2
GB/T 1843As the sheet prints it: 2.75J GB/T 1843
Which test: probably Izod
print settingsprinting temperature=240 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
listed under other properties
HDT at 1.8 MPa67 ℃p. 1: Heat distortion temperature(° C) ASTM D648 1.8MPa 0.45MPa ℃specimen not stated; its document points to a moulded or resin bar,
ASTM D648As the sheet prints it: 1.8MPa ASTM D648
not in the median: set apart (never used to pass), test bar not described as printed
Glass transition temperature68 ℃p. 1: Glass transition temperature (° C) DSC, 10 ° C/min ℃specimen not stated,
DSCAs the sheet prints it: ° C DSC
in the median
Vicat softening temperature78 ℃p. 1: Vicat Softening Temperature(° C) ASTM D1525 (ISO 306 GB/T 1633) ℃specimen not stated, ASTM D1525, ISO 306, GB/T 1633
Density1.25 g/cm³p. 1: Density(g/cm³ at 21.5 ° C) ASTM D792 (ISO 1183, GB/T 1033) g/cm³specimen not stated,
ASTM D792, ISO 1183, GB/T 1033As the sheet prints it: g/cm³ at 21.5 ° C) ASTM D792 ISO 1183 GB/T 1033
tested at 21.5°C
Melt mass-flow rate18 ± 2 g/10minp. 1: Melt Index(g/10 min) 220 ° C, 10kg 240 ° C, 2.16 kg g/10minspecimen not stated,
no standard namedAs the sheet prints it: g/10 min 220 ° C 10kg 240 ° C 2.16 kg
tested at 220°C

Print settings

Nozzle
230–250 °Cown data sheet
Bed
75–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
80 °C for 12 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (3)
eSUN PETGStrength XY, MPa34.8Strength Z, MPa28.6Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C64HDT 1.8, °C—Price, CAD/kg26Nozzle, °C230–260Bed, °C75–90Chamber, °CnoneDrying, °C, h60≥ 8 h

eSUN PETGeSUN

Published values

PropertyAs publishedConditionsOn the Overview
eSUN, Technical Data Sheet PETG12 valuesThe same values also in eSUN, PETG Technical Data Sheet.Unless a row says otherwise: printed specimen
print settingsExtruder Temperature 260℃; Build Platform Temperature 80℃; Outer Layer Number 2; Top/Bottom Layer Number 3; Infill Density 100%; Fan Speed 100%; Based on Bambu P1S 0.4 mm nozzle and Orcaslicer 2.1.0 Beta
Tensile strength (yield or break not stated) XY34.77 Mpap. 2: Tensile Strength (X-Y) GB/T 1040GB/T 1040in the median
Tensile strength (yield or break not stated) Z28.65 MPap. 2: Tensile Strength (Z) GB/T 1040GB/T 1040in the median
Elongation at break XY5.15 %p. 2: Elongation at Break (X-Y) GB/T 1040GB/T 1040in the median
Elongation at break Z3.91 %p. 2: Elongation at Break (Z) GB/T 1040GB/T 1040in the median
Flexural modulus XY1228.33 MPap. 2: Flexural Modulus (X-Y) GB/T 9341GB/T 9341in the median
Flexural modulus Z1276.45 Mpap. 2: Flexural Modulus (Z) GB/T 9341GB/T 9341in the median
Flexural strength XY41.9 MPap. 2: Flexural Strength (X-Y) GB/T 9341GB/T 9341in the median
Flexural strength Z39.9 Mpap. 2: Flexural Strength (Z) GB/T 9341GB/T 9341in the median
Izod impact strength XY4.86 KJ/m²p. 2: IZOD Impact Strength (X-Y) GB/T 1843GB/T 1843not in the median: notch not stated
Izod impact strength Z1.78 KJ/m²p. 2: IZOD Impact Strength (Z) GB/T 1843GB/T 1843not in the median: notch not stated
HDT at 0.45 MPa64 ℃p. 1: Heat Distortion Temperature GB/T 1634
GB/T 1634As the sheet prints it: GB/T 1634 0.45Mpa
print settings not stated		in the median
Density1.27 g/cm3p. 1: Density GB/T 1033also in eSUN, PETG Technical Data Sheetspecimen not stated, GB/T 1033print settings not stated
eSUN, PETG Technical Data Sheet6 valuesUnless a row says otherwise: moulded bar (resin supplier's value)
Tensile strength (yield or break not stated) orientation not stated52.2 MPap. 1: Tensile Strength GB/T 1040GB/T 1040not in the median: measured on a moulded bar
Elongation at break orientation not stated83 %p. 1: Elongation at Break GB/T 1040GB/T 1040not in the median: measured on a moulded bar
Flexural modulus orientation not stated1073 MPap. 1: Flexural Modulus GB/T 9341GB/T 9341not in the median: measured on a moulded bar
Flexural strength orientation not stated58.1 MPap. 1: Flexural Strength GB/T 9341GB/T 9341not in the median: measured on a moulded bar
Izod impact strength4.7 kJ/m2p. 1: IZOD Impact StrengthGB/T 1843not in the median: measured on a moulded bar
HDT64 ℃p. 1: Heat distortion TemperatureGB/T 1634not in the median: measured on a moulded bar

Print settings

Nozzle
230–260 °Cown data sheet
Bed
75–90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60 °C for ≥ 8 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): nozzle in eSUN, PETG Technical Data Sheet.

Its 2 print profiles, in the documents' words
  • Nozzle 230-260℃; Bed 75-90℃; Drying 60℃ >8HeSUN, Technical Data Sheet PETGp. 2: Recommended printing settings: Nozzle Temperature; p. 2: Drying Preparation; p. 2: Build Platform Type
  • Nozzle 230-250℃; Bed 75-90°C; Chamber no need of temperature chambereSUN, PETG Technical Data Sheetp. 2: Recommended printing settings; p. 1: Description

Price

26 CAD/kgthe median of its 2 regular prices in the sample

2 listings
  • Shop3D.ca: 26 CAD/kgeSun PETG Filament - 1kg / 1.75 / Natural (SKU PETG-P175N1)in its price; seen 30 Sep 2026
  • DigitMakers: 26 CAD/kgeSUN PETG Filament 1.75 mm 1kg Spool Various Colors / Grey (SKU ESUN-FL-PETG-1.75-1KG-GRY)in its price; seen 30 Sep 2026

Its 3 documents

What the maker says (9)
eSUN PETG-MatteModified: cosmetic dense fillerStrength XY, MPa49.8Strength Z, MPa19.5Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C71HDT 1.8, °C—Price, CAD/kg20Nozzle, °C240–260Bed, °C70Chamber, °CnoneDrying, °C, h60

eSUN PETG-MatteeSUN

Modified: cosmetic dense filler. Its values are kept out of the material's medians.

Published values

PropertyAs publishedConditionsOn the Overview
eSUN, Technical Data Sheet PETG-Matte12 valuesUnless a row says otherwise: printed specimen
print settingsExtruder Temperature 250℃; Build Platform Temperature 70℃; Outer Layer Number 2; Top/Bottom Layer Number 3; Infill Density 100%; Fan Speed 100%; Based on Bambu P1S 0.4 mm nozzle and Orcaslicer 2.1.0 Beta
Tensile strength (yield or break not stated) XY49.79 Mpap. 2: Tensile Strength (X-Y) GB/T 1040GB/T 1040not in the median: added filler or additive
Tensile strength (yield or break not stated) Z19.51 MPap. 2: Tensile Strength (Z) GB/T 1040GB/T 1040not in the median: added filler or additive
Elongation at break XY13.49 %p. 2: Elongation at Break (X-Y) GB/T 1040GB/T 1040not in the median: added filler or additive
Elongation at break Z2.71 %p. 2: Elongation at Break (Z) GB/T 1040GB/T 1040not in the median: added filler or additive
Flexural modulus XY2405.17 MPap. 2: Flexural Modulus (X-Y) GB/T 9341GB/T 9341not in the median: added filler or additive
Flexural modulus Z1757.03 Mpap. 2: Flexural Modulus (Z) GB/T 9341GB/T 9341not in the median: added filler or additive
Flexural strength XY77.1 MPap. 2: Flexural Strength (X-Y) GB/T 9341GB/T 9341not in the median: added filler or additive
Flexural strength Z30.1 Mpap. 2: Flexural Strength (Z) GB/T 9341GB/T 9341not in the median: added filler or additive
Izod impact strength XY2.2 KJ/m²p. 2: IZOD Impact Strength (X-Y) GB/T 1843GB/T 1843not in the median: notch not stated
Izod impact strength Z2.29 KJ/m²p. 2: IZOD Impact Strength (Z) GB/T 1843GB/T 1843not in the median: notch not stated
HDT at 0.45 MPa71.1 ℃p. 1: Heat Distortion Temperature GB/T 1634
GB/T 1634As the sheet prints it: GB/T 1634 0.45Mpa
print settings not stated		not in the median: added filler or additive
Density1.35 g/cm3p. 1: Density GB/T 1033specimen not stated, GB/T 1033print settings not stated

Print settings

Nozzle
240–260 °Cown data sheet
Bed
70 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
60 °Cown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 240-260℃; Bed 70℃; Drying 60℃eSUN, Technical Data Sheet PETG-Mattep. 2: Recommended printing settings: Nozzle Temperature; p. 2: Drying Preparation; p. 2: Build Platform Type

Price

20 CAD/kgits one regular price in the sample

1 listing
  • DigitMakers: 20 CAD/kgeSUN PETG Matte Refill 1.75 mm 1kg - Various Colors / White (SKU ESUN-PETG-MATTE-RFL-WHT)in its price; seen 30 Sep 2026

Its 2 documents

What the maker says (2)
eSUN PETG+Strength XY, MPa48Strength Z, MPa26Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg25Nozzle, °C230–250Bed, °C75–90Chamber, °CnoneDrying, °C, h60≥ 8 h

eSUN PETG+eSUN

Published values

PropertyAs publishedConditionsOn the Overview
eSUN, PETG+ Technical Data Sheet12 valuesUnless a row says otherwise: printed specimen
print settingsExtruder Temperature 245℃; Build Platform Temperature 70℃; Outer Layer Number 2; Top/Bottom Layer Number 3; Infill Density 100%; Fan Speed 20%; Based on Bambu P1S 0.4mm nozzle and Orcaslicer 2.1.0 Beta
Tensile strength (yield or break not stated) XY48 Mpap. 2: Tensile Strength (X-Y) GB/T 1040GB/T 1040in the median
Tensile strength (yield or break not stated) Z26 MPap. 2: Tensile Strength (Z) GB/T 1040GB/T 1040in the median
Elongation at break XY5.56 %p. 2: Elongation at Break (X-Y) GB/T 1040GB/T 1040in the median
Elongation at break Z3.31 %p. 2: Elongation at Break (Z) GB/T 1040GB/T 1040in the median
Flexural modulus XY1993.64 MPap. 2: Flexural Modulus (X-Y) GB/T 9341GB/T 9341in the median
Flexural modulus Z1687.64 Mpap. 2: Flexural Modulus (Z) GB/T 9341GB/T 9341in the median
Flexural strength XY83.2 MPap. 2: Flexural Strength (X-Y) GB/T 9341GB/T 9341in the median
Flexural strength Z53.2 Mpap. 2: Flexural Strength (Z) GB/T 9341GB/T 9341in the median
Izod impact strength XY2.21 KJ/m²p. 2: IZOD Impact Strength (X-Y) GB/T 1843GB/T 1843not in the median: notch not stated
Izod impact strength Z2.02 KJ/m²p. 2: IZOD Impact Strength (Z) GB/T 1843GB/T 1843not in the median: notch not stated
HDT at 0.45 MPa70 ℃p. 2: Heat Distortion Temperature GB/T 1634
GB/T 1634As the sheet prints it: GB/T 1634 0.45Mpa
print settings not stated		in the median
Density1.27 ± 0.01 g/cm3p. 1: Density GB/T 1033specimen not stated, GB/T 1033print settings not stated

Print settings

Nozzle
230–250 °Cown data sheet
Bed
75–90 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
60 °C for ≥ 8 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 230-250℃; Bed 75-90℃; Drying 60℃>8HeSUN, PETG+ Technical Data Sheetp. 3: Recommended printing settings: Nozzle Temperature; p. 3: Drying Preparation; p. 3: Build Platform Type

Price

25 CAD/kgits one regular price in the sample

1 listing
  • DigitMakers: 25 CAD/kgeSUN PETG+ Refill 1.75 mm 1kg Spool Various Colors / Black (SKU ESUN-PETG+-REFILL-1.75MM-1KG-BLCK)in its price; seen 30 Sep 2026

Its 2 documents

What the maker says (5)
SUNLU PETGStrength XY, MPa48Strength Z, MPa—Modulus XY, GPa2.99Charpy notched, kJ/m²3IzodHDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–240Bed, °C60–70Chamber, °CnoneDrying, °C, h50

SUNLU PETGSUNLU

Published values

PropertyAs publishedConditionsOn the Overview
SUNLU, Product Information PETG14 values
Tensile modulus orientation not stated2990 MPap. 1: Young’s Modulus ASTM D638 1mm/min MPa
ASTM D638As the sheet prints it: 1mm/min ASTM D638
not in the median: set apart (never used to pass), test bar not described as printed
Tensile strength (yield or break not stated) orientation not stated61.4 MPap. 1: Tensile Strength ASTM D638 50mm/min MPa
ASTM D638As the sheet prints it: 50mm/min ASTM D638
not in the median: another value of this product is in it
Elongation at break orientation not stated5.3 %p. 1: Elongation at break ASTM D638 50mm/min %
ASTM D638As the sheet prints it: 50mm/min ASTM D638
not in the median: another value of this product is in it
Flexural modulus orientation not stated1686 MPap. 1: Flexural Modulus ASTM D790 2mm/min MPa
ASTM D790As the sheet prints it: 2mm/min ASTM D790
not in the median: another value of this product is in it
Flexural strength orientation not stated74.8 MPap. 1: Flexural Strength ASTM D790 2mm/min MPa
ASTM D790As the sheet prints it: 2mm/min ASTM D790
not in the median: another value of this product is in it
Izod impact strength35 J/mp. 1: IZOD Impact Notched ASTM D256 3.2mm, 23℃ J/m
ASTM D256As the sheet prints it: 3.2mm 23℃ ASTM D256
tested at 23°C		not in the median: in J/m
HDT at 0.45 MPa63 ℃p. 1: Heat Deflection (HDT) ASTM D648 0.45MPa ℃
ASTM D648As the sheet prints it: 0.45MPa ASTM D648
not in the median: another value of this product is in it
Glass transition temperature65.5 ℃p. 1: Glass Transition(Tg) ASTM D7426 10℃/min ℃ASTM D7426not in the median: another value of this product is in it
Vicat softening temperature68 ℃p. 1: Vicat Softening Temp. ASTM D1525 5kg,50℃/h ℃
ASTM D1525As the sheet prints it: 5kg ASTM D1525
Melting temperature128 ℃p. 1: Melting Point ASTM D7426 10℃/min ℃ASTM D7426
Decomposition temperature423 ℃p. 1: @5%Decomposition Temp. ASTM E2402 20℃/min ℃
ASTM E2402As the sheet prints it: E2402
Density1.3 g/cm3p. 1: Density ASTM D792 23℃ g/cm3
ASTM D792As the sheet prints it: 23℃ ASTM D792
tested at 23°C
Melt mass-flow rate14 g/10minp. 1: Melt Flow Rate ASTM D1238 210℃/2.16kg g/10min
ASTM D1238As the sheet prints it: 210℃/2.16kg ASTM D1238
tested at 210°C
Mould shrinkage orientation not stated0.1-0.5 %p. 1: Mold Shrinkage ASTM D955 23℃ %
ASTM D955As the sheet prints it: 23℃ ASTM D955
tested at 23°C
SUNLU, 三绿物性表 ISO PETG12 values
Tensile strength (yield or break not stated) XY48 ± 10 MPap. 1: 拉伸强度(X-Y) Tensile Strength ISO 527/2 50 mm/min MPa
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
print settings测试样条打印速度 150 mm/s，打印温度 255 ℃。填充 100%，走线方式为 90 度。
in the median
Elongation at break XY11 ± 5 %p. 1: 断裂伸长率(X-Y) Elongation at break ISO 527/2 50 mm/min %
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
print settings测试样条打印速度 150 mm/s，打印温度 255 ℃。填充 100%，走线方式为 90 度。
in the median
Flexural modulus XY2100 ± 300 MPap. 1: 弯曲模量(X-Y) Flexural Modulus ISO 178 2 mm/min MPa
ISO 178As the sheet prints it: 2 mm/min ISO 178
print settings测试样条打印速度 150 mm/s，打印温度 255 ℃。填充 100%，走线方式为 90 度。
in the median
Flexural strength XY70 ± 10 MPap. 1: 弯曲强度(X-Y) Flexural Strength ISO 178 2 mm/min MPa
ISO 178As the sheet prints it: 2 mm/min ISO 178
print settings测试样条打印速度 150 mm/s，打印温度 255 ℃。填充 100%，走线方式为 90 度。
in the median
Izod impact strength XY3.0 ± 1 KJ/m2p. 1: 悬臂梁缺口冲击强度(X-Y) Izod Impact ISO 180 23℃ KJ/m2 Strength of Notched Specimen
ISO 180As the sheet prints it: 23℃ KJ/m2 Strength of Specimen ISO 180
tested at 23°C
print settings测试样条打印速度 150 mm/s，打印温度 255 ℃。填充 100%，走线方式为 90 度。
in the median
Izod impact strength ZX5.0 ± 2 KJ/m2p. 1: 悬臂梁无缺口冲击强度(Z-X) Izod Impact ISO 180 23℃ KJ/m2 Strength of Unnotched Specimen
ISO 180As the sheet prints it: 23℃ KJ/m2 Strength of Specimen ISO 180
tested at 23°C
print settings测试样条打印速度 150 mm/s，打印温度 255 ℃。填充 100%，走线方式为 90 度。
not in the median: unnotched
Hardness80 Shore Dp. 1: 邵氏硬度 Shore Hardness ISO 868 23℃ HA/HD
ISO 868As the sheet prints it: 23℃ HA/HD ISO 868
tested at 23°C		in the median
HDT XY, at 0.45 MPa70 ± 5 ℃p. 1: 热变形温度(X-Y) Heat Distortion (HDT) ISO 75 0.45 MPa ℃
ISO 75As the sheet prints it: 0.45 MPa ISO 75
in the median
Glass transition temperature79.4 ℃p. 1: 玻璃化转变温度 Glass Transition (Tg) ISO 11357-2 10 ℃/min ℃
ISO 11357As the sheet prints it: ISO 11357-2
in the median
Melting temperature195 ℃p. 1: 熔点温度 Melting Temperature ISO 11357-3 10 ℃/min ℃
ISO 11357As the sheet prints it: ISO 11357-3
Density1.27 g/cm3p. 1: 密度 Density ISO 1183 23℃ g/cm3
ISO 1183As the sheet prints it: 23℃ ISO 1183
tested at 23°C
Melt mass-flow rate5.7 ± 3 g/10 minp. 1: 熔体指数 Melt Mass-flow Rate ISO 1133 190℃/2.16 kg g/10 min
ISO 1133As the sheet prints it: 190℃/2.16 kg ISO 1133
tested at 190°C

Print settings

Nozzle
230–240 °Cown data sheet
Bed
60–70 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
50 °Cown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its 3 print profiles, in the documents' words
  • Nozzle 230-240℃; Bed 60-70℃; Chamber Room Temperature; Drying 50℃SUNLU, Product Information PETGp. 2: Recommended printing settings; p. 2: Nozzle Print Temp.; p. 2: Print Platform Temp.; p. 2: Room Temp.
  • Nozzle 240-260; Bed 60-70℃; Chamber 常温; Drying 60-65℃SUNLU, 三绿物性表 ISO PETGp. 2: 喷嘴温度 Nozzle Temp., 平台温度 Plate Temp.
  • Nozzle 240-260℃; Bed 60-70℃; Chamber Room Temperature; Drying 50℃SUNLU, Product Information PETGp. 2: Recommended Printing Parameters: Zonal Temperature, 100-200mm/s

Price

Not in the price sample.

Its 3 documents

What the maker says (4)
Fiberlogy EASY PET-GData sheet shared with Fiberlogy R PET-GStrength XY, MPa51Strength Z, MPa—Modulus XY, GPa2.8Charpy notched, kJ/m²5IzodHDT 0.45, °C68HDT 1.8, °C62Price, CAD/kg—Nozzle, °C220–250Bed, °C90Chamber, °CnoneDrying, °C, h604 h

Fiberlogy EASY PET-GFiberlogy

Data sheet shared with Fiberlogy R PET-G: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy EASY PET-G11 valuesUnless a row says otherwise: specimen not stated; its document points to a moulded or resin bar
Tensile modulus orientation not stated2800 MPap. 1: Tensile Modulus ISO 527 MPaISO 527not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated51 MPap. 1: Tensile Strength @ Yield ISO 527 MPaISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated29 %p. 1: Elongation @ Break ISO 527 %ISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4 %p. 1: Elongation @ Yield ISO 527 %specimen not stated, ISO 527listed under other properties
Flexural modulus orientation not stated2000 MPap. 1: Flexular Modulus ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated70 MPap. 1: Flexular Strength ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength5 kJ/m2p. 1: Izod Impact Strength (Notched) @ 23°C ISO 180 kJ/m2
ISO 180As the sheet prints it: 23°C ISO 180
tested at 23°C		not in the median: set apart (never used to pass), test bar not described as printed
HDT at 0.45 MPa68 °Cp. 1: Heat Distortion Temperature @ 0.45 MPa ISO 75 °C
ISO 75As the sheet prints it: 0.45 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa62 °Cp. 1: Heat Distortion Temperature @ 1.8 MPa ISO 75 °C
ISO 75As the sheet prints it: 1.8 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
Glass transition temperature80 °Cp. 1: Glass Transition Temperature Tg ASTM D3418 °Cspecimen not stated, ASTM D3418in the median
Vicat softening temperature78 °Cp. 1: Vicat Softening Temperature ISO 306 °Cspecimen not stated, ISO 306
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy EASY PET-G4 valuesThe same values also in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy EASY PET-G.Unless a row says otherwise: specimen not stated
Tensile break strength orientation not stated51 MPap. 1: Tensile Strength @ Break ISO 527 MPaalso in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy EASY PET-Gspecimen not stated; its document points to a moulded or resin bar, ISO 527not in the median: another value of this product is in it
Glass transition temperature82 °Cp. 1: Glass Transition Temperature Tg DSC °Calso in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy EASY PET-Gno standard statednot in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Continuous service temperature50 °Cp. 1: Continuous Use Temperature (UL Yellow Card) UL 746 °Calso in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy EASY PET-G
no standard namedAs the sheet prints it: UL 746
Density1.27 g/cm³p. 1: Specific GravityISO 1183
Fiberlogy, Easy PETG Filament2 valuesUnless a row says otherwise: specimen not stated
Izod impact strength orientation not stated5 kJ/m²p. 1: Izod impact strength (notched) @ 23°CISO 180tested at 23°Cnot in the median: another value of this product is in it
Density1.29 g/cm³p. 1: Densityno standard stated

Print settings

Nozzle
220–250 °Cown data sheet
Bed
90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60 °C for 4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its 4 print profiles, in the documents' words

Price

Not in the price sample.

