PVB

6 products from 5 makers. Most documented first. Select a column to sort, a product to see its values, print settings and documents.

Key

set apart: test bar not described as printed, or no stated load
Izod where no Charpy is published
not published

How the numbers are worked out

Polymaker PolycastStrength XY, MPa53.2Strength Z, MPa26.3Modulus XY, GPa2.21Charpy notched, kJ/m²2.9HDT 0.45, °C67HDT 1.8, °C53Price, CAD/kg85Nozzle, °C190–220Bed, °C25–70Chamber, °CnoneDrying, °C, h5012 h

Polymaker PolycastPolymaker

Published values

Property	As published	Conditions	On the Overview
Polymaker, TECHNICAL DATA SHEET Polymaker™ Polycast16 valuesThe same values also in Polymaker, Techanical Data Sheet PolyCast™.
Tensile modulus XY	2215 ± 42 MPap. 1: Young’s modulus (X-Y)	ISO 527, GB/T 1040 print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	in the median
Tensile modulus Z	2111 ± 87 MPap. 1: Young’s modulus (Z)	no standard stated print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	in the median
Tensile strength (yield or break not stated) XY	53.2 ± 1.1 MPap. 1: Tensile strength (X-Y)	no standard stated print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	in the median
Tensile strength (yield or break not stated) Z	26.3 ± 2.1 MPap. 1: Tensile strength (Z)	no standard stated print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	in the median
Elongation at break XY	5.7 ± 0.5 %p. 1: Elongation at break (X-Y)	ISO 527, GB/T 1040 print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	in the median
Elongation at break Z	1.3 ± 0.1 %p. 1: Elongation at break (Z)	no standard stated print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	in the median
Flexural modulus XY	2233 ± 106 MPap. 1: Bending modulus (X-Y)	ISO 178, GB/T 9341 print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	in the median
Charpy impact strength XY	2.9 ± 0.3 kJ/m2p. 1: Notched Charpy impact strength (X-Y) ISO 179, GB/T 1043	ISO 179, GB/T 1043 print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	in the median
Charpy impact strength Z	2.9 ± 0.3 kJ/m2p. 1: Notched Charpy impact strength (Z) ISO 179, GB/T 1043	ISO 179, GB/T 1043 print settings Printing temperature 220°C; Infill 100%; Bed temperature 60°C; Shell 2; Top & bottom layer 3; Cooling fan ON; Environmental Temperature Ambient	not in the median: measured on a bar in another orientation
HDT at 0.45 MPa	67 °Cp. 1: Heat deflection temp. ISO 75, 0.45MPa	ISO 75 As the sheet prints it: 0.45MPa ISO 75	in the median
HDT at 1.8 MPa	53 °Cp. 1: Heat deflection temp. ISO 75, 1.8MPa	ISO 75 As the sheet prints it: 1.8MPa ISO 75	in the median
Glass transition temperature	70 °Cp. 1: Glass transition temp. DSC, 10°C/minalso in Polymaker, Techanical Data Sheet PolyCast™	DSC	in the median
Vicat softening temperature	67 °Cp. 1: Vicat softening temp. ISO 306, GB/T 1633also in Polymaker, Techanical Data Sheet PolyCast™	ISO 306, GB/T 1633
Density	1.1 g/cm3p. 1: Density ISO1183, GB/T1033also in Polymaker, Techanical Data Sheet PolyCast™	ISO 1183, GB/T 1033
Water absorption	2.09 %p. 1: Equilibrium water absorption (%)=also in Polymaker, Techanical Data Sheet PolyCast™	no standard stated
Melt mass-flow rate	6.6-6.7 g/10minp. 1: Melt index 210°C, 2.16kgalso in Polymaker, Techanical Data Sheet PolyCast™	no standard named As the sheet prints it: 210°C 2.16kg tested at 210°C