Its 5 documents

What the maker says (1)
  • Good forIt is ideal for users seeking a balance between high mechanical properties and printability comparable to EASY PLA.Fiberlogy, Easy PETG Filamentp. 1
Fiberlogy R PET-GData sheet shared with Fiberlogy EASY PET-GStrength XY, MPa51Strength Z, MPa—Modulus XY, GPa2.8Charpy notched, kJ/m²5IzodHDT 0.45, °C68HDT 1.8, °C62Price, CAD/kg—Nozzle, °C220–250Bed, °C90Chamber, °CnoneDrying, °C, h604 h

Fiberlogy R PET-GFiberlogy

Data sheet shared with Fiberlogy EASY PET-G: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy R PET-G11 valuesUnless a row says otherwise: specimen not stated; its document points to a moulded or resin bar
Tensile modulus orientation not stated2800 MPap. 1: Tensile Modulus ISO 527 MPaISO 527not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated51 MPap. 1: Tensile Strength @ Yield ISO 527 MPaISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated29 %p. 1: Elongation @ Break ISO 527 %ISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4 %p. 1: Elongation @ Yield ISO 527 %specimen not stated, ISO 527listed under other properties
Flexural modulus orientation not stated2000 MPap. 1: Flexular Modulus ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated70 MPap. 1: Flexular Strength ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength5 kJ/m2p. 1: Izod Impact Strength (Notched) @ 23°C ISO 180 kJ/m2
ISO 180As the sheet prints it: 23°C ISO 180
tested at 23°C		not in the median: set apart (never used to pass), test bar not described as printed
HDT at 0.45 MPa68 °Cp. 1: Heat Distortion Temperature @ 0.45 MPa ISO 75 °C
ISO 75As the sheet prints it: 0.45 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa62 °Cp. 1: Heat Distortion Temperature @ 1.8 MPa ISO 75 °C
ISO 75As the sheet prints it: 1.8 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
Glass transition temperature80 °Cp. 1: Glass Transition Temperature Tg ASTM D3418 °Cspecimen not stated, ASTM D3418in the median
Vicat softening temperature78 °Cp. 1: Vicat Softening Temperature ISO 306 °Cspecimen not stated, ISO 306
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy R PET-G3 valuesUnless a row says otherwise: specimen not stated
Tensile break strength orientation not stated51 MPap. 1: Tensile Strength @ Break ISO 527 MPaspecimen not stated; its document points to a moulded or resin bar, ISO 527not in the median: another value of this product is in it
Glass transition temperature82 °Cp. 1: Glass Transition Temperature Tg DSC °Cno standard statednot in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Continuous service temperature50 °Cp. 1: Continuous Use Temperature (UL Yellow Card) UL 746 °C
no standard namedAs the sheet prints it: UL 746

Print settings

Nozzle
220–250 °Cown data sheet
Bed
90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60 °C for 4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (1)
  • BenefitsIt combines high mechanical and chemical strength with ease of printing, attractive print appearance, and lower material costs.Fiberlogy, Filament rPETG – S2p. 1
Anycubic PETGStrength XY, MPa52Strength Z, MPa31Modulus XY, GPa1.85Charpy notched, kJ/m²—HDT 0.45, °C69HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–250Bed, °C60–70Chamber, °CnoneDrying, °C, h55–656–8 h

Anycubic PETGAnycubic

Published values

PropertyAs publishedConditionsOn the Overview
Anycubic, Anycubic PETG13 values
Tensile modulus XY1850±100 MPap. 1: Young's Modulus / MPa (X-Y)ISO 527in the median
Tensile strength (yield or break not stated) XY52±1 MPap. 1: Tensile Strength / MPa (X-Y)ISO 527in the median
Tensile strength (yield or break not stated) Z31±3 MPap. 1: Tensile Strength / MPa (Z)ISO 527in the median
Elongation at break XY13±1 %p. 1: Elongation at Break / % (X-Y)ISO 527in the median
Flexural modulus XY2000±50 MPap. 1: Bending Modulus / MPa (X-Y)ISO 178in the median
Flexural strength XY80±2 MPap. 1: Bending Strength / MPa (X-Y)ISO 178in the median
Izod impact strength XY45±2 kJ/m²p. 1: Izod Impact Strength (kJ/m²) (X-Y)ISO 179not in the median: notch not stated
HDT at 0.45 MPa69 ℃p. 2: Heat Deflection Temperature (HDT) ISO 75-2, 0.45MPa ℃
ISO 75As the sheet prints it: 0.45MPa ISO 75-2
in the median
Glass transition temperature74.1 ℃p. 2: Glass Transition Temperature ISO 11357-1, 10℃/min ℃
ISO 11357As the sheet prints it: ISO 11357-1
in the median
Vicat softening temperature72 ℃p. 2: Vicat Softening Temperature (VST) ISO 306, 10N ℃
ISO 306As the sheet prints it: VST 10N ISO 306
Density1.23 g/cm3p. 1: Density/(g/cm³) ISO 1183,at 23°C g/cm3
ISO 1183As the sheet prints it: at 23°C ISO 1183
tested at 23°C
Moisture content0.27 %p. 1: Moisture Content ISO 787-2 %
ISO 787As the sheet prints it: ISO 787-2
Melt mass-flow rate26.3 ± 2.35 g/10minp. 1: Melt Index/ ( g/10min) ISO 1133 g/10min
ISO 1133As the sheet prints it: g/10min ISO 1133

Print settings

Nozzle
230–250 °Cown data sheet
Bed
60–70 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
55–65 °C for 6–8 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 230-250; Bed 60-70; Drying 55-65℃,6-8hAnycubic, Anycubic PETGp. 2: Recommended printing settings; p. 2: Dry Environment; p. 2: Nozzle Temperature; p. 2: Bed Temperature; p. 2: Recommended Printing Parameters

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
  • BenefitsAnycubic PETG is a high-toughness basic filament known for its vibrant colors, durability (impact-resistant), water/weather resistance, and chemical stability.Anycubic, Anycubic PETGp. 1
eSUN PETG BasicStrength XY, MPa68.4Strength Z, MPa35.8Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg20Nozzle, °C245–255Bed, °C70Chamber, °CnoneDrying, °C, h60

eSUN PETG BasiceSUN

Published values

PropertyAs publishedConditionsOn the Overview
eSUN, Technical Data Sheet PETG Basic11 valuesUnless a row says otherwise: printed specimen
Tensile strength (yield or break not stated) XY68.41 MPap. 2: Tensile Strength (X-Y) GB/T 1040GB/T 1040in the median
Tensile strength (yield or break not stated) Z35.84 MPap. 2: Tensile Strength (Z) GB/T 1040GB/T 1040in the median
Elongation at break XY7.56 %p. 2: Elongation at Break (X-Y) GB/T 1040GB/T 1040in the median
Elongation at break Z3.17 %p. 2: Elongation at Break (Z) GB/T 1040GB/T 1040in the median
Flexural modulus XY2636.66 MPap. 2: Flexural Modulus (X-Y) GB/T 9341GB/T 9341in the median
Flexural modulus Z2207.6 MPap. 2: Flexural Modulus (Z) GB/T 9341GB/T 9341in the median
Flexural strength XY100.2 MPap. 2: Flexural Strength (X-Y) GB/T 9341GB/T 9341in the median
Flexural strength Z59.7 MPap. 2: Flexural Strength (Z) GB/T 9341GB/T 9341in the median
Izod impact strength XY2.28 kJ/m2p. 2: IZOD Impact Strength (X-Y) GB/T 1843GB/T 1843not in the median: notch not stated
Izod impact strength Z2.06 kJ/m2p. 2: IZOD Impact Strength (Z) GB/T 1843GB/T 1843not in the median: notch not stated
Density1.27 g/cm3p. 1: Density GB/T 1033specimen not stated, GB/T 1033

Print settings

Nozzle
245–255 °Cown data sheet
Bed
70 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
60 °Cown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 250±5℃; Bed 70℃; Drying 60℃eSUN, Technical Data Sheet PETG Basicp. 2: Recommended printing settings: Extruder Temperature; p. 2: Drying Preparation; p. 2: Build Platform Type

Price

20 CAD/kgits one regular price in the sample

1 listing
  • DigitMakers: 20 CAD/kgeSUN PETG Basic Filament (Clear) - 1.75mm 1kg / Clear (SKU ESUN-PETG-BSC-175-1KG-CLR)in its price; seen 30 Sep 2026

Its 2 documents

What the maker says (3)
QIDI PETG RAPIDOStrength XY, MPa39Strength Z, MPa35Modulus XY, GPa1.7Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg24Nozzle, °C235–275Bed, °C60–80Chamber, °CnoneDrying, °C, h60–654–6 h

QIDI PETG RAPIDOQIDI

Published values

PropertyAs publishedConditionsOn the Overview
QIDI, Technical Data Sheet QIDI PETG Rapido14 values
Tensile modulus XY1700-2000 MPap. 2: Young's Modulus (MPa) (XY)
ISO 527As the sheet prints it: ISO 527; infill=100%
in the median
Tensile modulus XZ2000-2200 MPap. 2: Young's Modulus (MPa) (XZ)
ISO 527As the sheet prints it: ISO 527; infill=100%
not in the median: measured on a bar in another orientation
Tensile modulus ZX1600-1800 MPap. 2: Young's Modulus (MPa) (ZX)
ISO 527As the sheet prints it: ISO 527; infill=100%
not in the median: measured on a bar in another orientation
Tensile strength (yield or break not stated) XY39-47 MPap. 2: Tensile Strength (MPa) (XY)
ISO 527As the sheet prints it: ISO 527; infill=100%
in the median
Tensile strength (yield or break not stated) XZ52-59 MPap. 2: Tensile Strength (MPa) (XZ)
ISO 527As the sheet prints it: ISO 527; infill=100%
not in the median: measured on a bar in another orientation
Tensile strength (yield or break not stated) ZX33-37 MPap. 2: Tensile Strength (MPa) (ZX)
ISO 527As the sheet prints it: ISO 527; infill=100%
not in the median: measured on a bar in another orientation
Elongation at break XY7-10 %p. 2: Elongation at Break (%) (XY)
ISO 527As the sheet prints it: ISO 527; infill=100%
in the median
Elongation at break XZ8-10 %p. 2: Elongation at Break (%) (XZ)
ISO 527As the sheet prints it: ISO 527; infill=100%
not in the median: measured on a bar in another orientation
Elongation at break ZX5-8 %p. 2: Elongation at Break (%) (ZX)
ISO 527As the sheet prints it: ISO 527; infill=100%
not in the median: measured on a bar in another orientation
HDT at 0.45 MPa70 ℃p. 3: Heat Deflection Temperature ISO 75 (HDT)ISO 75in the median
Glass transition temperature~66℃p. 3: GlassTransition TemperatureISO 11357in the median
Vicat softening temperature83 ℃p. 3: Vicat Softening Temperature ISO 306 (VST)ISO 306
Density1.29-1.31 g/cm³p. 3: Density ISO 1183ISO 1183
Melt mass-flow rate5-10 g/10 minp. 3: Melt Flow Rate (MFR)ISO 1133
QIDI, QIDI Filament Guide | Choose the Right Filament3 valuesUnless a row says otherwise: printed bar (its stated orientation says so)
Tensile strength (yield or break not stated) Z35.0MPap. 1: Tensile Strength - Zno standard statedin the median
Flexural modulus XY2100.0MPap. 1: Bending Modulus - XYno standard statedin the median
Flexural strength XY74.5MPap. 1: Bending Strength - XYno standard statedin the median

Print settings

Nozzle
235–275 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
optional: 60–65 °C for 4–6 hown data sheet
Hardened nozzle
not neededown data sheet
Its 2 print profiles, in the documents' words

Price

24 CAD/kgits one regular price in the sample

1 listing
  • QIDI Canada: 24 CAD/kgPETG Rapido / 1 Kg / White HEX Code #FFFFFF (SKU 041WHT-1-1000)in its price; seen 30 Sep 2026

Its 3 documents

What the maker says (5)
SUNLU PETG 2.0Strength XY, MPa43Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²4IzodHDT 0.45, °C71HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–270Bed, °C70–80Chamber, °CnoneDrying, °C, h65

SUNLU PETG 2.0SUNLU

Published values

PropertyAs publishedConditionsOn the Overview
SUNLU, 三绿耗材物性表 ISO PETG 2.018 valuesUnless a row says otherwise: printed specimen
print settings测试样条打印速度 45 mm/s，打印温度 255 ℃。填充 100%，走线方式为 90 度。
Tensile modulus XY500 ± 50 MPaphysically implausiblep. 1: 拉伸模量(X-Y) Tensile Modulus ISO 527/2 50 mm/min MPa
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
not in the median: physically implausible as published
Tensile modulus ZX300 ± 50 MPaphysically implausiblep. 1: 拉伸模量(Z-X) Tensile Modulus ISO 527/2 50 mm/min MPa
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
not in the median: physically implausible as published
Tensile strength (yield or break not stated) XY43 ± 10 MPap. 1: 拉伸强度(X-Y) Tensile Strength ISO 527/2 50 mm/min MPa
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
in the median
Tensile strength (yield or break not stated) ZX20 ± 5 MPap. 1: 拉伸强度(Z-X) Tensile Strength ISO 527/2 50 mm/min MPa
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
not in the median: measured on a bar in another orientation
Elongation at break XY12 ± 5 %p. 1: 断裂伸长率(X-Y) Elongation at break ISO 527/2 50 mm/min %
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
in the median
Elongation at break ZX8 ± 3 %p. 1: 断裂伸长率(Z-X) Elongation at break ISO 527/2 50 mm/min %
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
not in the median: measured on a bar in another orientation
Flexural modulus XY1900 ± 300 MPap. 1: 弯曲模量(X-Y) Flexural Modulus ISO 178 2 mm/min MPa
ISO 178As the sheet prints it: 2 mm/min ISO 178
in the median
Flexural modulus ZX1650 ± 300 MPap. 1: 弯曲模量(Z-X) Flexural Modulus ISO 178 2 mm/min MPa
ISO 178As the sheet prints it: 2 mm/min ISO 178
not in the median: measured on a bar in another orientation
Flexural strength XY70 ± 10 MPap. 1: 弯曲强度(X-Y) Flexural Strength ISO 178 2 mm/min MPa
ISO 178As the sheet prints it: 2 mm/min ISO 178
in the median
Flexural strength ZX35 ± 10 MPap. 1: 弯曲强度(Z-X) Flexural Strength ISO 178 2 mm/min MPa
ISO 178As the sheet prints it: 2 mm/min ISO 178
not in the median: measured on a bar in another orientation
Izod impact strength XY38 ± 8 KJ/m2p. 1: 悬臂梁无缺口冲击强度(X-Y) Izod Impact ISO 180 23℃ KJ/m2 Strength of Unnotched Specimen
ISO 180As the sheet prints it: 23℃ KJ/m2 Strength of Specimen ISO 180
tested at 23°C		not in the median: unnotched
Izod impact strength XY4 ± 2 KJ/m2p. 1: 悬 臂 梁 缺 口 冲 击 强 度 (X-Y) Izod Impact ISO 180 23℃ KJ/m2 Strength of Notched Specimen
ISO 180As the sheet prints it: 23℃ KJ/m2 Strength of Specimen ISO 180
tested at 23°C		in the median
Izod impact strength ZX4.5 ± 2.5 KJ/m2p. 1: 悬臂梁无缺口冲击强度(Z-X) Izod Impact ISO 180 23℃ KJ/m2 Strength of Unnotched Specimen
ISO 180As the sheet prints it: 23℃ KJ/m2 Strength of Specimen ISO 180
tested at 23°C		not in the median: unnotched
Hardness80 Shore Dp. 1: 邵氏硬度 Shore Hardness ISO 868 23℃ HA/HDspecimen not stated,
ISO 868As the sheet prints it: 23℃ HA/HD ISO 868
tested at 23°Cprint settings not stated		in the median
HDT XY, at 0.45 MPa71 ± 4 ℃p. 1: 热变形温度(X-Y) Heat Distortion (HDT) ISO 75 0.45 MPa ℃printed specimen (implied by the document),
ISO 75As the sheet prints it: 0.45 MPa ISO 75
print settings not stated		in the median
Glass transition temperature83 ℃p. 1: 玻璃化转变温度 Glass Transition (Tg) ISO 11357-2 10 ℃/min ℃specimen not stated,
ISO 11357As the sheet prints it: ISO 11357-2
print settings not stated		in the median
Density1.22 g/cm3p. 1: 密度 Density ISO 1183 23℃ g/cm3specimen not stated,
ISO 1183As the sheet prints it: 23℃ ISO 1183
tested at 23°Cprint settings not stated
Melt mass-flow rate3.42 ± 2 g/10 minp. 1: 熔体指数(线材) Melt Mass-flow Rate ISO 1133 210℃/2.16 kg g/10 minspecimen not stated,
ISO 1133As the sheet prints it: 210℃/2.16 kg ISO 1133
tested at 210°Cprint settings not stated

Print settings

Nozzle
230–270 °Cown data sheet
Bed
70–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °Cown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
AzureFilm PETGStrength XY, MPa51Strength Z, MPa38.4Modulus XY, GPa2.98Charpy notched, kJ/m²—HDT 0.45, °C73HDT 1.8, °C—Price, CAD/kg—Nozzle, °C220–240Bed, °C80–90Chamber, °CnoneDrying, °C, h658 h

AzureFilm PETGAzureFilm

Published values

PropertyAs publishedConditionsOn the Overview
AzureFilm, Technical Data Sheet 05.24 PETG21 valuesThe same values also in AzureFilm, Technical Data Sheet PETG TDS.Unless a row says otherwise: printed specimen
print settings100% infill; 2 shells; layer height of 0.2mm
Tensile modulus XY2100 MPap. 1: Tensile Modulus (XY Value)
ISO 527As the sheet prints it: ISO 527-2
not in the median: another value of this product is in it
Tensile modulus Z (ZX)2100 MPap. 1: Tensile Modulus (ZX Value)
ISO 527As the sheet prints it: ISO 527-2
in the median
Tensile modulus XZ2200 MPap. 1: Tensile Modulus (XZ Value)
ISO 527As the sheet prints it: ISO 527-2
not in the median: measured on a bar in another orientation
Tensile strength (yield or break not stated) XY56.7 MPap. 1: Tensile Strength (XY Value)
ISO 527As the sheet prints it: ISO 527-2
not in the median: another value of this product is in it
Tensile strength (yield or break not stated) Z (ZX)38.4 MPap. 1: Tensile Strength (ZX Value)
ISO 527As the sheet prints it: ISO 527-2
in the median
Tensile strength (yield or break not stated) XZ59.2 MPap. 1: Tensile Strength (XZ Value)
ISO 527As the sheet prints it: ISO 527-2
not in the median: measured on a bar in another orientation
Tensile yield strength XY37.5 MPap. 1: Yield Strength (XY Value)
ISO 527As the sheet prints it: ISO 527-2
not in the median: another value of this product is in it
Tensile yield strength Z (ZX)0.0 MPaphysically implausiblep. 1: Yield Strength (ZX Value)
ISO 527As the sheet prints it: ISO 527-2
print settings not stated		not in the median: physically implausible as published
Tensile yield strength XZ38.2 MPap. 1: Yield Strength (XZ Value)
ISO 527As the sheet prints it: ISO 527-2
not in the median: measured on a bar in another orientation
Elongation at yield XY8.7 %p. 1: Strain at Yield (XY Value)
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Elongation at yield Z (ZX)2.3 %p. 1: Strain at Yield (ZX Value)
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Elongation at yield XZ4.3 %p. 1: Strain at Yield (XZ Value)
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Flexural modulus XY2200 MPap. 1: Flexural Modulus (XY Value)ISO 178not in the median: another value of this product is in it
Flexural modulus XZ2300 MPap. 1: Flexural Modulus (XZ Value)ISO 178not in the median: measured on a bar in another orientation
Flexural modulus ZX2200 MPap. 1: Flexural Modulus (ZX Value)ISO 178not in the median: measured on a bar in another orientation
Flexural strength XY82.3 MPap. 1: Flexural Strength (XY Value)ISO 178not in the median: another value of this product is in it
Flexural strength XZ87.4 MPap. 1: Flexural Strength (XZ Value)ISO 178not in the median: measured on a bar in another orientation
Flexural strength ZX64.0 MPap. 1: Flexural Strength (ZX Value)ISO 178not in the median: measured on a bar in another orientation
HDT73 °Cp. 1: Heat deflect. temp.specimen not stated; its document points to a moulded or resin bar, ISO 75print settings not statednot in the median: set apart (never used to pass), test bar not described as printed
Melting temperature180-250 °Cp. 1: Melting temp. ISO 294specimen not stated, ISO 294print settings not stated
Density1.29 g/ccp. 1: Specific gravity ISO 1133also in AzureFilm, Technical Data Sheet PETG TDSspecimen not stated, ISO 1133print settings not stated
AzureFilm, Technical Data Sheet PETG TDS7 valuesUnless a row says otherwise: printed specimen
print settings3D printer: AzureFilm; Nozzle temperature: 230 °C; Infill: 100 %; Slicer: Cura; Bed temperature: 80-90 °C; Shells: /; Nozzle: 0,4 mm; Print speed: 50 mm/s; Layer height: 0,2 mm
Tensile modulus orientation not stated2980 MPap. 1: Tensile Modulus ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
in the median
Tensile yield strength orientation not stated51 MPap. 1: Tensile Yield Stress ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
in the median
Tensile break strength orientation not stated20 MPap. 1: Tensile Stress at Break ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
not in the median: another value of this product is in it
Elongation at break orientation not stated29 %p. 1: Elongation at break ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
in the median
Elongation at yield orientation not stated4 %p. 1: Elongation at yield ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Flexural modulus orientation not stated2040 MPap. 1: Flexural Modulus ISO 178ISO 178in the median
Flexural strength orientation not stated68 MPap. 1: Flexural Strength ISO 178ISO 178in the median