Polymaker, Techanical Data Sheet PolyCast™9 valuesUnless a row says otherwise: printed specimen print settings Printing temperature 220 °C; Bed temperature 60 °C; Shell 2; Top & bottom layer 4; Infill 100%; Environmental temperature 25 °C; Cooling fan ON
Tensile modulus XY	1745 ± 151 MPap. 4: Young’s modulus (X-Y)	ISO 527, GB/T 1040	not in the median: another value of this product is in it
Tensile strength (yield or break not stated) XY	35.7 ± 1.7 MPap. 4: Tensile strength (X-Y)	ISO 527, GB/T 1040	not in the median: another value of this product is in it
Elongation at break XY	5.8 ± 0.9 %p. 4: Elongation at break (X-Y)	ISO 527, GB/T 1040	not in the median: another value of this product is in it
Flexural modulus XY	1198 ± 173 MPap. 4: Bending modulus (X-Y)	ISO 178, GB/T 9341	not in the median: another value of this product is in it
Flexural strength XY	60.2 ± 1.2 MPap. 4: Bending strength (X-Y)	ISO 178, GB/T 9341	in the median
Charpy impact strength XY	9.6 ± 0.9 kJ/m2p. 4: Charpy impact strength (X-Y)	ISO 179, GB/T 1043notched	not in the median: another value of this product is in it
HDT at 0.45 MPa	66.5 °Cp. 3: Heat deflection temperature ISO 75 0.45MPa	printed specimen (implied by the document), ISO 75 As the sheet prints it: 0.45MPa ISO 75 print settings not stated	not in the median: another value of this product is in it
HDT at 1.8 MPa	52.7 °Cp. 3: Heat deflection temperature ISO 75 1.8MPa	printed specimen (implied by the document), ISO 75 As the sheet prints it: 1.8MPa ISO 75 print settings not stated	not in the median: another value of this product is in it
Decomposition temperature	260 °Cp. 3: Decomposition temperature TGA, 20°C/min	specimen not stated, TGAprint settings not stated

Print settings

Nozzle: 190–220 °Cown data sheet
Bed: 25–70 °Cown data sheet
Heated chamber: not requiredown data sheet
Drying: 50 °C for 12 hown data sheet
Hardened nozzle: not stated

Its 2 print profiles, in the documents' words

Nozzle 190-220°C; Bed 25-70°C; Drying 50°C/12HPolymaker, TECHNICAL DATA SHEET Polymaker™ Polycastp. 1: Recommended printing settings: Nozzle temperature; p. 1: Drying temp. and time; p. 1: Closure chamber
Nozzle 190 – 220 (℃); Bed 25 - 70 (°C); Chamber Room temperaturePolymaker, Techanical Data Sheet PolyCast™p. 4: Recommended printing settings: Nozzle temperature; p. 4: Environmental temperature

Price

85.3 CAD/kgits one regular price in the sample

1 listing

Voxel Factory: 85.3 CAD/kgPolymaker PolyCast 1.75mm 0.75kg (SKU PMK-PCT-NAT-175-750)in its price; seen 30 Sep 2026

Its 4 documents

What the maker says (9)

Good forPolyCast™ is a filament engineered specifically for producing investment patterns used in investment casting applications, streamlining the traditional casting workflow.Polymaker, PolyCast™ (PVB) | Polymaker Wikip. 1
Good forChoose PolyCast™ for rapid, accurate, and efficient production of investment casting patterns - perfect for foundries, jewelry making, and custom manufacturing projects.Polymaker, PolyCast™ (PVB) | Polymaker Wikip. 1
Surface finishPolyCast™ can be easily smoothed with IPA for a smoother surface finish which is reflected on the casted model.Polymaker, PolyCast™ (PVB) | Polymaker Wikip. 1
Printing adviceIncrease printing temperature to 220˚C if printing at this fast 15mm^3/s.Polymaker, PolyCast™ (PVB) | Polymaker Wikip. 1
Printing adviceKeep fan speed on at full blast for best surface quality.Polymaker, PolyCast™ (PVB) | Polymaker Wikip. 1
Printing adviceThe burnout temperature for our PolyCast is 1,100 - 1,200˚C to entirely burnout.Polymaker, PolyCast™ (PVB) | Polymaker Wikip. 1
Good forPolyCast™ is a filament designed to produce investment patterns for investment casting applications.Polymaker, Techanical Data Sheet PolyCast™p. 2
Moisture sensitivityIt is highly recommended to use the PolyBox™ when printing with PolyCast™ and to store it in the resealable bag.Polymaker, Techanical Data Sheet PolyCast™p. 4
Supports and removalRecommended support material PolyDissolve™ S1Polymaker, Techanical Data Sheet PolyCast™p. 4