Print settings

Nozzle
220–240 °Cown data sheet
Bed
80–90 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (3)
3D4Makers PETGData sheet shared with iSANMATE PETGStrength XY, MPa53Strength Z, MPa—Modulus XY, GPa3Charpy notched, kJ/m²4.5IzodHDT 0.45, °C68HDT 1.8, °C62Price, CAD/kg—Nozzle, °C210–235Bed, °C50–80Chamber, °C50–70Drying, °C, h658 h

3D4Makers PETG3D4Makers

Data sheet shared with iSANMATE PETG: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
3D4Makers, Technical data sheet 3D printing filament PETG Filament13 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated3000 MPap. 1: Tensile modulus ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Tensile strength (yield or break not stated) orientation not stated53 MPap. 1: Tensile Strength ISO 527-2printed specimen (implied by the document),
ISO 527As the sheet prints it: ISO 527-2
in the median
Tensile yield strength orientation not stated53 MPap. 1: Tensile Yield stress ISO 527-2printed specimen (implied by the document),
ISO 527As the sheet prints it: ISO 527-2
not in the median: another value of this product is in it
Tensile break strength orientation not stated19 MPap. 1: Stress at Break ISO 527-2printed specimen (implied by the document),
ISO 527As the sheet prints it: ISO 527-2
not in the median: another value of this product is in it
Elongation at break orientation not stated31 %p. 1: Nominal elongation at Break ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4 %p. 1: Elongation at Yield ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Tensile strain at strength orientation not stated4 %p. 1: Elongation at Strength ISO 527-2
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Flexural modulus orientation not stated2040 MPap. 1: Flexural Modulus ISO 178ISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated171 MPaphysically implausiblep. 1: Flexural Stress ISO 178ISO 178not in the median: physically implausible as published
Izod impact strength4.5 kJ/m2p. 1: Notched Izod Impact Strength 23°C, 50 % RH ISO 180printed specimen (implied by the document),
ISO 180As the sheet prints it: 23°C 50 % RH ISO 180
tested at 23°C		in the median
Vicat softening temperature78 °Cp. 2: Vicat Softening Temperature ISO 306ISO 306
Density1.29 g/cm3p. 1: Density ASTM D792ASTM D792
Water absorption0.12 %p. 1: Water Absorption ASTM D570ASTM D570

Print settings

Nozzle
210–235 °Cown data sheet
Bed
50–80 °Cown data sheet
Heated chamber
50–70 °CiSANMATE PETG's data sheet, shared
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): nozzle in 3D4Makers, PETG Filament; bed in 3D4Makers, PETG Filament.

Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (7)
  • Surface finishThis material is easy to print and has a glossy and smooth surface finish3D4Makers, PETG Filamentp. 1
  • Good forPETG Filament ( Polyethylene Terepthalate Glycol-modified) is the common thermoplastics of the polyester family and is used in fibers for clothing, bottles for liquids and foods.3D4Makers, PETG Filamentp. 1
  • BenefitsThis material is easy to print3D4Makers, PETG Filamentp. 1
  • Surface finishThis material is easy to print and has a glossy and smooth surface finish, due to great thermal characteristics the print will cool efficiently resulting in minimal warpage and strong layer bonding.3D4Makers, PETG Filamentp. 1
  • BenefitsThe mechanical properties features high impact resistance and excellent flexibility.3D4Makers, PETG Filamentp. 1
  • Printing adviceTo get the best results while printing we advise you to keep the 3D printer in a room where there is hardly any draft and/or temperature fluctuations.3D4Makers, PETG Filamentp. 1
  • Moisture sensitivityWhen the 3D printer is not being used it is important to keep the 3D4MAKERS PETG Filament in a bag and stored in a cool (15-25˚C) and dry room away from UV light until it is used again.3D4Makers, PETG Filamentp. 1
iSANMATE PETGData sheet shared with 3D4Makers PETGStrength XY, MPa53Strength Z, MPa—Modulus XY, GPa3Charpy notched, kJ/m²4.5IzodHDT 0.45, °C68HDT 1.8, °C62Price, CAD/kg—Nozzle, °C210–235Bed, °C50–80Chamber, °C50–70Drying, °C, h658 h

iSANMATE PETGiSANMATE

Data sheet shared with 3D4Makers PETG: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
iSANMATE, PETG17 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated3000 MPap. 1: Tensile Modulus
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Tensile strength (yield or break not stated) orientation not stated53 MPap. 1: Tensile Strengthprinted specimen (implied by the document),
ISO 527As the sheet prints it: ISO 527-2
in the median
Tensile break strength orientation not stated19 MPap. 1: Stress at Breakprinted specimen (implied by the document),
ISO 527As the sheet prints it: ISO 527-2
not in the median: another value of this product is in it
Elongation at break orientation not stated31 %p. 1: Nominal Elongation at Break
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4 %p. 1: Elongation at Yield
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Tensile strain at strength orientation not stated4 %p. 1: Elongation at Stress
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Flexural modulus orientation not stated2040 MPap. 1: Flexural ModulusISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated171 MPaphysically implausiblep. 1: Flexural StressISO 178not in the median: physically implausible as published
Izod impact strength4.5 kJ/m2p. 1: Notched Izod Impact Strength 23ºC, 50 % RHprinted specimen (implied by the document), ISO 180tested at 23°Cin the median
Izod impact strength orientation not statedNo Break Qualitative (no fracture)p. 2: UnnotchedISO 180
after moisture conditioning50% RH
tested at 23°C		not in the median: no number given
Hardness orientation not statedheld back: the sheet's unit or table layout is unclearheld backp. 2: Shore HardnessASTM D2240listed under other properties
HDT at 0.45 MPa68 ºC °Cp. 2: Heat Deflection Temperature 0,45 MPa
ISO 75As the sheet prints it: ISO 75-2, 0,45 MPa
in the median
HDT at 1.8 MPa62 ºC °Cp. 2: Heat Deflection Temperature 1.8 MPa
ISO 75As the sheet prints it: ISO 75-2, 1.8 MPa
in the median
Glass transition temperature80ºC °Cp. 2: Glass Transition TemperatureASTM D3418in the median
Vicat softening temperature78ºC °Cp. 2: Vicat Softening TemperatureISO 306
Density1.29 g/Cm3p. 1: DensityASTM D792
Water absorption0.12 %p. 1: Water AbsorptionASTM D570
3D4Makers, PETG Filament6 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated2020 MPap. 1: Tensile modulusISO 527not in the median: another value of this product is in it
Tensile yield strength orientation not stated50 MPap. 1: Tensile strength at yieldISO 527not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Flexural modulus orientation not stated2050 MPap. 1: Flexural modulusISO 178not in the median: another value of this product is in it
Charpy impact strength orientation not stated8,1 kJ/m²p. 1: Impact strength - Charpy method 23ºCprinted specimen (implied by the document), ISO 179tested at 23ºCnot in the median: notch not stated
HDT70˚C °Cp. 1: Heat deflection temp.ASTM D648not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
Density1,27 g/ccp. 1: DensityISO 1183

Print settings

Nozzle
210–235 °Cown data sheet
Bed
50–80 °Cown data sheet
Heated chamber
50–70 °Cown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 210 -235 ºC; Bed 50 -80 ºC; Chamber 50-70 °CiSANMATE, PETGRecommended printing settings

Price

Not in the price sample.

Its 3 documents

What the maker says (4)
  • Good forThe strength of it allow to be a suitable material for food packaging, the chemical non-reactive characteristic allow it to be the most valuable material in medical field, normally used for orthopedic and prosthetic device.iSANMATE, PETGp. 1
  • Good forPETG is a very waterproof material which make it become an excellent choice for outdoor activity.iSANMATE, PETGp. 1
  • BenefitsPolyethylene Terephthalate Glycol-modified (PETG) is a tough and durable materials and it is easy to use.iSANMATE, PETGp. 1
  • BenefitsIt also has excellent chemical resistance, which can be well-used in both acidic and alkaline environment, PETG also have strong impact resistance, which make it be the substitute material for PMMA and PC.iSANMATE, PETGp. 1
Recreus PET-GStrength XY, MPa50Strength Z, MPa—Modulus XY, GPa3.02Charpy notched, kJ/m²—HDT 0.45, °C68HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–260Bed, °C40–70Chamber, °CnoneDrying, °C, h658 h

Recreus PET-GRecreus

Published values

PropertyAs publishedConditionsOn the Overview
Recreus, TECHNICAL DATA SHEET PET-G8 valuesUnless a row says otherwise: specimen not stated
Tensile strength (yield or break not stated) orientation not stated50,00 MPap. 1: Tensile strength
DIN 53504As the sheet prints it: DIN 53504-S2
not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated50,00 MPap. 1: Yield strength
DIN 53504As the sheet prints it: DIN 53504-S2
not in the median: another value of this product is in it
Elongation at break orientation not stated31 %p. 1: Elongation at break
DIN 53504As the sheet prints it: DIN 53504-S2
not in the median: set apart (never used to pass), test bar not described as printed
Charpy impact strength orientation not stated58,00 kJ/m2physically implausiblep. 1: Notched impact strengh (Charpy)n at +23ºCISO 179tested at +23ºCnot in the median: physically implausible as published
Izod impact strength orientation not stated4,4 kJ/m2p. 1: Izod impact strengh (23°C notched)
ISO 34As the sheet prints it: ISO 34-1
tested at 23 °C		not in the median: to another standard
HDT at 0.45 MPa68,0 °Cp. 1: HDT (0,45MPa) 68,0 °C ISO 75-2
ISO 75As the sheet prints it: HDT (0,45MPa); ISO 75-2
in the median
Glass transition temperature80,0 °Cp. 1: Glass Transition Temperature 10°C/min
ISO 11357As the sheet prints it: ISO 11357-1/-2; rate=10 °C/min
in the median
Vicat softening temperature78,0 °Cp. 1: VST Vicat Softening Temperature
no standard namedAs the sheet prints it: Vicat A Method: 50 Nw, 50°C/h; method=Vicat A; rate=50 °C/h
Recreus, TECHNICAL DATA SHEET PET-G6 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated3020 MPap. 1: Tensile Modulus
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2040 MPap. 1: Flexural Modulus
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated68 MPap. 1: Flexural StrenghtISO 178not in the median: set apart (never used to pass), test bar not described as printed
Hardness76 Shore Dp. 1: Hardness
ASTM D2240As the sheet prints it: ASTM D2240 (2010)
in the median
Vicat softening temperature82 °Cp. 1: Vicat Softening temp.ISO 306
Density1.29 g/cm³p. 1: Material density
ISO 1183As the sheet prints it: DIN EN ISO 1183-1-A

Print settings

Nozzle
230–260 °Cown data sheet
Bed
40–70 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

Extrudr XPETG MATTModified: cosmetic dense fillerStrength XY, MPa53Strength Z, MPa—Modulus XY, GPa3.1Charpy notched, kJ/m²1.7HDT 0.45, °C—HDT 1.8, °C62Price, CAD/kg—Nozzle, °C210–240Bed, °C60–90Chamber, °C—Drying, °C, h606 h

Extrudr XPETG MATTExtrudr

Modified: cosmetic dense filler. Its values are kept out of the material's medians.

Published values

PropertyAs publishedConditionsOn the Overview
Extrudr, XPETG MATT official maker product page19 values
Tensile modulus orientation not stated3100 MPa ±46p. 1: Tensile modulus (Young's modulus)
ISO 527As the sheet prints it: ISO 527-1
not in the median: added filler or additive
Tensile yield strength orientation not stated53 MPa ±0.2p. 1: Tensile strength at yield
ISO 527As the sheet prints it: ISO 527-1
not in the median: added filler or additive
Tensile break strength orientation not stated53 MPa ±0.2p. 1: Tensile stress at break
ISO 527As the sheet prints it: ISO 527-1
not in the median: another value of this product is in it
Elongation at break orientation not stated7.6 % ±1.1p. 1: Elongation at break
ISO 527As the sheet prints it: ISO 527-1
not in the median: added filler or additive
Flexural modulus orientation not stated3300 MPap. 1: Flexural modulusISO 178not in the median: added filler or additive
Flexural strength orientation not stated75 MPap. 1: Flexural strengthISO 178not in the median: added filler or additive
Charpy impact strength orientation not stated1.7 kJ/m² ±0.4p. 1: Charpy notched impact strength (+23°C)
ISO 179As the sheet prints it: ISO 179-1eA; notched
tested at +23 °C		not in the median: added filler or additive
Charpy impact strength orientation not stated1.5 kJ/m²p. 1: Charpy notched impact strength (-30°C)
ISO 179As the sheet prints it: ISO 179-1eA; notched
tested at -30 °C		not in the median: tested below room temperature
Charpy impact strength orientation not stated78 kJ/m² ±6p. 1: Charpy unnotched impact strength (+23°C)
ISO 179As the sheet prints it: ISO 179-1eU; unnotched
tested at +23 °C		not in the median: unnotched
Charpy impact strength orientation not stated60 kJ/m²p. 1: Charpy unnotched impact strength (-30°C)
ISO 179As the sheet prints it: ISO 179-1eU; unnotched
tested at -30 °C		not in the median: unnotched
HDT at 1.8 MPa62 °Cp. 1: Heat deflection temp. (HDT/A) — 1.8 MPa
ISO 75As the sheet prints it: ISO 75-1; 1.8 MPa
not in the median: added filler or additive
Glass transition temperature80 °Cp. 1: Glass transition temp. (Tg)
ISO 11357As the sheet prints it: ISO 11357-1 (DSC)
not in the median: added filler or additive
Vicat softening temperature76 °Cp. 1: Vicat softening temp. (VST/B50)ISO 306
Decomposition temperature370 °Cp. 1: Thermal decomposition temp.no standard stated
Density1.36 g/cm³p. 1: Density
ISO 1183As the sheet prints it: ISO 1183-1
Water absorption< 0.12 %p. 1: Water absorption (saturation, 23°C)
no standard namedAs the sheet prints it: saturation
tested at 23 °C
Melt mass-flow rate5 g/10 minp. 1: Melt flow rate (MFR) — 210°C/2.16 kg
ISO 1133As the sheet prints it: ISO 1133-1 (210°C/2.16 kg)
tested at 210 °C
Melt volume-flow rate18 cm³/10 minp. 1: Melt volume rate (MVR) — 235°C/5.0 kg
no standard namedAs the sheet prints it: 5.0 kg
tested at 235 °C
Mould shrinkage orientation not stated0.3–0.5 %p. 1: Mould shrinkage
ISO 294As the sheet prints it: ISO 294-4
Extrudr, TECHNICAL DATA SHEET XPETG MATT11 valuesUnless a row says otherwise: moulded bar (resin supplier's value)
Tensile modulus3100 ± 46 MPap. 1: Tensile modulus (E-Modulus) ISO 527 MPaISO 527not in the median: measured on a moulded bar
Tensile strength (yield or break not stated)53 ± 0,2 MPap. 1: Strength ISO 527 MPaISO 527not in the median: measured on a moulded bar
Tensile yield strength53 ± 0,2 MPap. 1: Yield stress ISO 527 MPaISO 527not in the median: measured on a moulded bar
Elongation at break7,6 ± 1,1 %p. 1: Elongation at break ISO 527-2 %
ISO 527As the sheet prints it: ISO 527-2
not in the median: measured on a moulded bar
Elongation at yield3,5 ± 0,1 %p. 1: Elongation at yield ISO 527-2 %
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Izod impact strength1,7 ± 0,4 kj/m²p. 1: Notched impact strength ISO 180 kj/m²ISO 180not in the median: measured on a moulded bar
Izod impact strength78 ± 6 kj/m²p. 1: Unnotched impact strength ISO 180 kj/m²ISO 180not in the median: measured on a moulded bar
Hardness76 Shore Dp. 1: Shore hardness ISO 868/D Shore D
ISO 868As the sheet prints it: ISO 868/D
not in the median: the resin supplier's value, not a printed part
HDT at 0.45 MPa67 °Cp. 1: Heat Deflection Temperature HDT/B ISO 15075 °C
ISO 15075As the sheet prints it: HDT B ISO 15075
not in the median: measured on a moulded bar
Vicat softening temperature85 °Cp. 1: VICAT A (VST) ISO 306 °CISO 306
Density1,41 g/cm³p. 1: Density ISO 1183-1/A g/cm³specimen not stated,
ISO 1183As the sheet prints it: ISO 1183-1/A

Print settings

Nozzle
210–240 °Cown data sheet
Bed
60–90 °Cown data sheet
Heated chamber
not stated
Drying
60 °C for 6 hown data sheet
Hardened nozzle
not neededown data sheet
Its 2 print profiles, in the documents' words
  • Nozzle 210-240°C; Bed 60-90°CExtrudr, TECHNICAL DATA SHEET XPETG MATTp. 1: Recommended printing settings; p. 1: Hardened Nozzle; p. 1: Recommended settings for printers with a 0.4mm Nozzle
  • Nozzle 210–240 °C; Bed 60–90 °C; Drying Drying temperature 60 °C; Drying time 4–6 hExtrudr, XPETG MATT official maker product pagep. 1: Exact product drying table and own nozzle recommendation; other recipe fields not transcribed in this scoped profile; p. 1: Nozzle temperature; p. 1: Build plate temperature; p. 1: Surface preparation; p. 1: Enclosed chamber required; p. 1: Hardened nozzle required

Price

Not in the price sample.

Its 3 documents

What the maker says (6)
Extrudr PETGStrength XY, MPa51Strength Z, MPa—Modulus XY, GPa2.98Charpy notched, kJ/m²5HDT 0.45, °C68HDT 1.8, °C62Price, CAD/kg—Nozzle, °C210–230Bed, °C60–90Chamber, °C—Drying, °C, h600–6 h

Extrudr PETGExtrudr

Published values

PropertyAs publishedConditionsOn the Overview
Extrudr, PETG official maker product page17 valuesThe same values also in Extrudr, TECHNICAL DATA SHEET PETG and Extrudr, TECHNICAL DATA SHEET PETG.
Tensile modulus orientation not stated2980 MPap. 1: Tensile modulus (Young's modulus)
ISO 527As the sheet prints it: ISO 527-1
not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated51 MPap. 1: Tensile strength at yield
ISO 527As the sheet prints it: ISO 527-1
not in the median: set apart (never used to pass), test bar not described as printed
Tensile break strength orientation not stated20 MPap. 1: Tensile stress at break
ISO 527As the sheet prints it: ISO 527-1
not in the median: another value of this product is in it
Elongation at break orientation not stated29 %p. 1: Elongation at break
ISO 527As the sheet prints it: ISO 527-1
not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2040 MPap. 1: Flexural modulusISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated68 MPap. 1: Flexural strengthISO 178not in the median: set apart (never used to pass), test bar not described as printed
Charpy impact strength orientation not stated5 kJ/m²p. 1: Charpy notched impact strength (+23°C)
ISO 179As the sheet prints it: ISO 179-1eA
tested at +23°C		not in the median: set apart (never used to pass), test bar not described as printed
Charpy impact strength orientation not stated4 kJ/m²p. 1: Charpy notched impact strength (-30°C)
ISO 179As the sheet prints it: ISO 179-1eA
tested at -30°C		not in the median: tested below room temperature
Charpy impact strength orientation not stated120 kJ/m²p. 1: Charpy unnotched impact strength (-30°C)
ISO 179As the sheet prints it: ISO 179-1eU
tested at -30°C		not in the median: unnotched
HDT at 0.45 MPa68 °Cp. 1: Heat deflection temp. (HDT/B) — 0.45 MPa
ISO 75As the sheet prints it: ISO 75-1; 0.45 MPa; method B
not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa62 °Cp. 1: Heat deflection temp. (HDT/A) — 1.8 MPa
ISO 75As the sheet prints it: ISO 75-1; 1.8 MPa; method A
not in the median: set apart (never used to pass), test bar not described as printed
Glass transition temperature80 °Cp. 1: Glass transition temp. (Tg)
ISO 11357As the sheet prints it: ISO 11357-1 (DSC)
in the median
Vicat softening temperature75 °Cp. 1: Vicat softening temp. (VST/B50)ISO 306
Decomposition temperature370 °Cp. 1: Thermal decomposition temp.no standard stated
Water absorption< 0.1 %p. 1: Water absorption (saturation, 23°C)
no standard namedAs the sheet prints it: saturation
tested at 23°C
Melt mass-flow rate6 g/10 minp. 1: Melt flow rate (MFR) — 210°C/2.16 kgalso in Extrudr, TECHNICAL DATA SHEET PETGalso in Extrudr, TECHNICAL DATA SHEET PETG
ISO 1133As the sheet prints it: ISO 1133-1 (210°C/2.16 kg)
tested at 210°C
Melt volume-flow rate40 cm³/10 minp. 1: Melt volume rate (MVR) — 235°C/5.0 kg
no standard namedAs the sheet prints it: 5.0 kg
tested at 235°C
Extrudr, TECHNICAL DATA SHEET PETG11 valuesThe same values also in Extrudr, TECHNICAL DATA SHEET PETG.Unless a row says otherwise: moulded bar (resin supplier's value)
Tensile modulus3100 MPap. 1: Tensile modulus (E-Modulus) ISO 527 MPaISO 527not in the median: measured on a moulded bar
Tensile strength (yield or break not stated)61 MPap. 1: Strength ISO 527 MPaISO 527not in the median: measured on a moulded bar
Tensile yield strength51 MPap. 1: Yield stress ISO 527 MPaISO 527not in the median: measured on a moulded bar
Elongation at break28 %p. 1: Nominal elongation at break ISO 527-2 %
ISO 527As the sheet prints it: ISO 527-2
not in the median: measured on a moulded bar
Elongation at yield4 %p. 1: Elongation at yield ISO 527-2 %
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Tensile strain at strength4 %p. 1: Elongation at strength ISO 527 %ISO 527listed under other properties
Flexural modulus2100 MPap. 1: Flexural modulus (E-Modulus) ISO 178 MPaISO 178not in the median: measured on a moulded bar
Flexural strength68 MPap. 1: Flexural strength ISO 178 MPaISO 178not in the median: measured on a moulded bar
Izod impact strength4,7 kj/m²p. 1: Notched impact strength ISO 180 kj/m²ISO 180not in the median: measured on a moulded bar
Vicat softening temperature78 °Cp. 1: VICAT A (VST) ISO 306 °CISO 306
Melting temperature180-200 °Cp. 1: Melting temperature ISO 3146-C °Calso in Extrudr, TECHNICAL DATA SHEET PETGspecimen not stated,
ISO 3146As the sheet prints it: ISO 3146-C
Extrudr, TECHNICAL DATA SHEET PETG2 values
Density1,29 g/cm³p. 1: Density ASTM D792 g/cm³ASTM D792
Mould shrinkage orientation not stated0,5 %p. 1: Shrinking
ISO 294As the sheet prints it: ISO 294-4

Print settings

Nozzle
210–230 °Cown data sheet
Bed
60–90 °Cown data sheet
Heated chamber
not stated
Drying
optional: 60 °C for 0–6 hown data sheet
Hardened nozzle
not neededown data sheet
Its 3 print profiles, in the documents' words
  • Nozzle 210-230°C; Bed 60-90°CExtrudr, TECHNICAL DATA SHEET PETGp. 1: Recommended printing settings; p. 1: Hardened Nozzle; p. 1: Recommended settings for printers with a 0.4mm Nozzle
  • Nozzle 210-230°C; Bed 60-90°CExtrudr, TECHNICAL DATA SHEET PETGp. 1: Recommended printing settings; p. 1: Hardened Nozzle; p. 1: Recommended settings for printers with a 0.4mm Nozzle
  • Nozzle 210–230 °C; Bed 60–90 °C; Drying 60 °C, 0–6 hExtrudr, PETG official maker product pagep. 1: Nozzle temperature; p. 1: Build plate temperature; p. 1: Enclosed chamber required; p. 1: Hardened nozzle required; p. 1: Recommended settings for printers with a 0.4 mm nozzle; p. 1: Drying temperature

Price

Not in the price sample.

Its 4 documents

What the maker says (7)
3DXTECH 3DXMAX PETGStrength XY, MPa45Strength Z, MPa—Modulus XY, GPa1.65Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–260Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

3DXTECH 3DXMAX PETG3DXTECH

Published values

PropertyAs publishedConditionsOn the Overview
3DXTECH, Technical Data Sheet: 3DXMAX™ PETG 3D Printing Filament8 valuesUnless a row says otherwise: printed specimen
print settingsPrinted Specimen Conditions Printer: Open Source FDM/FFF Nozzle: 0.4mm Layer Height: 0.25mm Infill: 100%, +/- 45° Extrusion Temp: 245°C Bed Temp: 70°C Specimen Orientation: XY Flat
Tensile modulus XY1650 MPap. 1: Tensile Modulus ISO 527 MPaISO 527in the median
Tensile break strength XY45 MPap. 1: Tensile Strength, Break ISO 527 MPaISO 527in the median
Elongation at break XY24 %p. 1: Tensile Elongation, Break ISO 527 %ISO 527in the median
Flexural modulus XY1600 MPap. 1: Flexural Modulus ISO 178 MPaISO 178in the median
Flexural strength XY72 MPap. 1: Flexural Strength ISO 178 MPaISO 178in the median
HDT at 0.45 MPa70 °Cp. 1: Deflection Temperature at 0.45 ISO 75 °C
ISO 75As the sheet prints it: ISO 75, 0.45 MPa (66psi)
in the median
Glass transition temperature80 °Cp. 1: Glass Transition Temperature (Tg) DSC °C
DSCAs the sheet prints it: Tg DSC °C
in the median
Density1.24 g/ccp. 1: Density ISO 1183 g/cc
ISO 1183As the sheet prints it: 1183 g/cc ISO 1183

Print settings

Nozzle
230–260 °CBambu Lab Filament Guide
Bed
60–80 °CBambu Lab Filament Guide
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

3DXTECH 3DXPRO LG PETGStrength XY, MPa47Strength Z, MPa—Modulus XY, GPa1.4Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C260–280Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

3DXTECH 3DXPRO LG PETG3DXTECH

Published values

PropertyAs publishedConditionsOn the Overview
3DXTECH, 3DXPRO LG PETG8 valuesUnless a row says otherwise: printed specimen
print settingsPrinted Specimen Conditions Printer: Open Source FDM/FFF Nozzle: 0.4mm Layer Height: 0.25mm Infill: 100%, +/- 45° Extrusion Temp: 255°C Bed Temp: 70°C Specimen Orientation: XY Flat
Tensile modulus XY1400 MPap. 1: Tensile ModulusISO 527in the median
Tensile break strength XY47 MPap. 1: Tensile Strength, BreakISO 527in the median
Elongation at break XY8 %p. 1: Tensile Elongation, BreakISO 527in the median
Flexural modulus XY1645 MPap. 1: Flexural ModulusISO 178in the median
Flexural strength XY75 MPap. 1: Flexural StrengthISO 178in the median
HDT at 0.45 MPa70 °Cp. 1: Deflection Temperature at 0.45
ISO 75As the sheet prints it: ISO 75, 0.45 MPa (66 psi)
in the median
Glass transition temperature80 °Cp. 1: Glass Transition Temperature (Tg)DSCin the median
Density1.28 g/ccp. 1: DensityISO 1183

Print settings

Nozzle
260–280 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (14)
SUNLU High Speed Matte PETGStrength XY, MPa46Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²3IzodHDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C240–260Bed, °C60–70Chamber, °CnoneDrying, °C, h60–65

SUNLU High Speed Matte PETGSUNLU

Published values

PropertyAs publishedConditionsOn the Overview
SUNLU, High Speed Matte PETG12 valuesThe same values also in SUNLU, TECHNICAL DATA SHEET ISO High Speed Matte PETG.
Tensile strength (yield or break not stated) XY48 MPap. 1: Tensile Strength(X-Y) ISO527/2 50mm/min MPa
ISO 527As the sheet prints it: 50mm/min ISO527/2
not in the median: another value of this product is in it
Elongation at break XY33 %p. 1: Elongation at break(X-Y) ISO527/2 50mm/min %
ISO 527As the sheet prints it: 50mm/min ISO527/2
not in the median: another value of this product is in it
Flexural modulus XY2700 MPap. 1: Flexural Modulus(X-Y) ISO178 2mm/min MPa
ISO 178As the sheet prints it: 2mm/min ISO178
not in the median: another value of this product is in it
Flexural strength XY78 MPap. 1: Flexural Strength(X-Y) ISO178 2mm/min MPa
ISO 178As the sheet prints it: 2mm/min ISO178
not in the median: another value of this product is in it
Izod impact strength XY4.1 KJ/m2p. 1: IZOD Impact Notched(X-Y) ISO180 23℃ KJ/m2
ISO 180As the sheet prints it: 23℃ ISO180
tested at 23°C		not in the median: another value of this product is in it
Izod impact strength ZX4.8 KJ/m2p. 1: IZOD Impact Notched (Z-X) ISO180 23℃ KJ/m2
ISO 180As the sheet prints it: Z-X 23℃ ISO180
tested at 23°C		not in the median: measured on a bar in another orientation
Hardness80 Shore (scale not specified by source)p. 1: Shore hardness ISO868 23℃ HA/HD
ISO 868As the sheet prints it: 23℃ HA/HD ISO868
tested at 23°C		listed under other properties
HDT at 0.45 MPa70 ℃p. 1: Heat Deflection (HDT) ISO75 0.45MPa ℃
ISO 75As the sheet prints it: 0.45MPa ISO75
not in the median: another value of this product is in it
Melting temperature128 ℃p. 1: Melting Point ISO11357-3 10℃/min ℃also in SUNLU, TECHNICAL DATA SHEET ISO High Speed Matte PETG
ISO 11357As the sheet prints it: ISO11357-3
Decomposition temperature≥423 ℃p. 1: @5%Decomposition Temp. ISO11358 20℃/min ℃ISO 11358
Density1.26 g/cm3p. 1: Density ISO1183 23℃ g/cm3
ISO 1183As the sheet prints it: 23℃ ISO1183
tested at 23°C
Melt mass-flow rate4.4 g/10minp. 1: Melt Flow Rate ISO1133 230℃/2.16kg g/10min
ISO 1133As the sheet prints it: 230℃/2.16kg ISO1133
tested at 230°C
SUNLU, TECHNICAL DATA SHEET ISO High Speed Matte PETG11 valuesThe same values also in SUNLU, High Speed Matte PETG.Unless a row says otherwise: printed specimen
Tensile strength (yield or break not stated) XY46 ± 5 MPap. 1: (X-Y) Tensile Strength ISO 527/2 50 mm/min MPa
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
print settingsPrinting speed 160 mm/s; Printing temperature 255 °C; Infill: 100%; 90° raster orientation
in the median
Elongation at break XY14 ± 5 %p. 1: (X-Y) Elongation at break ISO 527/2 50 mm/min %
ISO 527As the sheet prints it: 50 mm/min ISO 527/2
print settingsPrinting speed 160 mm/s; Printing temperature 255 °C; Infill: 100%; 90° raster orientation
in the median
Flexural modulus XY2650 ± 200 MPap. 1: (X-Y) Flexural Modulus ISO 178 2 mm/min MPa
ISO 178As the sheet prints it: 2 mm/min ISO 178
print settingsPrinting speed 160 mm/s; Printing temperature 255 °C; Infill: 100%; 90° raster orientation
in the median
Flexural strength XY75 ± 6 MPap. 1: (X-Y) Flexural Strength ISO 178 2 mm/min MPa
ISO 178As the sheet prints it: 2 mm/min ISO 178
print settingsPrinting speed 160 mm/s; Printing temperature 255 °C; Infill: 100%; 90° raster orientation
in the median
Izod impact strength XY3 ± 1.5 KJ/m2p. 1: (X-Y) Izod Impact Strength of Notched ISO 180 23℃ KJ/m2 Specimen
ISO 180As the sheet prints it: 23℃ KJ/m2 Specimen ISO 180
tested at 23°C
print settingsPrinting speed 160 mm/s; Printing temperature 255 °C; Infill: 100%; 90° raster orientation
in the median
Izod impact strength ZX4.5 ± 2 KJ/m2p. 1: (Z-X) Izod Impact Strength of Unnotched ISO 180 23℃ KJ/m2 Specimen
ISO 180As the sheet prints it: 23℃ KJ/m2 Specimen ISO 180
tested at 23°C
print settingsPrinting speed 160 mm/s; Printing temperature 255 °C; Infill: 100%; 90° raster orientation
not in the median: unnotched
Hardness79 Shore (scale not specified by source)p. 1: Shore Hardness ISO 868 23℃ HA/HD
ISO 868As the sheet prints it: 23℃ HA/HD ISO 868
tested at 23°C		listed under other properties
HDT XY, at 0.45 MPa70 ± 2 ℃p. 1: (X-Y) Heat Distortion (HDT) ISO 75 0.45 MPa ℃
ISO 75As the sheet prints it: 0.45 MPa ISO 75
in the median
Glass transition temperature65.5 ℃p. 1: Glass Transition (Tg) ISO 11357-2 10 ℃/min ℃also in SUNLU, High Speed Matte PETG
ISO 11357As the sheet prints it: ISO 11357-2
in the median
Density1.28 g/cm3p. 1: Density ISO 1183 23℃ g/cm3specimen not stated,
ISO 1183As the sheet prints it: 23℃ ISO 1183
tested at 23°C
Melt mass-flow rate4.4 ± 2 g/10 minp. 1: Melt Mass-flow Rate ISO 1133 210℃/2.16 kg g/10 min
ISO 1133As the sheet prints it: 210℃/2.16 kg ISO 1133
tested at 210°C

Print settings

Nozzle
240–260 °Cown data sheet
Bed
60–70 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60–65 °Cown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its 4 print profiles, in the documents' words
  • Nozzle 240-260; Bed 60-70℃; Chamber Room Temperature; Drying 60-65℃SUNLU, TECHNICAL DATA SHEET ISO High Speed Matte PETGp. 2: Recommended printing settings; p. 2: Nozzle Temp.
  • Nozzle 230-240; Bed 60-70℃; Chamber Normal temperature; Drying 50℃SUNLU, High Speed Matte PETGp. 2: Recommended printing settings; p. 2: Nozzle Print Temp.; p. 2: Nozzle temperature, 50-100mm/s; p. 2: Print Platform Material
  • Nozzle 240-255; Bed 60-70℃; Chamber Normal temperature; Drying 50℃SUNLU, High Speed Matte PETGp. 2: Recommended Printing Parameters: Nozzle temperature, 100-300mm/s; p. 2: Print Platform Material
  • Nozzle 255-270; Bed 60-70℃; Chamber Normal temperature; Drying 50℃SUNLU, High Speed Matte PETGp. 2: Recommended Printing Parameters: Nozzle temperature, 300-600mm/s; p. 2: Print Platform Material

Price

Not in the price sample.

Its 3 documents

What the maker says (6)
Fiberlogy FiberWORKS PETGStrength XY, MPa47Strength Z, MPa—Modulus XY, GPa2.45Charpy notched, kJ/m²4IzodHDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C240–260Bed, °C70Chamber, °CnoneDrying, °C, h604 h

Fiberlogy FiberWORKS PETGFiberlogy

Published values

PropertyAs publishedConditionsOn the Overview
Fiberlogy, TECHNICAL DATA SHEET FiberWORKS PETG14 values
Tensile modulus orientation not stated2451 MPap. 2: Tensile Modulus ISO 527 MPaISO 527in the median
Tensile yield strength orientation not stated47 MPap. 2: Tensile Strength @ Yield ISO 527 MPaISO 527in the median
Tensile break strength orientation not stated50 MPap. 1: Tensile Strength @ Break ISO 527 MPaISO 527not in the median: another value of this product is in it
Tensile break strength orientation not stated36 MPap. 2: Tensile Strength @ Break ISO 527 MPaISO 527not in the median: another value of this product is in it
Elongation at break orientation not stated5 %p. 2: Elongation @ Break ISO 527 %ISO 527in the median
Elongation at yield orientation not stated3 %p. 2: Elongation @ Yield ISO 527 %ISO 527listed under other properties
Flexural modulus orientation not stated2100 MPap. 1: Flexular Modulus ISO 178 MPaISO 178not in the median: another value of this product is in it
Flexural modulus orientation not stated2238 MPap. 2: Flexural Modulus ISO 178 MPaISO 178in the median
Flexural strength orientation not stated70 MPap. 1: Flexular Strength ISO 178 MPaISO 178not in the median: another value of this product is in it
Flexural strength orientation not stated77 MPap. 2: Flexural Strength ISO 178 MPaISO 178in the median
Izod impact strength7 kJ/m2p. 1: Izod Impact Strength (Notched) @ 23℃ ISO 180 kJ/m2
ISO 180As the sheet prints it: 23℃ ISO 180
tested at 23°C		not in the median: another value of this product is in it
Izod impact strength4 kJ/m2p. 2: Izod Impact Strength (Notched) @ 23℃ ISO 180 kJ/m2
ISO 180As the sheet prints it: 23℃ ISO 180
tested at 23°C		in the median
HDT at 0.45 MPa70 °Cp. 1: Heat Distortion Temperature @ 0.45 MPa ASTM D648 °C
ASTM D648As the sheet prints it: 0.45 MPa ASTM D648
not in the median: set apart (never used to pass), test bar not described as printed
Density1.29 g/cm3p. 1: Specific Density ASTM D792 g/cm3ASTM D792
Fiberlogy, FiberWORKS PETG Filament 2×1 kg2 valuesUnless a row says otherwise: specimen not stated
Izod impact strength orientation not stated7 kJ/m²p. 1: Izod Impact Strength (Notched) @ 23°CISO 180tested at 23 °Cnot in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding
HDT at 1.8 MPaheld back: the sheet's unit or table layout is unclearheld backp. 1: Heat Deflection Temperature @ 1.8 MPa
ASTM D648As the sheet prints it: ASTM D648; 1.8 MPa
not in the median: held back

Print settings

Nozzle
240–260 °Cown data sheet
Bed
70 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60 °C for 4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (1)
Prusa Research Prusament PETG by Prusa PolymersData sheet shared with Prusa Research Prusament PETG Recycled by Prusa PolymersStrength XY, MPa47Strength Z, MPa—Modulus XY, GPa1.5Charpy notched, kJ/m²6HDT 0.45, °C68HDT 1.8, °C—Price, CAD/kg—Nozzle, °C240–260Bed, °C70–90Chamber, °CnoneDrying, °C, h658 h

Prusa Research Prusament PETG by Prusa PolymersPrusa Research

Data sheet shared with Prusa Research Prusament PETG Recycled by Prusa Polymers: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Prusa Research, Technical datasheet Prusament PETG Recycled by Prusa Polymers20 valuesUnless a row says otherwise: printed specimen
Tensile modulus XY1.5 ± 0.1 GPap. 2: Tensile Modulus [GPa] (Horizontal (source label))
ISO 527As the sheet prints it: ISO 527-1
in the median
Tensile modulus XZ1.6 ± 0.1 GPap. 2: Tensile Modulus [GPa] (Vertical XZ (source label))
ISO 527As the sheet prints it: ISO 527-1
not in the median: measured on a bar in another orientation
Tensile yield strength XY43 ± 1.8 MPap. 2: Tensile Yield Strength [MPa] (Horizontal (source label))
ISO 527As the sheet prints it: ISO 527-1
not in the median: another value of this product is in it
Tensile yield strength orientation not stated45 ± 1 MPap. 2: Tensile Yield Strength for Filament [MPa]Filament, ISO 527not in the median: measured on a filament strand
Tensile yield strength XZ48 ± 2.5 MPap. 2: Tensile Yield Strength [MPa] (Vertical XZ (source label))
ISO 527As the sheet prints it: ISO 527-1
not in the median: measured on a bar in another orientation
Elongation at yield XY4.5 ± 0.2 %p. 2: Elongation at Yield Point (Horizontal (source label))
ISO 527As the sheet prints it: ISO 527-1
listed under other properties
Elongation at yield XZ4.5 ± 0.5 %p. 2: Elongation at Yield Point (Vertical XZ (source label))
ISO 527As the sheet prints it: ISO 527-1
listed under other properties
Flexural modulus XY1.8 ± 0.1 GPap. 2: Flexural Modulus (Horizontal (source label))ISO 178not in the median: another value of this product is in it
Flexural modulus XZ1.8 ± 0.2 GPap. 2: Flexural Modulus (Vertical XZ (source label))ISO 178not in the median: measured on a bar in another orientation
Flexural strength XY63 ± 1 MPap. 2: Flexural Strength (Horizontal (source label))ISO 178not in the median: another value of this product is in it
Flexural strength XZ70 ± 1 MPap. 2: Flexural Strength (Vertical XZ (source label))ISO 178not in the median: measured on a bar in another orientation
Charpy impact strength XY25 ± 3 kJ/m2p. 2: Impact Strength Charpy [kJ/m2](3) (Horizontal (source label))
ISO 179As the sheet prints it: ISO 179-1; edgewise
unnotched		not in the median: unnotched
Charpy impact strength XY12 ± 1 kJ/m2p. 2: Impact Strength Charpy Notched [kJ/m2](4) (Horizontal (source label))
ISO 179As the sheet prints it: ISO 179-1; edgewise
not in the median: another value of this product is in it
Charpy impact strength XZ38 ± 11 kJ/m2p. 2: Impact Strength Charpy [kJ/m2](3) (Vertical XZ (source label))
ISO 179As the sheet prints it: ISO 179-1; edgewise
unnotched		not in the median: unnotched
Charpy impact strength XZ15 ± 3 kJ/m2p. 2: Impact Strength Charpy Notched [kJ/m2](4) (Vertical XZ (source label))
ISO 179As the sheet prints it: ISO 179-1; edgewise
not in the median: measured on a bar in another orientation
Interlayer adhesion strength orientation not stated15 ± 5 MPap. 2: Interlayer Adhesion [MPa]specimen not stated,
no standard namedAs the sheet prints it: Prusa Polymers
HDT at 0.45 MPa68 °Cp. 2: Heat Deflection Temperature (0.45 MPa) [°C]specimen not stated; its document points to a moulded or resin bar,
ISO 75As the sheet prints it: ISO 75; 0.45 MPa
not in the median: set apart (never used to pass), test bar not described as printed
Density1.27 g/cm3p. 2: Density [g/cm3]specimen not stated, ISO 1183
Water absorption0.07 %p. 2: Moisture Absorption in 24 hours [%](1)specimen not stated,
no standard namedAs the sheet prints it: Prusa Polymers; time=24 hours; humidity=22 %
tested at 24 °C
Water absorption0.10 %p. 2: Moisture Absorption in 7 days [%](1)specimen not stated,
no standard namedAs the sheet prints it: Prusa Polymers; time=7 days; humidity=22 %
tested at 24 °C
Prusa Research, Technical datasheet Prusament PETG by Prusa Polymers12 valuesUnless a row says otherwise: printed specimen
Tensile yield strength XY47 ± 2 MPap. 2: Tensile Yield Strength [MPa] (Horizontal (source label))
ISO 527As the sheet prints it: ISO 527-1
in the median
Tensile yield strength orientation not stated46 ± 1 MPap. 2: Tensile Yield Strength for Filament [MPa]Filament, ISO 527not in the median: measured on a filament strand
Tensile yield strength XZ50 ± 1 MPap. 2: Tensile Yield Strength [MPa] (Vertical XZ (source label))
ISO 527As the sheet prints it: ISO 527-1
not in the median: measured on a bar in another orientation
Elongation at yield XY5.1 ± 0.1 %p. 2: Elongation at Yield Point (Horizontal (source label))
ISO 527As the sheet prints it: ISO 527-1
listed under other properties
Elongation at yield XZ5.1 ± 0.1 %p. 2: Elongation at Yield Point (Vertical XZ (source label))
ISO 527As the sheet prints it: ISO 527-1
listed under other properties
Flexural modulus XY1.7 ± 0.1 GPap. 2: Flexural Modulus (Horizontal (source label))ISO 178in the median
Flexural modulus XZ1.6 ± 0.1 GPap. 2: Flexural Modulus (Vertical XZ (source label))ISO 178not in the median: measured on a bar in another orientation
Flexural strength XY66 ± 2 MPap. 2: Flexural StrengthISO 178in the median
Charpy impact strength XY6 ± 1 kJ/m2p. 2: Impact Strength Charpy Notched [kJ/m2](4) (Horizontal (source label))
ISO 179As the sheet prints it: ISO 179-1; edgewise
in the median
Charpy impact strength XZ3 ± 1 kJ/m2p. 2: Impact Strength Charpy Notched [kJ/m2](4) (Vertical XZ (source label))
ISO 179As the sheet prints it: ISO 179-1; edgewise
not in the median: measured on a bar in another orientation
Hardness74 Shore Dp. 2: Hardness – Shore Dspecimen not stated, no standard statedin the median
Interlayer adhesion strength orientation not stated18 ± 4 MPap. 2: Interlayer Adhesion [MPa]specimen not stated,
no standard namedAs the sheet prints it: Prusa Polymers

Print settings

Nozzle
240–260 °Cown data sheet
Bed
70–90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (49)
Prusa Research Prusament PETG Recycled by Prusa PolymersData sheet shared with Prusa Research Prusament PETG by Prusa PolymersStrength XY, MPa47Strength Z, MPa—Modulus XY, GPa1.5Charpy notched, kJ/m²6HDT 0.45, °C68HDT 1.8, °C—Price, CAD/kg—Nozzle, °C240–260Bed, °C70–90Chamber, °CnoneDrying, °C, h658 h

Prusa Research Prusament PETG Recycled by Prusa PolymersPrusa Research

Data sheet shared with Prusa Research Prusament PETG by Prusa Polymers: their values are one table, recorded once.