Polymaker PolySmoothStrength XY, MPa51.8Strength Z, MPa38.9Modulus XY, GPa2.2Charpy notched, kJ/m²3.1HDT 0.45, °C68HDT 1.8, °C66Price, CAD/kg71Nozzle, °C190–220Bed, °C25–70Chamber, °CnoneDrying, °C, h5012 h

Polymaker PolySmoothPolymaker

Published values

Property	As published	Conditions	On the Overview
Polymaker, PolySmooth Technical Data Sheet16 valuesUnless a row says otherwise: printed specimen
Tensile modulus XY	2199 ± 43 MPap. 4: Young's modulus (X-Y)	ISO 527, GB/T 1040 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
Tensile modulus Z	2010 ± 69 MPap. 4: Young's modulus (Z)	ISO 527, GB/T 1040 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
Tensile strength (yield or break not stated) XY	51.8 ± 0.7 MPap. 4: Tensile strength (X-Y)	ISO 527, GB/T 1040 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
Tensile strength (yield or break not stated) Z	38.9 ± 0.8 MPap. 4: Tensile strength (Z)	ISO 527, GB/T 1040 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
Elongation at break XY	14.5 ± 2.9 %p. 4: Elongation at break (X-Y)	ISO 527, GB/T 1040 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
Elongation at break Z	2.8 ± 0.3 %p. 4: Elongation at break (Z)	ISO 527, GB/T 1040 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
Flexural modulus XY	2198 ± 57 MPap. 4: Bending modulus (X-Y)	ISO 178, GB/T 9341 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
Flexural strength XY	75.9 ± 0.8 MPap. 4: Bending strength (X-Y)	ISO 178, GB/T 9341 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
Charpy impact strength XY	3.1 ± 0.8 kJ/m²p. 4: Notched Charpy impact strength (X-Y)	ISO 179, GB/T 1043 print settings Printed at 220 °C nozzle, 60 °C bed, 100% infill, 2 shells, 3 top and bottom layers, ambient environment, cooling fan on (p. 5: How to make specimens)	in the median
HDT at 0.45 MPa	68 °Cp. 3: Heat deflection temperature (0.45 MPa)	ISO 75 As the sheet prints it: ISO 75, 0.45 MPa	in the median
HDT at 1.8 MPa	66 °Cp. 3: Heat deflection temperature (1.8 MPa)	ISO 75 As the sheet prints it: ISO 75, 1.8 MPa	in the median
Glass transition temperature	70 °Cp. 3: Glass transition temperature	specimen not stated, DSC As the sheet prints it: DSC, 10 °C/min	in the median
Vicat softening temperature	70 °Cp. 3: Vicat softening temperature	ISO 306, GB/T 1633
Density	1.10 g/cm³ at 23 °Cp. 2: Density	specimen not stated, ISO 1183, GB/T 1033tested at 23 °C
Water absorption	2.36 %p. 2: Moisture absorption curve	specimen not stated, no standard named As the sheet prints it: Equilibrium water absorption (moisture absorption curve)
Melt mass-flow rate	6.7 g/10minp. 2: Melt index	specimen not stated, no standard named As the sheet prints it: 210 °C, 2.16 kg tested at 210 °C

Print settings

Nozzle: 190–220 °Cown data sheet
Bed: 25–70 °Cown data sheet
Heated chamber: not requiredown data sheet
Drying: 50 °C for 12 hown data sheet
Hardened nozzle: not stated

Its print profile, in the documents' words

Nozzle 190 – 220 (℃); Bed 25 - 70 (˚C); Drying 50˚C for 12hPolymaker, PolySmooth Technical Data Sheetp. 4: Build plate temperature, Drying setting, Nozzle temperature; p. 4: Closure chamber

Price

71.3 CAD/kgthe median of its 2 regular prices in the sample

2 listings

MakerWiz: 80 CAD/kgPolymaker PolySmooth™ Filament - 1.75 mm, 0.75 kg (11 Colours) / Jet Black / 1.75 mm (SKU 61000103)in its price; seen 30 Sep 2026
Voxel Factory: 62.6 CAD/kgPolymaker PolySmooth 1.75mm 0.75kg / Jet black (SKU PMK-PSM-BLK-175-750)in its price; seen 30 Sep 2026

Its 2 documents

What the maker says (4)