Published values

No value is on file for this product.

Print settings

Nozzle
240–260 °Cown data sheet
Bed
70–90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (55)
Prusa Research Prusament PETG V0 by Prusa PolymersStrength XY, MPa39Strength Z, MPa—Modulus XY, GPa1.7Charpy notched, kJ/m²—HDT 0.45, °C74HDT 1.8, °C68Price, CAD/kg—Nozzle, °C220–240Bed, °C70–90Chamber, °CnoneDrying, °C, h556 h

Prusa Research Prusament PETG V0 by Prusa PolymersPrusa Research

Published values

PropertyAs publishedConditionsOn the Overview
Prusa Research, Technical datasheet Prusament PETG V0 by Prusa Polymers20 values
Tensile modulus XY1.7 ± 0.1 GPap. 2: Tensile Modulus [GPa] (Horizontal (source label))
ISO 527As the sheet prints it: ISO 527-1
in the median
Tensile modulus XZ1.8 ± 0.1 GPap. 2: Tensile Modulus [GPa] (Vertical XZ (source label))
ISO 527As the sheet prints it: ISO 527-1
not in the median: measured on a bar in another orientation
Tensile yield strength XY39 ± 2 MPap. 2: Tensile Yield Strength [MPa] (Horizontal (source label))
ISO 527As the sheet prints it: ISO 527-1
in the median
Tensile yield strength orientation not stated39.4 ± 0.1 MPap. 2: Tensile Yield Strength for Filament [MPa]ISO 527not in the median: measured on a filament strand
Tensile yield strength XZ42 ± 1 MPap. 2: Tensile Yield Strength [MPa] (Vertical XZ (source label))
ISO 527As the sheet prints it: ISO 527-1
not in the median: measured on a bar in another orientation
Elongation at yield XY3.5 ± 0.2 %p. 2: Elongation at Yield Point (Horizontal (source label))
ISO 527As the sheet prints it: ISO 527-1
listed under other properties
Elongation at yield XZ3.7 ± 0.1 %p. 2: Elongation at Yield Point (Vertical XZ (source label))
ISO 527As the sheet prints it: ISO 527-1
listed under other properties
Flexural modulus XY1.0 ± 0.1 GPap. 2: Flexural Modulus (Horizontal (source label))ISO 178in the median
Flexural modulus XZ1.0 ± 0.1 GPap. 2: Flexural Modulus (Vertical XZ (source label))ISO 178not in the median: measured on a bar in another orientation
Flexural strength XY60 ± 1 MPap. 2: Flexural Strength (Horizontal (source label))ISO 178in the median
Flexural strength XZ64 ± 1 MPap. 2: Flexural Strength (Vertical XZ (source label))ISO 178not in the median: measured on a bar in another orientation
Charpy impact strength XY23 ± 1 kJ/m2p. 2: Impact Strength Charpy [kJ/m2](3) (Horizontal (source label))
ISO 179As the sheet prints it: ISO 179-1; edgewise
unnotched		not in the median: unnotched
Charpy impact strength XZ33 ± 2 kJ/m2p. 2: Impact Strength Charpy [kJ/m2](3) (Vertical XZ (source label))
ISO 179As the sheet prints it: ISO 179-1; edgewise
unnotched		not in the median: unnotched
Hardness79 Shore Dp. 2: Hardness – Shore Dno standard statedin the median
Interlayer adhesion strength orientation not stated16.4 ± 1.3 MPap. 2: Interlayer Adhesion [MPa]
no standard namedAs the sheet prints it: Prusa Polymers
HDT at 0.45 MPa74 °Cp. 2: Heat Deflection Temperature (0.45 MPa) [°C]
ISO 75As the sheet prints it: ISO 75; 0.45 MPa
not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa68 °Cp. 2: Heat Deflection Temperature (1.80 MPa) [°C]
ISO 75As the sheet prints it: ISO 75; 1.80 MPa
not in the median: set apart (never used to pass), test bar not described as printed
Density1.27 g/cm3p. 2: Density [g/cm3]ISO 1183
Water absorption0.13 %p. 2: Moisture Absorption in 24 hours [%](1)
no standard namedAs the sheet prints it: Prusa Polymers; time=24 hours; humidity=23 %
tested at 25 °C
Water absorption0.19 %p. 2: Moisture Absorption in 7 days [%](1)
no standard namedAs the sheet prints it: Prusa Polymers; time=7 days; humidity=23 %
tested at 25 °C

Print settings

Nozzle
220–240 °Cown data sheet
Bed
70–90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
55 °C for 6 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (1)
BigRep rPETGStrength XY, MPa54Strength Z, MPa—Modulus XY, GPa1.8Charpy notched, kJ/m²10HDT 0.45, °C—HDT 1.8, °C63Price, CAD/kg—Nozzle, °C220–250Bed, °C70–90Chamber, °CnoneDrying, °C, h604–6 h

BigRep rPETGBigRep

Only 2.85 mm filament was found; the H2C takes 1.75 mm.

Published values

PropertyAs publishedConditionsOn the Overview
BigRep, FILAMENT rPETG8 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated1800 MPap. 1: Tensile Modulus (ISO 527)ISO 527not in the median: set apart (never used to pass), test bar not described as printed
Tensile strength (yield or break not stated) orientation not stated54 MPap. 1: Tensile Strength (ISO 527)ISO 527not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2000 MPap. 1: Flexural Modulus (ISO 178)ISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated68 MPap. 1: Flexural Strength (ISO 178)ISO 178not in the median: set apart (never used to pass), test bar not described as printed
Charpy impact strength10 kJ/m²p. 1: Impact Strength, Notched (ISO 179)ISO 179not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa63 °Cp. 1: HDT A - 1.8 MPa (ISO 75)
ISO 75As the sheet prints it: ISO 75; 1.8 MPa; method=A
in the median
Glass transition temperature85 °Cp. 1: Glass Transition Temperature (Tg) (DSC)
DSCAs the sheet prints it: DSC; method=DSC
in the median
Density1.23 g/cm³p. 1: Density (ISO 1183)ISO 1183

Print settings

Nozzle
220–250 °Cown data sheet
Bed
70–90 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
60 °C for 4–6 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 220 - 250 °C; Bed 70 - 90 °C; Drying 60 °C for 4 - 6 hoursBigRep, FILAMENT rPETGp. 1: Recommended printing settings

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
  • BenefitsEasy to print and perfect for design iterations, BigRep rPETG features well-balanced mechanical properties and chemical resistance.BigRep, FILAMENT rPETGp. 1
Fillamentum PETGStrength XY, MPa50Strength Z, MPa—Modulus XY, GPa1.9Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C235–255Bed, °C65–75Chamber, °CnoneDrying, °C, h653–4 h

Fillamentum PETGFillamentum

Published values

PropertyAs publishedConditionsOn the Overview
Fillamentum, PETG9 valuesThe same values also in Fillamentum, Datasheet PETG.Unless a row says otherwise: specimen not stated
Tensile modulus orientation not stated1900 MPap. 1: Tensile modulusISO 527not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated50 MPap. 1: Tensile strength at yieldISO 527not in the median: set apart (never used to pass), test bar not described as printed
Tensile break strength orientation not stated26 MPap. 1: Tensile strength at breakISO 527not in the median: another value of this product is in it
Elongation at break orientation not stated120 %p. 1: Elongation at breakalso in Fillamentum, Datasheet PETGISO 527not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2150 MPap. 1: Flexural modulusalso in Fillamentum, Datasheet PETGISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated71 MPap. 1: Flexural strengthalso in Fillamentum, Datasheet PETGISO 178not in the median: set apart (never used to pass), test bar not described as printed
Hardness75 Shore Dp. 1: HardnessISO 7619in the median
Vicat softening temperature75 °Cp. 1: Vicat softening temperatureISO 306
Density1.27 g/cm3p. 1: Material densityalso in Fillamentum, Datasheet PETGISO 1183
Fillamentum, Datasheet PETG3 valuesUnless a row says otherwise: specimen not stated
Izod impact strength85 J/mp. 1: Izod impact strengthASTM D256tested at 23°Cnotchednot in the median: in J/m
Hardness105 Rockwell Rp. 1: Rockwell hardnessASTM D785listed under other properties
HDT at 0.45 MPa70 °Cp. 1: Heat distortion temperature
ASTM D648As the sheet prints it: 0.455 MPa ASTM D648
in the median

Print settings

Nozzle
235–255 °Cown data sheet
Bed
65–75 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 3–4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (14)
Chemicals and environment (1)
Spectrum PET-G Premium High SpeedStrength XY, MPa35Strength Z, MPa—Modulus XY, GPa2.99Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C240–265Bed, °C60–80Chamber, °CnoneDrying, °C, h60≥ 4 h

Spectrum PET-G Premium High SpeedSpectrum

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, TECHNICAL DATA SHEET PET-G Premium High Speed9 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated2990 MPap. 1: Tensile Modulus
ASTM D638As the sheet prints it: D 638
not in the median: set apart (never used to pass), test bar not described as printed
Tensile strength (yield or break not stated) orientation not stated35 MPap. 1: Tensile Strengthno standard statednot in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated10,00 %p. 1: Elongation at Breakno standard statednot in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated6,00 %p. 1: Elongation at Yield
ASTM D638As the sheet prints it: D 638
listed under other properties
Flexural modulus orientation not stated2000 MPap. 1: Flexural Modulus
ASTM D790As the sheet prints it: D 790
not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated64 MPap. 1: Flexural Strength
ASTM D790As the sheet prints it: D 790
not in the median: set apart (never used to pass), test bar not described as printed
HDT70 °Cp. 1: Heat Deflection Temperature
ASTM D648As the sheet prints it: D 648
not in the median: set apart (never used to pass), no stated test load
Glass transition temperature80 °Cp. 1: Glass Transition Temperature
ASTM D3418As the sheet prints it: D3418
in the median
Density1.29 g/cm3p. 1: Specific Gravity
ASTM D792As the sheet prints it: D 792
Spectrum, Spectrum Filaments Product Portfolio 2025 — Prografen pp28–291 value
HDT at 0.45 MPa78°C78°C)
no standard namedAs the sheet prints it: method=B
not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding

Print settings

Nozzle
240–265 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
optional: 60 °C for ≥ 4 hown data sheet
Hardened nozzle
not neededown data sheet

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): nozzle in Spectrum, Spectrum Filaments Product Portfolio 2025 — Prografen pp28–29.

Its 4 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (4)
Flashforge PETGStrength XY, MPa40Strength Z, MPa—Modulus XY, GPa1Charpy notched, kJ/m²4.5IzodHDT 0.45, °C74HDT 1.8, °C—Price, CAD/kg—Nozzle, °C220–240Bed, °C25–80Chamber, °C25–50Drying, °C, h70≥ 5 h

Flashforge PETGFlashforge

Published values

PropertyAs publishedConditionsOn the Overview
Flashforge, Technical Data Sheet PETG Filament10 values
Tensile modulus XY1000-1100 Mpap. 1: Modulus of Elasticity (X-Y) ISO 527 MpaISO 527as printed
print settingsTest Equipment Guider IIs (Flashforge); Nozzle Diameter 0.4mm; Nozzle Temperature 240 °C; Printing Speed 50mm/s; Wall Thickness 1.2mm; Infill 100%; Note: The above test parameter data are obtained from actual printing, and the printed model has not been annealed.
in the median
Tensile strength (yield or break not stated) XY40-45 Mpap. 1: Tensile Strength (X-Y) ISO 527 MpaISO 527as printed
print settingsTest Equipment Guider IIs (Flashforge); Nozzle Diameter 0.4mm; Nozzle Temperature 240 °C; Printing Speed 50mm/s; Wall Thickness 1.2mm; Infill 100%; Note: The above test parameter data are obtained from actual printing, and the printed model has not been annealed.
in the median
Elongation at break XY6-8 %p. 1: Elongation at Break (X-Y) ISO 527 %ISO 527as printed
print settingsTest Equipment Guider IIs (Flashforge); Nozzle Diameter 0.4mm; Nozzle Temperature 240 °C; Printing Speed 50mm/s; Wall Thickness 1.2mm; Infill 100%; Note: The above test parameter data are obtained from actual printing, and the printed model has not been annealed.
in the median
Flexural strength XY50-55 Mpap. 1: Bending Strength (X-Y) ISO 178 MpaISO 178as printed
print settingsTest Equipment Guider IIs (Flashforge); Nozzle Diameter 0.4mm; Nozzle Temperature 240 °C; Printing Speed 50mm/s; Wall Thickness 1.2mm; Infill 100%; Note: The above test parameter data are obtained from actual printing, and the printed model has not been annealed.
in the median
Izod impact strength XY4.5-5 KJ/m2p. 1: Izod Impact Strength (X-Y) ISO 180 KJ/m2ISO 180as printednotched
print settingsTest Equipment Guider IIs (Flashforge); Nozzle Diameter 0.4mm; Nozzle Temperature 240 °C; Printing Speed 50mm/s; Wall Thickness 1.2mm; Infill 100%; Note: The above test parameter data are obtained from actual printing, and the printed model has not been annealed.
in the median
HDT at 0.45 MPa74 ℃p. 1: HDT@ 0.455 MPa (66 psi) ISO 75 ℃
ISO 75As the sheet prints it: 0.455 MPa 66 psi ISO 75
in the median
Continuous service temperature70 ℃p. 1: Continuous Service Temperature IEC 60216 ℃IEC 60216
Density1.27-1.28 g/cm3p. 1: Density ISO 1183 g/cm3ISO 1183
Water absorption0.2 %p. 1: Water Absorption (23℃/24h) ISO 62 %
ISO 62As the sheet prints it: 23℃/24h ISO 62
tested at 23°C
Melt mass-flow rate4-6 g/10minp. 1: Melt Index MFR (220℃/2.16Kg) ISO 1133 g/10min
ISO 1133As the sheet prints it: 220℃/2.16Kg ISO 1133
tested at 220°C

Print settings

Nozzle
220–240 °Cown data sheet
Bed
25–80 °Cown data sheet
Heated chamber
25–50 °Cown data sheet
Drying
70 °C for ≥ 5 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 220~240℃ (230℃ recommended); Bed Room temperature~80℃ (70℃ recommended); Chamber Room temperature~50℃; Drying Using a hot dry air oven at 70℃ for at least 5 hours is recommendedFlashforge, Technical Data Sheet PETG Filamentp. 2: Recommended printing settings: Nozzle Temperature; p. 2: Ambient Temperature for Printing; p. 3: Drying note

Price

Not in the price sample.

Its 2 documents

What the maker says (4)
Raise3D Premium PETGStrength XY, MPa31.9Strength Z, MPa—Modulus XY, GPa1.47Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg46Nozzle, °C230–240Bed, °C80Chamber, °CnoneDrying, °C, h658 h

Raise3D Premium PETGRaise3D

Published values

PropertyAs publishedConditionsOn the Overview
Raise3D, Raise3D Premium PETG Technical Data Sheet10 valuesUnless a row says otherwise: printed specimen
Tensile modulus XY1472 ± 270 (MPa)p. 1: Young’s modulus (X-Y)
ASTM D638, ISO 527, GB/T 1040As the sheet prints it: ASTM D638 (ISO 527, GB/T 1040)
moistureconditioned at room temperature for 24h prior to testing
in the median
Tensile strength (yield or break not stated) XY31.9 ± 1.1 (MPa)p. 1: Tensile strength (X-Y)
ASTM D638, ISO 527, GB/T 1040As the sheet prints it: ASTM D638 (ISO 527, GB/T 1040)
moistureconditioned at room temperature for 24h prior to testing
in the median
Elongation at break XY6.8 ± 0.9 (%)p. 1: Elongation at break (X-Y)
ASTM D638, ISO 527, GB/T 1040As the sheet prints it: ASTM D638 (ISO 527, GB/T 1040)
moistureconditioned at room temperature for 24h prior to testing
in the median
Flexural modulus orientation not stated1174 ± 64 (MPa)p. 1: Bending modulus
ASTM D790, ISO 178, GB/T 9341As the sheet prints it: ASTM D790 (ISO 178, GB/T 9341)
moistureconditioned at room temperature for 24h prior to testing
in the median
Flexural strength orientation not stated53.7 ± 2.4 (MPa)p. 1: Bending strength
ASTM D790, ISO 178, GB/T 9341As the sheet prints it: ASTM D790 (ISO 178, GB/T 9341)
moistureconditioned at room temperature for 24h prior to testing
in the median
Glass transition temperature81 (°C)p. 1: Glass transition temperature
DSCAs the sheet prints it: DSC, 10 ℃/min
in the median
Vicat softening temperature84 (˚C) °Cp. 1: Vicat Softening temperature
ASTM D1525, ISO 306, GB/T 1633As the sheet prints it: ASTM D1525 (ISO 306 GB/T 1633)
Density1.3 (g/cm³ at 21.5˚C)p. 1: Density
ASTM D792, ISO 1183, GB/T 1033As the sheet prints it: ASTM D792 (ISO 1183, GB/T 1033)
tested at 21.5 ˚C
Melt mass-flow rate3.9 (g/10 min)p. 1: Melt index (220 °C)
no standard namedAs the sheet prints it: 220 °C, 2.16 kg
tested at 220 °C
Melt mass-flow rate10.8 (g/10 min)p. 1: Melt index (240 °C)
no standard namedAs the sheet prints it: 240 °C, 2.16 kg
tested at 240 °C

Print settings

Nozzle
230–240 °Cown data sheet
Bed
80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

46 CAD/kgthe median of its 2 regular prices in the sample

2 listings
  • DigitMakers: 46 CAD/kgRaise3D Premium PETG Filament Black 1.75mm 1kg Spool (SKU RAISE3D-FL-PETG-1.75-1KG-BLK)in its price; seen 30 Sep 2026
  • Shop3D.ca: 46 CAD/kgRaise3D Premium PETG Filament - 1.75mm (1kg) / Black (SKU [S]5.11.19147A01)in its price; seen 30 Sep 2026

Its 2 documents

What the maker says (2)
Yousu PETGStrength XY, MPa53Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C74HDT 1.8, °C70Price, CAD/kg—Nozzle, °C220–260Bed, °C100–110Chamber, °CnoneDrying, °C, h658 h

Yousu PETGYousu

Published values

PropertyAs publishedConditionsOn the Overview
Yousu, Yousu PETG 3D FILMAENT Technical Data Sheet15 values
Tensile yield strength orientation not stated53 MPap. 1: Tensile Strength (53)
ASTM D638As the sheet prints it: ASTM D638; rate=50mm/min; yield
in the median
Tensile break strength orientation not stated26 MPap. 1: Tensile Strength (26)
ASTM D638As the sheet prints it: ASTM D638; rate=50mm/min; break
not in the median: another value of this product is in it
Elongation at break orientation not stated70 %p. 1: Tensile Elongation (70)
ASTM D638As the sheet prints it: ASTM D638; rate=50mm/min; break
in the median
Elongation at yield orientation not stated5.0 %p. 1: Tensile Elongation (5.0)
ASTM D638As the sheet prints it: ASTM D638; rate=50mm/min; yield
listed under other properties
Flexural modulus orientation not stated2150 MPap. 1: Flexural Modulus
ASTM D790As the sheet prints it: ASTM D790; rate=1.27mm/min
in the median
Flexural strength orientation not stated80 MPap. 1: Flexural Strength
ASTM D790As the sheet prints it: ASTM D790; rate=1.27mm/min
in the median
Izod impact strength orientation not stated90 J/mp. 1: Impact Strength, IZOD notchedASTM D256tested at 23℃not in the median: in J/m
Hardness116 Rockwell Rp. 1: Rockwell Hardness ASTM D785 R-scaleASTM D785listed under other properties
HDT at 0.45 MPa74 ℃p. 1: Heat Distortion Temperature (74)
ASTM D648As the sheet prints it: ASTM D648; 0.45 MPa
in the median
HDT at 1.8 MPa70 ℃p. 1: Heat Distortion Temperature (70)
ASTM D648As the sheet prints it: ASTM D648; 1.8 MPa
in the median
Vicat softening temperature83 ℃p. 1: Vicat Softening Temperature
ASTM D1525As the sheet prints it: ASTM D1525; 1KG
Density1.27 g/cm3p. 1: Density ASTM D1505 g/cm3 23 ℃
ASTM D1505As the sheet prints it: 23 ℃ ASTM D1505
tested at 23°C
Water absorption0.15 %p. 1: Water Absorption ASTM D570 % 23 ℃, 24hr
ASTM D570As the sheet prints it: 23 ℃ 24hr ASTM D570
tested at 23°C
Dielectric strength17 KV/mmp. 1: Dielectric Strength ASTM D149 KV/mmASTM D149
Relative permittivity3.00p. 1: Dielectric Constant
ASTM D150As the sheet prints it: ASTM D150; frequency=60 Hz

Print settings

Nozzle
220–260 °Cown data sheet
Bed
100–110 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (20)
colorFabb PETG EconomyStrength XY, MPa50Strength Z, MPa—Modulus XY, GPa1.9Charpy notched, kJ/m²4.7HDT 0.45, °C77HDT 1.8, °C—Price, CAD/kg—Nozzle, °C235–255Bed, °C70–80Chamber, °CnoneDrying, °C, h658 h

colorFabb PETG EconomycolorFabb

Published values

PropertyAs publishedConditionsOn the Overview
colorFabb, Technical datasheet PETG Economy16 valuesThe same values also in colorFabb, Technical datasheet colorFabb PETG Economy and colorFabb, Technical datasheet PETG Economy.Unless a row says otherwise: printed specimen
Tensile modulus XY1930 MPap. 1: Tensile modulus MPaISO 527
print settingsXY plane, 0.15mm layerheight, 100% infill, 0.4mm nozzle, 245 °C nozzle temperature and 70 °C bed temperature
not in the median: another value of this product is in it
Tensile modulus orientation not stated2000 MPap. 2: Tensile modulus MPaalso in colorFabb, Technical datasheet colorFabb PETG Economymoulded bar (resin supplier's value), ISO 527not in the median: measured on a moulded bar
Tensile strength (yield or break not stated) XY51.25 MPap. 1: Tensile strength MPaISO 527
print settingsXY plane, 0.15mm layerheight, 100% infill, 0.4mm nozzle, 245 °C nozzle temperature and 70 °C bed temperature
not in the median: another value of this product is in it
Tensile strength (yield or break not stated) orientation not stated49 MPap. 2: Tensile strength MPamoulded bar (resin supplier's value), ISO 527not in the median: measured on a moulded bar
Tensile yield strength XY51.25 MPap. 1: Yield strength MPaISO 527
print settingsXY plane, 0.15mm layerheight, 100% infill, 0.4mm nozzle, 245 °C nozzle temperature and 70 °C bed temperature
not in the median: another value of this product is in it
Tensile break strength XY28.67 MPap. 1: Tensile stress at break MPaISO 527
print settingsXY plane, 0.15mm layerheight, 100% infill, 0.4mm nozzle, 245 °C nozzle temperature and 70 °C bed temperature
not in the median: another value of this product is in it
Elongation at break XY91.06 %p. 1: Tensile strain at break %ISO 527
print settingsXY plane, 0.15mm layerheight, 100% infill, 0.4mm nozzle, 245 °C nozzle temperature and 70 °C bed temperature
not in the median: another value of this product is in it
Elongation at break orientation not stated36 %p. 2: Tensile strain at break %also in colorFabb, Technical datasheet colorFabb PETG Economymoulded bar (resin supplier's value), ISO 527not in the median: measured on a moulded bar
Elongation at yield XY4.35 %p. 1: Yield strain %ISO 527
print settingsXY plane, 0.15mm layerheight, 100% infill, 0.4mm nozzle, 245 °C nozzle temperature and 70 °C bed temperature
listed under other properties
Tensile strain at strength XY4.35 %p. 1: Tensile strain at tensile strength %ISO 527
print settingsXY plane, 0.15mm layerheight, 100% infill, 0.4mm nozzle, 245 °C nozzle temperature and 70 °C bed temperature
listed under other properties
Flexural strength XY68.17 MPap. 1: Flexural strength MPaISO 178
print settingsXY plane, 0.15mm layerheight, 100% infill, 0.4mm nozzle, 245 °C nozzle temperature and 70 °C bed temperature
not in the median: another value of this product is in it
Flexural stress at conventional deflection XY42.35 MPap. 1: Flexural strain at standard deflectionISO 178listed under other properties
Charpy impact strength4.72 kJ/m2p. 1: Charpy notched impact strength kJ/m2
ISO 179As the sheet prints it: ISO 179-1/1
not in the median: another value of this product is in it
HDT76.75 °Cp. 1: Heat Deflection Temperature (HDT) °CISO 75not in the median: set apart (never used to pass), no stated test load
Glass transition temperature70 °Cp. 2: Glass transition temperature °Calso in colorFabb, Technical datasheet PETG Economymoulded bar (resin supplier's value), no standard statednot in the median: the resin supplier's value, not a printed part
Density1,28 g/cm3p. 2: Density g/cm3also in colorFabb, Technical datasheet PETG Economymoulded bar (resin supplier's value), no standard stated
colorFabb, Technical datasheet PETG Economy8 valuesThe same values also in colorFabb, Technical datasheet PETG Economy.Unless a row says otherwise: printed specimen
Tensile modulus XY1900 MPap. 1: Youngs Modulus Tensile, ISO 527-1A
ISO 527As the sheet prints it: ISO 527-1A
print settingsThe specimens have been printed in XY plane, using 0.15 mm layer height, 100% infill, 0,4 mm nozzle, 245˚C nozzle temperature and 70˚C bed temperature.
in the median
Tensile strength (yield or break not stated) XY50 MPap. 1: Tensile Strength Tensile, ISO 527-1A
ISO 527As the sheet prints it: ISO 527-1A
print settingsThe specimens have been printed in XY plane, using 0.15 mm layer height, 100% infill, 0,4 mm nozzle, 245˚C nozzle temperature and 70˚C bed temperature.
in the median
Elongation at break XY90 %p. 1: Elongation at break Tensile, ISO 527-1A
ISO 527As the sheet prints it: ISO 527-1A
print settingsThe specimens have been printed in XY plane, using 0.15 mm layer height, 100% infill, 0,4 mm nozzle, 245˚C nozzle temperature and 70˚C bed temperature.
in the median
Flexural modulus XY1000 MPap. 1: Flexural Modulus Flexural, ISO 178also in colorFabb, Technical datasheet PETG EconomyISO 178
print settingsThe specimens have been printed in XY plane, using 0.15 mm layer height, 100% infill, 0,4 mm nozzle, 245˚C nozzle temperature and 70˚C bed temperature.
in the median
Flexural strength XY70 MPap. 1: Flexural Strength Flexural, ISO 178ISO 178
print settingsThe specimens have been printed in XY plane, using 0.15 mm layer height, 100% infill, 0,4 mm nozzle, 245˚C nozzle temperature and 70˚C bed temperature.
in the median
Charpy impact strength XY4.7 kJ/m2p. 1: Impact Strength Charpy Notch, ISO 179ISO 179notchedin the median
Izod impact strength107 J/mp. 1: Izod Impact Strength Izod Notch, ISO 179moulded bar (resin supplier's value), ISO 179notchednot in the median: in J/m
HDT at 0.45 MPa65 °Cp. 1: Heat Deflection Temp. HDT-B, ISO 75moulded bar (resin supplier's value),
ISO 75As the sheet prints it: HDT B ISO 75
not in the median: measured on a moulded bar
colorFabb, Technical datasheet colorFabb PETG Economy1 value
Tensile yield strength orientation not stated49 MPap. 1: Tensile Strength@Yield MPa
ISO 527As the sheet prints it: ISO 527-1
not in the median: another value of this product is in it

Print settings

Nozzle
235–255 °Cown data sheet
Bed
70–80 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (6)
Prusa Research Buddy3D PET-GStrength XY, MPa51Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C64Price, CAD/kg—Nozzle, °C235–265Bed, °C≤ 85Chamber, °CnoneDrying, °C, hif wet

Prusa Research Buddy3D PET-GPrusa Research

Published values

PropertyAs publishedConditionsOn the Overview
Prusa Research, Buddy3D Product card PET-G12 valuesUnless a row says otherwise: specimen not stated
Tensile strength (yield or break not stated) orientation not stated51 MPa
ASTM D638As the sheet prints it: D638
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated138 %
ASTM D638As the sheet prints it: D638
not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2.1 GPa
ASTM D790As the sheet prints it: D790
not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated73 MPap. 2: Bending stress
ASTM D790As the sheet prints it: D790
not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength orientation not stated100 J/mp. 2: Notched impact strength, IZOD
ASTM D256As the sheet prints it: ASTM D256; test conditions cell=1.27 mm/min
not in the median: in J/m
HDT at 0.45 MPa70 °C
ASTM D648As the sheet prints it: 0.45 MPa D648
in the median
HDT at 1.8 MPa64 °C
ASTM D648As the sheet prints it: 1.8 MPa D648
in the median
Glass transition temperature90 °Cp. 2: Glass transition DSC – °C
DSCAs the sheet prints it: DSC –
in the median
Vicat softening temperature85 °Cp. 2: Vicat softening point D1525 – °C
ASTM D1525As the sheet prints it: D1525
Decomposition temperature350 °Cp. 3: Decomposition of PET-Gno standard stated
Water absorption0.12 %p. 2: Moisture absorption ASTM D570 – %ASTM D570
Surface resistivity10^16 Ω
ASTM D257As the sheet prints it: D257

Print settings

Nozzle
235–265 °Cown data sheet
Bed
85 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
optionalown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (10)
Fiberlogy MATTE PET-GStrength XY, MPa44Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²2IzodHDT 0.45, °C68HDT 1.8, °C62Price, CAD/kg—Nozzle, °C250–270Bed, °C90Chamber, °CnoneDrying, °C, h604 h

Fiberlogy MATTE PET-GFiberlogy

Published values

PropertyAs publishedConditionsOn the Overview
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-G7 valuesThe same values also in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-G.
Tensile yield strength orientation not stated44 MPap. 1: Tensile Strength @ Yield ISO 527 MPaISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated7 %p. 1: Elongation @ Yield ISO 527 %also in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-GISO 527listed under other properties
Flexural strength orientation not stated45 MPap. 1: Flexular Strength ISO 178 MPaalso in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-GISO 178not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength2 kJ/m2p. 1: Izod Impact Strength (Notched) @ 23°C ISO 180 kJ/m2also in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-G
ISO 180As the sheet prints it: 23°C ISO 180
tested at 23°C		not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa62 °Cp. 1: Heat Distortion Temperature @ 1.8 MPa ISO 75 °Calso in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-G
ISO 75As the sheet prints it: 1.8 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
Glass transition temperature80 °Cp. 1: Glass Transition Temperature Tg ASTM D3418 °CASTM D3418in the median
Vicat softening temperature78 °Cp. 1: Vicat Softening Temperature ISO 306 °Calso in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-GISO 306
Fiberlogy, PETG Matte Filament2 valuesUnless a row says otherwise: specimen not stated
Izod impact strength orientation not stated2 kJ/m²p. 1: Izod impact strength (uncharved) @ 23°CISO 180tested at 23 °Cunnotchednot in the median: unnotched
Density1.29 g/cm³p. 1: Densityno standard stated
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-G2 values
HDT at 0.45 MPa68 °Cp. 1: Heat Distortion Temperature @ 0.45 MPa ISO 75 °C
ISO 75As the sheet prints it: 0.45 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
Density1.26 g/cm³p. 1: Specific DensityISO 1183

Print settings

Nozzle
250–270 °Cown data sheet
Bed
90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60 °C for 4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): nozzle in Fiberlogy, TECHNICAL DATA SHEET Fiberlogy MATTE PET-G.

Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (1)
FormFutura HDglassData sheet shared with FormFutura ReForm - rPETStrength XY, MPa50Strength Z, MPa—Modulus XY, GPa1.94Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C195–225Bed, °C60–80Chamber, °C—Drying, °C, h658 h

FormFutura HDglassFormFutura

Data sheet shared with FormFutura ReForm - rPET: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
FormFutura, Technical Data Sheet HDglass™10 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated1940 Mpap. 1: Tensile modulusISO 527not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated50 Mpap. 1: Tensile strengthASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated120 %p. 1: Elongation at breakASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2147.6 Mpap. 1: Flexural modulusASTM D790not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated70.6 Mpap. 1: Flexural strengthASTM D790not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength7.2 KJ/m²p. 1: Impact strengthASTM D256tested at @23° Cnotchednot in the median: to another standard
Hardness105 Rockwell Rp. 1: HardnessASTM D785listed under other properties
HDT at 0.45 MPa70° C °Cp. 1: Viscat softening temp.
ASTM D648As the sheet prints it: ASTM D648; @ 0.455 Mpa (66psi)
in the median
Density1.27 g/ccp. 1: Specific gravityASTM D792
Water absorption0.13 %p. 1: Moisture absorptionASTM D570

Print settings

Nozzle
195–225 °Cown data sheet
Bed
60–80 °CFormFutura ReForm - rPET's data sheet, shared
Heated chamber
not stated
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
  • BenefitsHDglass™ is developed/modified to have an impressive thermal stability and by that perfect 3D printing flowing behaviour, resulting in a very easy to print 3D printer filament with a remarkable transparency and excellent properties with respect to strength, toughness and temperature resistance.FormFutura, Technical Data Sheet HDglass™p. 1
FormFutura ReForm - rPETData sheet shared with FormFutura HDglassStrength XY, MPa50Strength Z, MPa—Modulus XY, GPa1.94Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C195–225Bed, °C60–80Chamber, °C—Drying, °C, h658 h

FormFutura ReForm - rPETFormFutura

Data sheet shared with FormFutura HDglass: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
FormFutura, Technical Data Sheet ReForm™ - rPET9 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated1940 Mpap. 1: Tensile modulusISO 527not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated50 Mpap. 1: Tensile strengthASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated120 %p. 1: Elongation at breakASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2147.6 Mpap. 1: Flexural modulusASTM D790not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated70.6 Mpap. 1: Flexural strengthASTM D790not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength7.2 KJ/m²p. 1: Impact strengthASTM D256tested at 23° Cnotchednot in the median: to another standard
Hardness105 Rockwell Rp. 1: HardnessASTM D785listed under other properties
Density1.27 g/ccp. 1: Specific gravityASTM D792
Water absorption0.13 %p. 1: Water absorption - - - Moisture absorption MechanicalASTM D570

Print settings

Nozzle
195–225 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not stated
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): nozzle in FormFutura, ReForm - rPET.

Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (5)
  • Printing adviceHeat bed: ± 60 – 80° C Enclosure: No / RecommendedFormFutura, ReForm - rPETp. 1
  • BenefitsThis sustainable PETG filament combines strength and toughness with printability.FormFutura, ReForm - rPETp. 1
  • Surface finishHomogeneous compound runs can vary in color intensity.FormFutura, ReForm - rPETp. 1
  • Surface finishThis may result in lighter or darker 3D printing filament colors extruded from various homogeneous compound runs.FormFutura, ReForm - rPETp. 1
  • Surface finishrPET White and Black will always have the same color, as extrusion waste from black and white PETG filament is collected separately.FormFutura, ReForm - rPETp. 1
SIDDAMENT PETGStrength XY, MPa55Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²17IzodHDT 0.45, °C68HDT 1.8, °C—Price, CAD/kg—Nozzle, °C240–260Bed, °C70Chamber, °CnoneDrying, °C, h502–4 h

SIDDAMENT PETGSIDDAMENT

Published values

PropertyAs publishedConditionsOn the Overview
SIDDAMENT, PETG - Technical Datasheet8 valuesUnless a row says otherwise: specimen not stated
Tensile strength (yield or break not stated) orientation not stated55 MPap. 1: Tensile Strength ISO 527 MPaISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated17.3 %p. 1: Elongation at Break ISO 527 %ISO 527not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2226 MPap. 1: Flexural Modulus ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated77 MPap. 1: Bending Strength ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength17 kJ/m2p. 1: Notched Impact Strength ISO 180 kJ/m2ISO 180not in the median: set apart (never used to pass), test bar not described as printed
HDT68 °Cp. 1: Heat Deflection ISO 75 °CISO 75not in the median: set apart (never used to pass), no stated test load
Density1.23 g/cm3p. 1: Density ISO 1183 g/cm3ISO 1183
Water absorption0.4 %p. 1: Water Absorption ISO 62 %ISO 62

Print settings

Nozzle
240–260 °Cown data sheet
Bed
70 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
optional: 50 °C for 2–4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 240-260°C; Bed 70°C; Drying If damp, dry at 50°C for 2-4 hours.SIDDAMENT, PETG - Technical Datasheetp. 1: Drying note; p. 2: Nozzle Temperature; p. 2: Bed Temperature; p. 2: Printing Platform; p. 2: Nozzle Diameter

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
Spectrum PET-G PremiumStrength XY, MPa48Strength Z, MPa—Modulus XY, GPa1.95Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–255Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

Spectrum PET-G PremiumSpectrum

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, TECHNICAL DATA SHEET PET-G Premium12 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated1950 MPap. 1: Tensile Modulus
ASTM D638As the sheet prints it: D 638
not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated26 MPaphysically implausiblep. 1: Tensile Stress at Yield
ASTM D638As the sheet prints it: D 638
not in the median: physically implausible as published
Tensile break strength orientation not stated48 MPap. 1: Tensile Stress at Break
ASTM D638As the sheet prints it: D 638
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated58,00 %p. 1: Elongation at Break
ASTM D638As the sheet prints it: D 638
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4,30 %p. 1: Elongation at Yield
ASTM D638As the sheet prints it: D 638
listed under other properties
Flexural modulus orientation not stated1880 MPap. 1: Flexural Modulus
ASTM D790As the sheet prints it: D 790
not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated64 MPap. 1: Flexural Strength
ASTM D790As the sheet prints it: D 790
not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength126 J/mp. 1: Izod Impact Strength, Notched @ 23°C
ASTM D256As the sheet prints it: 23°C D 256
tested at 23°C		not in the median: in J/m
Izod impact strength57 J/mp. 1: Izod Impact Strength, Notched @ -40°C
ASTM D256As the sheet prints it: -40°C D 256
tested at -40°C		not in the median: in J/m
Hardness108 Rockwell Rp. 1: Rockwell Hardness, R Scale
ASTM D785As the sheet prints it: D 785
listed under other properties
HDT70 °Cp. 1: Heat Deflection Temperature
ASTM D648As the sheet prints it: D 648
not in the median: set apart (never used to pass), no stated test load
Density1.27 g/cm3p. 1: Specific Gravity
ASTM D792As the sheet prints it: D 792
Spectrum, 3D Printing Filament Manufacturer PRODUCT PORTFOLIO1 value
HDT at 0.45 MPa78°Cp. 4: HDT B
no standard namedAs the sheet prints it: method=B
not in the median: replaced by a newer edition of the sheet or by the data sheet, so not used in deciding

Print settings

Nozzle
230–255 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededown data sheet
Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (8)
Filament2Print PETGStrength XY, MPa53Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–260Bed, °C70–90Chamber, °CnoneDrying, °C, h606 h

Filament2Print PETGFilament2Print

Published values

PropertyAs publishedConditionsOn the Overview
Filament2Print, PETG Technical Data Sheet10 values
Tensile modulus orientation not stated358.495 MPa (TDS prints "358,495" with European decimal separator)physically implausiblep. 1: Elastic ModulusISO 527, GB/T 9341not in the median: physically implausible as published
Tensile yield strength orientation not stated52.977 MPA (TDS prints "52,977" with European decimal separator)p. 1: Yield StrengthISO 527, GB/T 1040in the median
Elongation at break orientation not stated18.268 % (TDS prints "18,268" with European decimal separator)p. 1: Elongation at BreakISO 527, GB/T 1040in the median
Flexural modulus orientation not stated1954,543 MPap. 1: Flexural ModulusISO 178, GB/T 9341in the median
Flexural strength orientation not stated75.071 MPa (TDS prints "75,071" with European decimal separator)p. 1: Flexural StrengthISO 178, GB/T 9341in the median
Charpy impact strength2.721 kJ/m² (TDS prints "2,721" with European decimal separator)p. 1: Impact StrengthISO 179, GB/T 1043not in the median: notch not stated
HDT at 0.45 MPa70 °Cp. 1: Vicat Softening Temperature
ISO 75As the sheet prints it: ISO 75; 0.45 MPa
in the median
Density1,24 g/cm³p. 1: DensityISO 1183, GB/T 1033
Water absorption0.12 %p. 1: Moisture absorption limitISO 62
Melt mass-flow rate2,86 g/10 minp. 1: Melt Flow Index (MFR)ISO 1133, GB/T 3682

Print settings

Nozzle
230–260 °Cown data sheet
Bed
70–90 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
60 °C for 6 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
Flashforge HS PETGStrength XY, MPa41Strength Z, MPa—Modulus XY, GPa1.4Charpy notched, kJ/m²—HDT 0.45, °C68HDT 1.8, °C—Price, CAD/kg—Nozzle, °C220–260Bed, °C25–60Chamber, °C25–40Drying, °C, h658 h

Flashforge HS PETGFlashforge

Published values

PropertyAs publishedConditionsOn the Overview
Flashforge, Technical Data Sheet HS PETG Filament10 values
Tensile modulus XY1400-1500 Mpap. 1: Modulus of Elasticity (X-Y) ISO 527 MpaISO 527in the median
Tensile strength (yield or break not stated) XY41-45 Mpap. 1: Tensile Strength (X-Y) ISO 527 MpaISO 527in the median
Elongation at break XY10-12 %p. 1: Elongation at Break (X-Y) ISO 527 %ISO 527in the median
Flexural strength XY64-66 Mpap. 1: Bending Strength (X-Y) ISO 178 MpaISO 178in the median
Izod impact strength XY5-6 KJ/㎡p. 1: Izod Impact Strength (X-Y) ISO 180 KJ/㎡ISO 180not in the median: notch not stated
HDT at 0.45 MPa68 ℃p. 1: HDT@ 0.455 MPa(66 psi) ISO 75 ℃
ISO 75As the sheet prints it: 0.455 MPa (66 psi) ISO 75
in the median
Continuous service temperature65 ℃p. 1: Continuous Service Temperature IEC 60216 ℃IEC 60216
Density1.27-1.28 g/cm³p. 1: Density ISO 1183 g/cm³ISO 1183
Water absorption0.2 %p. 1: Water Absorption (23℃/24h) ISO 62 %
ISO 62As the sheet prints it: 23℃/24h ISO 62
tested at 23°C
Melt mass-flow rate8-12 g/10minp. 1: Melt Flow Rate (MFR) (220℃/2.16Kg) ISO 1133 g/10min
ISO 1133As the sheet prints it: MFR 220℃/2.16Kg ISO 1133
tested at 220°C

Print settings

Nozzle
220–260 °Cown data sheet
Bed
25–60 °Cown data sheet
Heated chamber
25–40 °Cown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 220~260℃; Bed Room temperature~60℃; Chamber Room temperature~40℃Flashforge, Technical Data Sheet HS PETG Filamentp. 2: Recommended printing settings; p. 2: Build Surface Material; p. 2: Nozzle Diameter (recommended printing settings)

Price

Not in the price sample.