Surface finishPolySmooth™ is a unique, easy-to-print filament designed for hands-free post processing.Polymaker, PolySmooth Technical Data Sheetp. 2
Surface finishThe surface can be smoothed with alcohol to achieve layer free models using the Polysher™.Polymaker, PolySmooth Technical Data Sheetp. 2
Moisture sensitivityIt is highly recommended to use the PolyBox™ when printing with PolySmooth™ and to store it in the resealable bag.Polymaker, PolySmooth Technical Data Sheetp. 4
Supports and removalRecommended support material PolyDissolve™ S1Polymaker, PolySmooth Technical Data Sheetp. 4

Prusa Research PVB PrusamentStrength XY, MPa50Strength Z, MPa—Modulus XY, GPa1.7Charpy notched, kJ/m²7HDT 0.45, °C63HDT 1.8, °C58Price, CAD/kg120Nozzle, °C205–225Bed, °C70–80Chamber, °CnoneDrying, °C, h604–8 h

Prusa Research PVB PrusamentPrusa Research

Published values

Property	As published	Conditions	On the Overview
Prusa Research, PVB Prusament23 valuesUnless a row says otherwise: print settings Prusa i3 MK3S; PrusaSlicer 2.2.0; 0.20 mm FAST; top/bottom 0; 2 perimeters; 100% rectilinear; 200 mm/s; nozzle215°C, bed75°C; extrusion multiplier1.05; print cooling off. Filament dried60°C for8h before printing.
Tensile modulus XY	1.7 ± 0.1 GPap. 2: Tensile modulus	ISO 527 As the sheet prints it: ISO 527-1	in the median
Tensile modulus XZ	1.7 ± 0.1 GPap. 2: Tensile modulus	ISO 527 As the sheet prints it: ISO 527-1	not in the median: measured on a bar in another orientation
Tensile yield strength XY	50 ± 5 MPap. 2: Tensile yield strength	ISO 527 As the sheet prints it: ISO 527-1	in the median
Tensile yield strength orientation not stated	57 ± 1 MPap. 2: Tensile yield strength	ISO 527print settings not stated	not in the median: measured on a filament strand
Tensile yield strength XZ	49 ± 5 MPap. 2: Tensile yield strength	ISO 527 As the sheet prints it: ISO 527-1	not in the median: measured on a bar in another orientation
Elongation at yield XY	4.6 ± 0.7 %p. 2: Elongation at yield	ISO 527 As the sheet prints it: ISO 527-1	listed under other properties
Elongation at yield XZ	4.4 ± 0.7 %p. 2: Elongation at yield	ISO 527 As the sheet prints it: ISO 527-1	listed under other properties
Flexural modulus XY	2.2 ± 0.1 GPap. 2: Flexural modulus	ISO 178	in the median
Flexural modulus XZ	2.3 ± 0.1 GPap. 2: Flexural modulus	ISO 178	not in the median: measured on a bar in another orientation
Flexural strength XY	72 ± 1 MPap. 2: Flexural strength	ISO 178	in the median
Flexural strength XZ	73 ± 3 MPap. 2: Flexural strength	ISO 178	not in the median: measured on a bar in another orientation
Charpy impact strength XY	55 ± 7 kJ/m²p. 2: Charpy strength unnotched	ISO 179 As the sheet prints it: ISO 179-1; unnotched; edgewise	not in the median: unnotched
Charpy impact strength XY	7 ± 1 kJ/m²p. 2: Charpy strength notched	ISO 179 As the sheet prints it: ISO 179-1; notched; edgewise	in the median
Charpy impact strength XZ	59 ± 12 kJ/m²p. 2: Charpy strength unnotched	ISO 179 As the sheet prints it: ISO 179-1; unnotched; edgewise	not in the median: unnotched
Charpy impact strength XZ	10 ± 1 kJ/m²p. 2: Charpy strength notched	ISO 179 As the sheet prints it: ISO 179-1; notched; edgewise	not in the median: measured on a bar in another orientation
Hardness	77 Shore Dp. 2: Hardness	no standard named As the sheet prints it: Prusa Polymers print settings not stated	in the median
Interlayer adhesion strength orientation not stated	9 ± 1 MPap. 2: Interlayer adhesion strength	no standard named As the sheet prints it: Prusa Polymers print settings not stated
HDT orientation not stated, at 0.45 MPa	63 °Cp. 2: HDT	ISO 75 As the sheet prints it: ISO 75; 0.45 MPa print settings not stated	not in the median: set apart (never used to pass), test bar not described as printed
HDT orientation not stated, at 1.8 MPa	58 °Cp. 2: HDT	ISO 75 As the sheet prints it: ISO 75; 1.80 MPa print settings not stated	not in the median: set apart (never used to pass), test bar not described as printed
Density orientation not stated	1.10 g/cm³p. 2: Density	no standard named As the sheet prints it: Prusa Polymers print settings not stated
Water absorption orientation not stated	0.18 %p. 2: Water absorption	no standard named As the sheet prints it: Prusa Polymers
Water absorption orientation not stated	0.35 %p. 2: Water absorption	no standard named As the sheet prints it: Prusa Polymers
Melt mass-flow rate	6–7 g/10 minp. 2: MFR [g/10 min]	ISO 1133 As the sheet prints it: ISO 1133; 230 °C, 2.16 kg print settings not stated