Its 2 documents

What the maker says (3)
Spectrum PET-G FX120Modified: declared softer gradeStrength XY, MPa22Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg87Nozzle, °C240–260Bed, °C80Chamber, °C—Drying, °C, h854 h

Spectrum PET-G FX120Spectrum

Modified: declared softer grade. Its values are kept out of the material's medians.

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, TECHNICAL DATA SHEET PET-G FX1207 valuesUnless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated14 MPap. 1: Tensile Stress @ Yield
ASTM D638As the sheet prints it: D 638
not in the median: another value of this product is in it
Tensile break strength orientation not stated22 MPap. 1: Tensile Stress @ Break
ASTM D638As the sheet prints it: D 638
not in the median: added filler or additive
Elongation at break orientation not stated400,00%p. 1: Elongation @ Break
ASTM D638As the sheet prints it: D 638
not in the median: added filler or additive
Elongation at yield orientation not stated38,00%p. 1: Elongation @ Yield
ASTM D638As the sheet prints it: D 638
listed under other properties
Flexural modulus orientation not stated150 MPap. 1: Flexural Modulus
ASTM D790As the sheet prints it: D 790
not in the median: added filler or additive
Izod impact strength orientation not stated40 J/mp. 1: Izod Impact Strength, Notched @ -40°C
ASTM D256As the sheet prints it: D 256
tested at -40°C		not in the median: in J/m
Hardness55 Shore Dp. 1: Shore D Scale
ASTM D2240As the sheet prints it: D 2240
not in the median: added filler or additive
Spectrum, 3D Printing Filament Manufacturer PRODUCT PORTFOLIO3 valuesUnless a row says otherwise: specimen not stated
Hardness95A Shore Ap. 3: Shore hardness 95Ano standard statednot in the median: added filler or additive
Vicat softening temperature170°Cp. 5: VICATno standard stated
Density1.13 g/cm³p. 5: Density [g/cm³]no standard stated

Print settings

Nozzle
240–260 °Cown data sheet
Bed
80 °Cown data sheet
Heated chamber
not stated
Drying
85 °C for 4 hown data sheet
Hardened nozzle
not neededown data sheet
Its 4 print profiles, in the documents' words

Price

87 CAD/kgits one regular price in the sample

1 listing
  • 3D Printing Canada: 87 CAD/kgNatural - Spectrum PET-G FX120 Filament - 1.75mm, 1kg (SKU 67bbb9f4eb8ea)in its price; seen 30 Sep 2026

Its 5 documents

What the maker says (7)
Creality Hyper PETGStrength XY, MPa48Strength Z, MPa—Modulus XY, GPa3.5Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C220–260Bed, °C70–80Chamber, °C0–50Drying, °C, h658 h

Creality Hyper PETGCreality

Published values

PropertyAs publishedConditionsOn the Overview
Creality, Hyper PETG Filament Technical Data Sheet8 values
Tensile modulus XY3500 MPap. 1: Emodulus (X-Y) ASTM D638 (ISO 527, GB/T 1040)ASTM D638, ISO 527, GB/T 1040in the median
Tensile strength (yield or break not stated) XY48 MPap. 1: Tensile strength (X-Y) ASTM D638 (ISO 527, GB/T 1040)ASTM D638, ISO 527, GB/T 1040in the median
Elongation at break XY10 %p. 1: Elongation at break (X-Y) ASTM D638 (ISO 527, GB/T 1040)ASTM D638, ISO 527, GB/T 1040in the median
Flexural modulus orientation not stated2200 MPap. 1: Flexural modulus ASTMD790 (ISO 178, GB/T 9341)ASTM D790, ISO 178, GB/T 9341in the median
Impact strength, test unclear orientation not stated6 (kJ/m²)p. 1: Notch impact strength
ASTM D256, ISO 179, GB/T 1043As the sheet prints it: ASTM D256 (ISO 179, GB/T 1043)
notchedWhich test: probably Charpy		listed under other properties
Vicat softening temperature83 °Cp. 1: Vicat Softening temperature ASTM D1525 (ISO 306 GB/T 1633)ASTM D1525, ISO 306, GB/T 1633
Density1.27 g/cm3p. 1: Density ASTM D792 (ISO 1183, GB/T 1033)ASTM D792, ISO 1183, GB/T 1033
Melt mass-flow rate12 g/10 minp. 1: Melt index 190°C, 2.16kg
no standard namedAs the sheet prints it: 190°C 2.16kg
tested at 190°C

Print settings

Nozzle
220–260 °Cown data sheet
Bed
70–80 °Cown data sheet
Heated chamber
0–50 °Cown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (2)
Fabru Type G polyethylene terephthalate (PETG)Strength XY, MPa50Strength Z, MPa—Modulus XY, GPa2.08Charpy notched, kJ/m²—HDT 0.45, °C77HDT 1.8, °C—Price, CAD/kg—Nozzle, °C210–260Bed, °C50–80Chamber, °CnoneDrying, °C, h652–4 h

Fabru Type G polyethylene terephthalate (PETG)Fabru

Published values

PropertyAs publishedConditionsOn the Overview
Fabru, Polyethylenterephthalat Typ G (PETG)7 values
Tensile modulus orientation not stated2079 MPap. 1: Zug-E-Modul (ASTM D790)ASTM D790not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated50 MPap. 1: Streckspannung (ASTM D638)ASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated165 %p. 1: Reissdehnung (ASTM D638)ASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated5 %p. 1: Streckdehnung (ASTM D638)ASTM D638listed under other properties
Vicat softening temperature81 °Cp. 1: Vicat Erweichungstemperatur Ano standard stated
Density1.29 g/cm3p. 1: Dichte (ASTM D792)ASTM D792
Mould shrinkage orientation not stated0.2-0.5 %p. 1: Schwindung (ISO 294-4, 2577)
ISO 294As the sheet prints it: 2577 ISO 294-4
Fabru, Type G polyethylene terephthalate (PETG)1 value
HDT at 0.45 MPa77 °Cp. 1: Heat deflection temperature 0.45 MPa (ASTM D648)
ASTM D648As the sheet prints it: ASTM D648; 0.45 MPa
not in the median: set apart (never used to pass), test bar not described as printed

Print settings

Nozzle
210–260 °Cown data sheet
Bed
50–80 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 2–4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (31)
FormFutura Bulk PETGStrength XY, MPa50.2Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C79HDT 1.8, °C—Price, CAD/kg—Nozzle, °C235–255Bed, °C80–90Chamber, °CnoneDrying, °C, hdry first

FormFutura Bulk PETGFormFutura

Published values

PropertyAs publishedConditionsOn the Overview
FormFutura, TECHNICAL DATA SHEET Bulk PETG9 valuesUnless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated50,2 MPap. 2: Tensile strength at yield (23°C, 50mm/min)
ASTM D638As the sheet prints it: 23°C 50mm/min ASTM D638
tested at 23°C		not in the median: set apart (never used to pass), test bar not described as printed
Tensile break strength orientation not stated29 MPap. 2: Tensile strength at break (23°C, 50mm/min)
ASTM D638As the sheet prints it: 23°C 50mm/min ASTM D638
tested at 23°C		not in the median: another value of this product is in it
Elongation at break orientation not stated160 %p. 2: Elongation at break (23°C, 50mm/min)
ASTM D638As the sheet prints it: 23°C 50mm/min ASTM D638
tested at 23°C		not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated6 %p. 2: Elongation at yield (23°C, 50mm/min)
ASTM D638As the sheet prints it: 23°C 50mm/min ASTM D638
tested at 23°C		listed under other properties
Flexural strength orientation not stated66.8 MPap. 2: Flexural strengthASTM D790not in the median: set apart (never used to pass), test bar not described as printed
HDT79 °Cp. 2: HDTASTM D648not in the median: set apart (never used to pass), no stated test load
Melting temperature200 °Cp. 2: Melting Pointno standard stated
Density1,29 g/cm3p. 2: Specific Gravity (23°C)
ASTM D792As the sheet prints it: 23°C ASTM D792
tested at 23°C
Melt mass-flow rate1.8 g/10minp. 2: MFI (210°C, 2.16kg)
ASTM D1238As the sheet prints it: ASTM D 1238; 2.16kg
tested at 210°C

Print settings

Nozzle
235–255 °Cown data sheet
Bed
80–90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
required, schedule not statedown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (6)
FormFutura ReFill PETGStrength XY, MPa20Strength Z, MPa—Modulus XY, GPa2.98Charpy notched, kJ/m²4.7IzodHDT 0.45, °C78HDT 1.8, °C—Price, CAD/kg35Nozzle, °C230–260Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

FormFutura ReFill PETGFormFutura

Published values

PropertyAs publishedConditionsOn the Overview
FormFutura, Technical Data Sheet ReFill PETG5 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated2980 MPap. 1: Tensile Modulus
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Tensile break strength orientation not stated20 MPap. 1: Tensile Strength at Break
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength4,7 kJ/m2p. 1: Izod impact strength (notched)ISO 180not in the median: set apart (never used to pass), test bar not described as printed
HDT78 °Cp. 1: HDTISO 306not in the median: set apart (never used to pass), no stated test load
Density1.29 g/cm3p. 1: Densityno standard stated

Print settings

Nozzle
230–260 °CBambu Lab Filament Guide
Bed
60–80 °CBambu Lab Filament Guide
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide

Price

34.6 CAD/kgits one regular price in the sample

1 listing
  • DigitMakers: 34.6 CAD/kgFormFutura ReFill PETG - 1.75mm 750g / Traffic Black (SKU FFTRA-REFILLPETG-RFPE-175TBLK-00750)in its price; seen 30 Sep 2026

Its document

What the maker says (5)
SIDDAMENT PETG MatteStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C68HDT 1.8, °C—Price, CAD/kg—Nozzle, °C240–260Bed, °C70Chamber, °C—Drying, °C, h502–4 h

SIDDAMENT PETG MatteSIDDAMENT

Published values

PropertyAs publishedConditionsOn the Overview
SIDDAMENT, PETG Matte - Technical Datasheet8 valuesUnless a row says otherwise: specimen not stated
Tensile strength (yield or break not stated) orientation not stated78 MPaphysically implausiblep. 1: Tensile Strength ISO 527 MPaISO 527not in the median: physically implausible as published
Elongation at break orientation not stated19 %p. 1: Elongation at Break ISO 527 %ISO 527not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2236 MPap. 1: Flexural Modulus ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated79 MPap. 1: Bending Strength ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength82 kJ/m2physically implausiblep. 1: Notched Impact Strength ISO 180 kJ/m2ISO 180not in the median: physically implausible as published
HDT68 °Cp. 1: Heat Deflection ISO 75 °CISO 75not in the median: set apart (never used to pass), no stated test load
Density1.23 g/cm3p. 1: Density ISO 1183 g/cm3ISO 1183
Water absorption0.4 %p. 1: Water Absorption ISO 62 %ISO 62

Print settings

Nozzle
240–260 °Cown data sheet
Bed
70 °Cown data sheet
Heated chamber
not stated
Drying
optional: 50 °C for 2–4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 240-260°C; Bed 70°C; Drying If damp, dry at 50°C for 2-4 hours.SIDDAMENT, PETG Matte - Technical Datasheetp. 1: Drying note; p. 2: Nozzle Temperature; p. 2: Bed Temperature; p. 2: Printing Platform; p. 2: Nozzle Diameter

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
3D-Fuel PETGStrength XY, MPa25Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C67HDT 1.8, °C—Price, CAD/kg—Nozzle, °C245–265Bed, °C70–90Chamber, °CnoneDrying, °C, h716 h

3D-Fuel PETG3D-Fuel

Published values

PropertyAs publishedConditionsOn the Overview
3D-Fuel, Technical Data Sheet PETG10 valuesUnless a row says otherwise: specimen not stated; its document points to a moulded or resin bar
Tensile break strength orientation not stated25 MPa
ASTM D638As the sheet prints it: D638
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated30 %
ASTM D638As the sheet prints it: D638
not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated2200 MPa
ASTM D790As the sheet prints it: D790
not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated75 MPa
ASTM D790As the sheet prints it: D790
not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength69 J/mp. 1: Izod Impact Strength, Notched @ 23°C (73°F)
ASTM D256As the sheet prints it: 23°C 73°F D256
tested at 23°C		not in the median: in J/m
Izod impact strength28 J/mp. 1: Izod Impact Strength, Notched @ -40°C (-40°F)
ASTM D256As the sheet prints it: D256
tested at -40°C (-40°F)		not in the median: in J/m
Izod impact strength orientation not stated2600 J/mp. 1: Impact Strength, Unnotched @ -40°C (-40°F)
ASTM D4812As the sheet prints it: D4812
tested at -40 °C		not in the median: in J/m
Hardness106 Rockwell Rspecimen not stated,
ASTM D785As the sheet prints it: D785
listed under other properties
HDT at 0.45 MPa67 °Cp. 1: Deflection Temperature @ 0.455 MPa (66 psi)
no standard namedAs the sheet prints it: 0.455 MPa 66 psi
not in the median: set apart (never used to pass), test bar not described as printed
Water absorption.13 %specimen not stated,
ASTM D570As the sheet prints it: 24 hr immersion D570

Print settings

Nozzle
245–265 °Cown data sheet
Bed
70–90 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
71 °C for 6 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (3)
3D-Fuel Pro PETGStrength XY, MPa44.6Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–260Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

3D-Fuel Pro PETG3D-Fuel

Published values

PropertyAs publishedConditionsOn the Overview
3D-Fuel, TECHNICAL DATA SHEET Pro PETG18 valuesUnless a row says otherwise: specimen not stated; its document points to a moulded or resin bar
Tensile yield strength orientation not stated455 Kgf/cm2p. 2: Tensile Strength @ Yield ASTM D638 Kgf/cm2ASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated49 MPap. 3: Tensile Strength @ Yield ISO 527 MPaISO 527not in the median: another value of this product is in it
Tensile break strength orientation not stated300 Kgf/cm2p. 2: Tensile Strength @ Break ASTM D638 Kgf/cm2ASTM D638not in the median: another value of this product is in it
Tensile break strength orientation not stated30 MPap. 3: Tensile Strength @ Break ISO 527 MPaISO 527not in the median: another value of this product is in it
Elongation at break orientation not stated250 %p. 2: Elongation @ Break ASTM D638 %ASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated240 %p. 3: Elongation @ Break ISO 527 %ISO 527not in the median: another value of this product is in it
Elongation at yield orientation not stated4.5 %p. 2: Elongation @ Yield ASTM D638 %ASTM D638listed under other properties
Elongation at yield orientation not stated4.1 %p. 3: Elongation @ Yield ISO 527 %ISO 527listed under other properties
Flexural modulus orientation not stated22,000 Kgf/cm2p. 2: Flexural Modulus ASTM D790 Kgf/cm2ASTM D790not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated1,800 MPap. 3: Flexural Modulus ISO 178 MPaISO 178not in the median: another value of this product is in it
Flexural strength orientation not stated755 Kgf/cm2p. 2: Flexural Strength ASTM D790 Kgf/cm2ASTM D790not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated64 MPap. 3: Flexural Strength ISO 178 MPaISO 178not in the median: another value of this product is in it
Izod impact strength105 J/mp. 2: Izod Impact Strength ASTM D256 J/mASTM D256notchednot in the median: in J/m
Izod impact strength7.3 KJ/m2p. 3: Izod Impact Strength ISO 180 KJ/m2ISO 180not in the median: notch not stated
Hardness108 Rockwell Rp. 2: Rockwell Hardness ASTM D785 R-scalespecimen not stated, ASTM D785listed under other properties
HDT70 °Cp. 2: Heat Distortion Temperature ASTM D648 °CASTM D648not in the median: set apart (never used to pass), test bar not described as printed
HDT72 °Cp. 3: Heat Distortion Temperature ISO 75 °CISO 75not in the median: another value of this product is in it
Mould shrinkage orientation not stated0.2-0.5 %p. 2: Mold Shrinkage ASTM D955 %specimen not stated, ASTM D955

Print settings

Nozzle
230–260 °CBambu Lab Filament Guide
Bed
60–80 °CBambu Lab Filament Guide
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide

Price

Not in the price sample.

Its document

What the maker says (2)
Nanovia PETGStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa2.26Charpy notched, kJ/m²20HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C220–240Bed, °C80–90Chamber, °C20Drying, °C, h604 h

Nanovia PETGNanovia

Published values

PropertyAs publishedConditionsOn the Overview
Nanovia, Nanovia PETG : Functional prototypes : Nanovia4 values
Tensile modulus orientation not stated2260 MPap. 1: Young’s modulus
ISO 527As the sheet prints it: ISO 527-2/1A
print settingsTest performed at 1mm/min on 3D printed test specimins at 0°, along with the tension stress.
not in the median: set apart (never used to pass), no stated orientation
Charpy impact strength20 kJ/m2p. 1: Charpy (notched)no standard statedin the median
Glass transition temperature80 °Cp. 1: Tgno standard statedin the median
Density1.27 g/cm3p. 1: DensityISO 1183
Nanovia, PETG official material safety data sheet1 value
Density1,29 g/cm3p. 5: Densityno standard stated

Print settings

Nozzle
220–240 °Cown data sheet
Bed
80–90 °Cown data sheet
Heated chamber
20 °Cown data sheet
Drying
optional: 60 °C for 4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (5)
Chemicals and environment (2)
Spectrum PET-G FR V0Data sheet shared with Fiberlogy PET-G VOStrength XY, MPa25Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C63HDT 1.8, °C58Price, CAD/kg—Nozzle, °C230–255Bed, °C60–80Chamber, °CnoneDrying, °C, h604 h

Spectrum PET-G FR V0Spectrum

Data sheet shared with Fiberlogy PET-G VO: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, TECHNICAL DATA SHEET PET-G FR V010 valuesThe same values also in Spectrum, KARTA TECHNICZNA PET-G FR V0.Unless a row says otherwise: moulded bar (resin supplier's value)
Tensile modulus orientation not stated2350 MPap. 1: Elastic modulus***ISO 527not in the median: measured on a moulded bar
Tensile yield strength orientation not stated40 MPap. 1: Tensile Strength at Yield**ISO 527not in the median: measured on a moulded bar
Tensile break strength orientation not stated25 MPap. 1: Tensile Strength at Break**ISO 527not in the median: measured on a moulded bar
Elongation at break orientation not stated40,00 %p. 1: Tensile Elongation at Break**ISO 527not in the median: measured on a moulded bar
Elongation at yield orientation not stated3,30 %p. 1: Tensile Elongation at Yield**ISO 527listed under other properties
Charpy impact strength3 kJ/m2p. 1: Charpy impact strength, notched*
ISO 179As the sheet prints it: ISO 179-1eA
not in the median: measured on a moulded bar
HDT at 1.8 MPa58 °Cp. 1: HDT 1.81 MN/m2, annealedalso in Spectrum, KARTA TECHNICZNA PET-G FR V0specimen not stated,
ISO 75As the sheet prints it: 1.81 MN/m2 annealed ISO 75
annealed at a temperature its sheet does not state for a time its sheet does not stateannealed
in the median
Vicat softening temperature70 °Cp. 1: VICAT Softening point****ISO 306
Density1.26 g/cm3p. 1: Densityspecimen not stated, ISO 1183
Oxygen index35%p. 1: Oxygen index*
ASTM D2863As the sheet prints it: D 2863
Spectrum, KARTA TECHNICZNA PET-G FR V05 valuesUnless a row says otherwise: moulded bar (resin supplier's value)
Tensile modulus2350 MPap. 1: Moduł sprężystości***
ISO 527As the sheet prints it: ISO 527 (1); rate=1 mm/min
not in the median: measured on a moulded bar
Tensile yield strength40 MPap. 1: Wytrzymałość na rozciąganie na granicy plastyczności**
ISO 527As the sheet prints it: ISO 527 (1); rate=5mm/min
not in the median: measured on a moulded bar
Tensile break strength25 MPap. 1: Wytrzymałość na rozciąganie na granicy zerwania**
ISO 527As the sheet prints it: ISO 527 (1); rate=5mm/min
not in the median: measured on a moulded bar
Elongation at break40,00%p. 1: Wydłużenie przy rozciąganiu na granicy zerwania**
ISO 527As the sheet prints it: ISO 527 (1); rate=5mm/min
not in the median: measured on a moulded bar
Elongation at yield3,30%p. 1: Wydłużenie przy rozciąganiu na granicy plastyczności**
ISO 527As the sheet prints it: ISO 527 (1); rate=5mm/min
listed under other properties
Spectrum, 3D Printing Filament Manufacturer PRODUCT PORTFOLIO1 valueThe same values also in Spectrum, TECHNICAL DATA SHEET PET-G FR V0 and Spectrum, KARTA TECHNICZNA PET-G FR V0.
HDT at 0.45 MPa63°Cp. 4: HDT Balso in Spectrum, TECHNICAL DATA SHEET PET-G FR V0also in Spectrum, KARTA TECHNICZNA PET-G FR V0
no standard namedAs the sheet prints it: method=B
in the median

Print settings

Nozzle
230–255 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60 °C for 4 hFiberlogy PET-G VO's data sheet, shared
Hardened nozzle
not neededown data sheet
Annealing
temperature not statedown data sheet
Its 4 print profiles, in the documents' words

Price

Not in the price sample.

Its 6 documents

What the maker says (31)
Spectrum PET-G MATTModified: cosmetic dense fillerStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²3.5HDT 0.45, °C80HDT 1.8, °C70Price, CAD/kg54Nozzle, °C230–255Bed, °C60–80Chamber, °CnoneDrying, °C, h604 h

Spectrum PET-G MATTSpectrum

Modified: cosmetic dense filler. Its values are kept out of the material's medians.

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, TECHNICAL DATA SHEET PET-G MATT10 valuesThe same values also in Spectrum, 3D Printing Filament Manufacturer PRODUCT PORTFOLIO.
Tensile modulus orientation not stated3150 MPap. 1: Elastic modulus**ISO 527not in the median: measured on a moulded bar
Tensile yield strength orientation not stated45 MPap. 1: Tensile Strength at Yield*ISO 527not in the median: measured on a moulded bar
Tensile break strength orientation not stated30 MPap. 1: Tensile Strength at Break*ISO 527not in the median: measured on a moulded bar
Elongation at break orientation not stated40,00 %p. 1: Tensile Elongation at Break*ISO 527not in the median: measured on a moulded bar
Elongation at yield orientation not stated3.1 %p. 1: Tensile Elongation at Yield*ISO 527listed under other properties
Charpy impact strength85 kJ/m2p. 1: Charpy impact strength, unnotched
ISO 179As the sheet prints it: ISO 179-1eU
not in the median: unnotched
Charpy impact strength3.5 kJ/m2p. 1: Charpy impact strength, notched
ISO 179As the sheet prints it: ISO 179-1eA
not in the median: added filler or additive
HDT at 1.8 MPa70 °Cp. 1: Heat Deflection Temperature • high rigidity of items 1.81 MN/m2, annealed
ISO 75As the sheet prints it: 1.81 MN/m2 annealed ISO 75
annealed at a temperature its sheet does not state for a time its sheet does not stateannealed
not in the median: added filler or additive
Vicat softening temperature85 °Cp. 1: VICAT Softening point***also in Spectrum, 3D Printing Filament Manufacturer PRODUCT PORTFOLIOISO 306
annealed at a temperature its sheet does not state for a time its sheet does not stateannealed
Density1.35 g/cm3p. 1: DensityISO 1183
Spectrum, Spectrum Filaments Product Portfolio 2025 — Prografen pp28–291 valueThe same values also in Spectrum, TECHNICAL DATA SHEET PET-G MATT.
HDT at 0.45 MPa80°C80°C)also in Spectrum, TECHNICAL DATA SHEET PET-G MATT
no standard namedAs the sheet prints it: method=B
not in the median: added filler or additive

Print settings

Nozzle
230–255 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
optional: 60 °C for 4 hown data sheet
Hardened nozzle
not neededown data sheet
Annealing
temperature not statedown data sheet
Its 4 print profiles, in the documents' words

Price

54 CAD/kgits one regular price in the sample

1 listing
  • 3D Printing Canada: 54 CAD/kgLion Orange - Spectrum PET-G MATT Filament - 1.75mm, 1kg (SKU 67bbc22116fcf)in its price; seen 30 Sep 2026

Its 5 documents

What the maker says (10)
Chemicals and environment (1)
FormFutura EasyFil ePETGStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa2.98Charpy notched, kJ/m²4.7IzodHDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–260Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

FormFutura EasyFil ePETGFormFutura

Published values

PropertyAs publishedConditionsOn the Overview
FormFutura, Technical Data Sheet EasyFil ePETG8 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated2980 Mpap. 1: Tensile ModulusASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated25 MPaphysically implausiblep. 1: Tensile Stress at YieldASTM D638not in the median: physically implausible as published
Elongation at yield orientation not stated4,30 %p. 1: Elongation at YieldASTM D638listed under other properties
Izod impact strength4.7 kJ/m2p. 1: Notched Izod Impactno standard statednot in the median: set apart (never used to pass), test bar not described as printed
Hardness111 Rockwell Rp. 1: Rockwell Hardness, R ScaleASTM D785listed under other properties
Glass transition temperature80 °Cp. 1: Glass Transition TemperatureASTM D3418in the median
Vicat softening temperature78 °Cp. 1: Vicat Softening Temperatureno standard stated
Density1.29 g/cm3p. 1: Specific GravityASTM D792

Print settings

Nozzle
230–260 °CBambu Lab Filament Guide
Bed
60–80 °CBambu Lab Filament Guide
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide

Price

Not in the price sample.

Its document

What the maker says (9)
MatterHackers RYNOStrength XY, MPa55.2Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C71HDT 1.8, °C—Price, CAD/kg—Nozzle, °C235–255Bed, °C65Chamber, °CnoneDrying, °C, h658 h

MatterHackers RYNOMatterHackers

Published values

PropertyAs publishedConditionsOn the Overview
MatterHackers, TECHNICAL DATA SHEET - RYNO4 valuesUnless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated8010 PSIp. 1: Tensile Strength at YieldASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated10 %p. 1: Tensile ElongationASTM D638not in the median: set apart (never used to pass), test bar not described as printed
HDT at 0.45 MPa71 °Cp. 1: Heat Deflection Temperature
ASTM D648As the sheet prints it: 66 PSI ASTM D648
in the median
Glass transition temperature80 °Cp. 1: Glass Transition TemperatureASTM D3418in the median

Print settings

Nozzle
235–255 °Cown data sheet
Bed
65 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
Spectrum rPETGStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–255Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

Spectrum rPETGSpectrum

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, TECHNICAL DATA SHEET rPETG10 valuesThe same values also in Spectrum, 3D Printing Filament Manufacturer PRODUCT PORTFOLIO.
Tensile yield strength orientation not stated52 MPap. 1: Tensile Strength at Yield
ASTM D882As the sheet prints it: D882
not in the median: measured on film
Tensile break strength orientation not stated59 MPap. 1: Tensile Strength at Break
ASTM D882As the sheet prints it: D882
not in the median: measured on film
Elongation at break orientation not stated400 %p. 1: Elongation at Break
ASTM D882As the sheet prints it: D882
not in the median: measured on film
Elongation at yield orientation not stated4 %p. 1: Elongation at Yield
ASTM D882As the sheet prints it: D882
listed under other properties
Flexural modulus orientation not stated2000 Mpap. 1: Flexural ModulusISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated68 MPap. 1: Flexural StrengthISO 178not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength101 J/mp. 1: Izod Impact Strength Notched @ 23°C
ASTM D256As the sheet prints it: 23°C D256
tested at 23°C		not in the median: in J/m
HDT at 0.45 MPa70 °Cp. 1: Heat Deflection Temperaturealso in Spectrum, 3D Printing Filament Manufacturer PRODUCT PORTFOLIO
ASTM D648As the sheet prints it: D648
in the median
Density1.23 g/cm3p. 1: Specific Gravity
ASTM D1505As the sheet prints it: D1505
Water absorption0.2 %p. 1: Moisture Absorption
ASTM D792As the sheet prints it: D792

Print settings

Nozzle
230–255 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededown data sheet
Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (7)
Fiberlogy PET-G VOData sheet shared with Spectrum PET-G FR V0Strength XY, MPa25Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C63HDT 1.8, °C58Price, CAD/kg—Nozzle, °C220–250Bed, °C90Chamber, °CnoneDrying, °C, h604 h

Fiberlogy PET-G VOFiberlogy

Data sheet shared with Spectrum PET-G FR V0: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy PET-G VO5 values
Tensile break strength orientation not stated25 MPap. 1: Tensile Strength @ Break ISO 527 MPaISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated3.3 %p. 1: Elongation @ Yield ISO 527 %ISO 527listed under other properties
HDT at 0.45 MPa63 °Cp. 1: Heat Distortion Temperature @ 0.45 MPa ISO 75 °C
ISO 75As the sheet prints it: 0.45 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa58 °Cp. 1: Heat Distortion Temperature @ 1.8 MPa ISO 75 °C
ISO 75As the sheet prints it: 1.8 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
Vicat softening temperature70 °Cp. 1: Vicat Softening Temperature ISO 306 °CISO 306

Print settings

Nozzle
220–250 °Cown data sheet
Bed
90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60 °C for 4 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Annealing
temperature not statedSpectrum PET-G FR V0's data sheet, shared
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (1)
Nobufil PETGStrength XY, MPa48Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²3IzodHDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C225–245Bed, °C65–85Chamber, °CnoneDrying, °C, h603–6 h

Nobufil PETGNobufil

Published values

PropertyAs publishedConditionsOn the Overview
Nobufil, Technical Datasheet PETG12 valuesUnless a row says otherwise:
print settingsFDM H column (the sheet does not say what H is)
Tensile strength (yield or break not stated) orientation not stated48 MPap. 1: Tensile strength, FDM HISO 527not in the median: set apart (never used to pass), no stated orientation
Tensile strength (yield or break not stated) orientation not stated50 MPap. 1: Tensile strength, InjectionISO 527not in the median: measured on a moulded bar
Elongation at break orientation not stated8 %p. 1: Elongation at break, FDM HISO 527not in the median: set apart (never used to pass), no stated orientation
Elongation at break orientation not stated4,5 %p. 1: Elongation at break, InjectionISO 527not in the median: measured on a moulded bar
Flexural modulus orientation not stated2150 MPap. 1: Flexural modulusISO 178print settings not statednot in the median: measured on a moulded bar
Flexural strength orientation not stated44 MPap. 1: Flexural strengthISO 178print settings not statednot in the median: measured on a moulded bar
Izod impact strength orientation not stated3 kJ/m²p. 1: Izod Impact strength notched, FDM HISO 180not in the median: set apart (never used to pass), no stated orientation
Izod impact strength orientation not stated3,5 kJ/m²p. 1: Izod Impact strength notched, InjectionISO 180not in the median: measured on a moulded bar
Izod impact strength orientation not stated22 kJ/m²p. 1: Izod Impact strength unnotched, FDM HISO 180not in the median: unnotched
Izod impact strength orientation not stated134 kJ/m²p. 1: Izod Impact strength unnotched, InjectionISO 180not in the median: measured on a moulded bar
HDT at 1.8 MPa61 °Cp. 1: HDT A
ISO 75As the sheet prints it: HDT A ISO 75
print settings not stated		not in the median: measured on a moulded bar
Density1,27 g/cm³p. 1: DensityISO 1183print settings not stated

Print settings

Nozzle
225–245 °Cown data sheet
Bed
65–85 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
60 °C for 3–6 hown data sheet
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words
  • Nozzle 235°C ± 10; Bed 75°C ± 10; Drying Pre-dry material for 3-6 hours at 60°C (max.).Nobufil, Technical Datasheet PETGp. 1: Recommended printing settings; p. 1: Drying note

Price

Not in the price sample.

Its 3 documents

What the maker says (6)
  • Adhesion between layersOur PETG 3D Filament delivers high-quality prints with excellent layer adhesion and robustness.Nobufil, PETG filamentp. 1
  • BenefitsNobufil PETG filament is a sustainable top-quality 3D printing material made from recycled industrial plastic waste.Nobufil, PETG filamentp. 1
  • BenefitsThe material also boasts high temperature resistance and strength properties that are comparable to ABS - at the same time it is just as easy to print as PLA.Nobufil, PETG filamentp. 1
  • Odour and emissionsBesides, it is almost odorless and has minimal delay between printing layers.Nobufil, PETG filamentp. 1
  • BenefitsIt is compatible with most common 3D printers and is easy to process.Nobufil, PETG filamentp. 1
  • Good forOverall, PETG filament is an excellent choice for environmentally-conscious 3D printing enthusiasts who value quality and convenience.Nobufil, PETG filamentp. 1
Spectrum THE FILAMENT PETGStrength XY, MPa46.9Strength Z, MPa—Modulus XY, GPa1.87Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–255Bed, °C60–75Chamber, °CnoneDrying, °C, h658 h

Spectrum THE FILAMENT PETGSpectrum

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, TECHNICAL DATA SHEET THE FILAMENT PETG8 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated1874 MPap. 1: Tensile Modulus
ASTM D638As the sheet prints it: D 638
not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated25 MPaphysically implausiblep. 1: Tensile Stress at Yield
ASTM D638As the sheet prints it: D 638
not in the median: physically implausible as published
Tensile break strength orientation not stated46.9 MPap. 1: Tensile Stress at Break
ASTM D638As the sheet prints it: D 638
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4.4 %p. 1: Elongation at Yield
ASTM D638As the sheet prints it: D 638
listed under other properties
Izod impact strength120 J/mp. 1: Izod Impact Strength, Notched @ 23°C
ASTM D256As the sheet prints it: 23°C D 256
tested at 23°C		not in the median: in J/m
Izod impact strength55.5 J/mp. 1: Izod Impact Strength, Notched @ -40°C
ASTM D256As the sheet prints it: -40°C D 256
tested at -40°C		not in the median: in J/m
HDT70 °Cp. 1: Heat Deflection Temperature
ASTM D648As the sheet prints it: D 648
not in the median: set apart (never used to pass), no stated test load
Density1.27 g/cm3p. 1: Specific Gravity
ASTM D792As the sheet prints it: D 792

Print settings

Nozzle
230–255 °Cown data sheet
Bed
60–75 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededown data sheet
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (4)
Spectrum THE FILAMENT PETG LiteData sheet shared with The Filament PETG LiteStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C77HDT 1.8, °C—Price, CAD/kg—Nozzle, °C235–255Bed, °C60Chamber, °CnoneDrying, °C, h658 h

Spectrum THE FILAMENT PETG LiteSpectrum

Data sheet shared with The Filament PETG Lite: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, TECHNICAL DATA SHEET THE FILAMENT PETG Lite5 valuesUnless a row says otherwise: specimen not stated
Tensile strength (yield or break not stated) orientation not stated49.8 MPap. 1: Tensile StrengthFilm specimen (ASTM D882); not a printed or moulded bar,
ASTM D882As the sheet prints it: D 882
not in the median: measured on film
Elongation at break orientation not stated160 %p. 1: Elongation at BreakASTM D638not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated66.8 MPap. 1: Flexural Strength
ASTM D790As the sheet prints it: D 790
not in the median: set apart (never used to pass), test bar not described as printed
HDT77 °Cp. 1: Heat Deflection Temperature
ASTM D648As the sheet prints it: D 648
not in the median: set apart (never used to pass), no stated test load
Density1.29 g/cm3p. 1: Specific Gravity
ASTM D792As the sheet prints it: D 792

Print settings

Nozzle
235–255 °Cown data sheet
Bed
60 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededown data sheet
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (3)
The Filament PETG LiteData sheet shared with Spectrum THE FILAMENT PETG LiteStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C77HDT 1.8, °C—Price, CAD/kg—Nozzle, °C235–255Bed, °C60Chamber, °CnoneDrying, °C, h658 h

The Filament PETG LiteThe Filament

Data sheet shared with Spectrum THE FILAMENT PETG Lite: their values are one table, recorded once.

Published values

No value is on file for this product.

Print settings

Nozzle
235–255 °Cown data sheet
Bed
60 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededown data sheet
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (3)
3DJake easyPETGStrength XY, MPa53Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–250Bed, °C60–90Chamber, °CnoneDrying, °C, h658 h

3DJake easyPETG3DJake

Published values

PropertyAs publishedConditionsOn the Overview
3DJake, Technical Data Sheet 3DJAKE easyPETG6 valuesUnless a row says otherwise: specimen not stated
Tensile strength (yield or break not stated) orientation not stated53 MPap. 1: Tensile strength
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated31 %p. 1: Elongation at break
ISO 527As the sheet prints it: ISO 527-2
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4 %p. 1: Elongation at yield
ISO 527As the sheet prints it: ISO 527-2
listed under other properties
Flexural modulus orientation not stated2190 MPap. 1: Flexural E-ModulusISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated71 MPap. 1: Flexural StrengthISO 178not in the median: set apart (never used to pass), test bar not described as printed
Vicat softening temperature78 °Cp. 1: VICAT A (VST)ISO 306

Print settings

Nozzle
230–250 °Cown data sheet
Bed
60–90 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (10)
MatterHackers PETGStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C65HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230–250Bed, °C65Chamber, °CnoneDrying, °C, h658 h

MatterHackers PETGMatterHackers

Published values

PropertyAs publishedConditionsOn the Overview
MatterHackers, TECHNICAL DATA SHEET - PRO Series PETG4 valuesUnless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated10800 PSIphysically implausiblep. 1: Tensile Strength at YieldASTM D638not in the median: physically implausible as published
Elongation at break orientation not stated5 %p. 1: Tensile ElongationASTM D638not in the median: set apart (never used to pass), test bar not described as printed
HDT at 0.45 MPa65 °Cp. 1: Heat Deflection Temperature
ASTM D648As the sheet prints it: ASTM D648 at 66 PS
in the median
Glass transition temperature80 °Cp. 1: Glass Transition TemperatureASTM D3418in the median

Print settings

Nozzle
230–250 °Cown data sheet
Bed
65 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (1)
MatterHackers MH Build Series PETGStrength XY, MPa49Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C235–255Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

MatterHackers MH Build Series PETGMatterHackers

Published values

PropertyAs publishedConditionsOn the Overview
MatterHackers, TECHNICAL DATA SHEET - MH Build Series PETG5 valuesThe same values also in MatterHackers, TECHNICAL DATA SHEET - Build Series PETG.Unless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated49 MPap. 1: Tensile Strength at Yieldalso in MatterHackers, TECHNICAL DATA SHEET - Build Series PETGISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated280 %p. 1: Tensile Elongation at Breakalso in MatterHackers, TECHNICAL DATA SHEET - Build Series PETGISO 527not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated60 MPaphysically implausiblep. 1: Flexural Modulusalso in MatterHackers, TECHNICAL DATA SHEET - Build Series PETGISO 178not in the median: physically implausible as published
Flexural strength orientation not stated1170 MPaphysically implausiblep. 2: Flexural Strengthalso in MatterHackers, TECHNICAL DATA SHEET - Build Series PETGISO 178not in the median: physically implausible as published
Density1.23 g/cm³p. 1: DensityISO 1183
MatterHackers, MatterHackers Black MH Build Series PETG Filament - 2.85mm (1kg)1 value
Density1.27 (g/cm³)p. 1: Densityno standard stated

Print settings

Nozzle
235–255 °Cown data sheet
Bed
60–80 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): bed in MatterHackers, MatterHackers Black MH Build Series PETG Filament - 2.85mm (1kg).

Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (14)
UltiMaker MakerBot PETGStrength XY, MPa44Strength Z, MPa—Modulus XY, GPa1.9Charpy notched, kJ/m²—HDT 0.45, °C70HDT 1.8, °C—Price, CAD/kg—Nozzle, °C230Bed, °C60–80Chamber, °CnoneDrying, °C, h658 h

UltiMaker MakerBot PETGUltiMaker

Published values

PropertyAs publishedConditionsOn the Overview
UltiMaker, Method material: PETG3 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated1,900 MPap. 1: Tensile modulusno standard statednot in the median: set apart (never used to pass), test bar not described as printed
Tensile strength (yield or break not stated) orientation not stated44 MPap. 1: Tensile strengthno standard statednot in the median: set apart (never used to pass), test bar not described as printed
HDT70 °Cp. 1: PETG ... heat deflection temperature (FAQ)no standard statednot in the median: set apart (never used to pass), no stated test load

Print settings

Nozzle
230 °Cown data sheet
Bed
60–80 °CBambu Lab Filament Guide
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (8)
eSUN PETG HSStrength XY, MPa—Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C220–260Bed, °C75–90Chamber, °CnoneDrying, °C, h658 h

eSUN PETG HSeSUN

Published values

PropertyAs publishedConditionsOn the Overview
eSUN, ePETG+HS Technical Data Sheet7 valuesUnless a row says otherwise: moulded bar (resin supplier's value)
Tensile strength (yield or break not stated) orientation not stated29.2 MPap. 1: Tensile Strength GB/T 1040GB/T 1040not in the median: measured on a moulded bar
Elongation at break orientation not stated4.2 %p. 1: Elongation at Break GB/T 1040GB/T 1040not in the median: measured on a moulded bar
Flexural modulus orientation not stated1708.7 MPap. 1: Flexural Modulus GB/T 9341GB/T 9341not in the median: measured on a moulded bar
Flexural strength orientation not stated63 MPap. 1: Flexural Strength GB/T 9341GB/T 9341not in the median: measured on a moulded bar
Izod impact strength5.6 kJ/m²p. 1: IZOD Impact StrengthGB/T 1843not in the median: measured on a moulded bar
HDT68 ℃p. 1: Heat distortion Temperature GB/T 1634GB/T 1634not in the median: measured on a moulded bar
Density1.26 g/cm3p. 1: Density GB/T 1033specimen not stated, GB/T 1033

Print settings

Nozzle
220–260 °Cown data sheet
Bed
75–90 °Cown data sheet
Heated chamber
not requiredBambu Lab Filament Guide
Drying
65 °C for 8 hBambu Lab Filament Guide
Hardened nozzle
not neededBambu Lab Filament Guide
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (5)

Values are for the colour each sheet tested; pigment can change them.