Print settings

Nozzle: 205–225 °Cown data sheet
Bed: 70–80 °Cown data sheet
Heated chamber: not requiredown data sheet
Drying: optional: 60 °C for 4–8 hown data sheet
Hardened nozzle: not stated

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): drying in Prusa Research, Prusament PVB.

Its 2 print profiles, in the documents' words

Nozzle 215 ±10°C; Bed 75 ±5°C; Drying Maximum60°C for4-8h depending on moisturePrusa Research, PVB PrusamentRecommended printing settings
Bed 65–85 °C Heated Bed required; Drying let it dry for 4 hours at 60 °C before printingPrusa Research, Prusament PVBp. 1: Bed Temperature; p. 1: Enclosure; p. 1: Print Surface; p. 1: Possibility of using 0.8mm nozzle; p. 1: Keep the filament dry

Price

120 CAD/kgits one regular price in the sample

1 listing

MakerWiz: 120 CAD/kgPrusa Research Prusament PVB Light Yellow Transparent 500g (SKU 37004014)in its price; seen 30 Sep 2026

Its 3 documents

What the maker says (1)

Adhesion between layersPoor layer to layer adhesion (slightly worse than PLA)Prusa Research, Prusament PVBp. 1

SUNLU PVBStrength XY, MPa48Strength Z, MPa—Modulus XY, GPa—Charpy notched, kJ/m²6.5IzodHDT 0.45, °C56HDT 1.8, °C—Price, CAD/kg—Nozzle, °C200–230Bed, °C50–60Chamber, °CnoneDrying, °C, h50

SUNLU PVBSUNLU

Published values

Property	As published	Conditions	On the Overview
SUNLU, TECHNICAL DATA SHEET ISO PVB12 valuesThe same values also in SUNLU, PVB.Unless a row says otherwise: printed specimen
Tensile strength (yield or break not stated) XY	48 ± 5 MPap. 1: (X-Y) Tensile Strength ISO 527/2 50 mm/min MPa	ISO 527 As the sheet prints it: 50 mm/min ISO 527/2 print settings Printing speed 45mm/s; Printing temperature 240 °C; Infill: 100%; 90° raster orientation	in the median
Elongation at break XY	14 ± 3 %p. 1: (X-Y) Elongation at break ISO 527/2 50 mm/min %	ISO 527 As the sheet prints it: 50 mm/min ISO 527/2 print settings Printing speed 45mm/s; Printing temperature 240 °C; Infill: 100%; 90° raster orientation	in the median
Flexural modulus XY	2250 ± 200 MPap. 1: (X-Y) Flexural Modulus ISO 178 2 mm/min MPa	ISO 178 As the sheet prints it: 2 mm/min ISO 178 print settings Printing speed 45mm/s; Printing temperature 240 °C; Infill: 100%; 90° raster orientation	in the median
Flexural strength XY	78 ± 6 MPap. 1: (X-Y) Flexural Strength ISO 178 2 mm/min MPa	ISO 178 As the sheet prints it: 2 mm/min ISO 178 print settings Printing speed 45mm/s; Printing temperature 240 °C; Infill: 100%; 90° raster orientation	in the median
Izod impact strength XY	6.5 ± 2 KJ/m2p. 1: (X-Y) Izod Impact Strength of Notched ISO 180 23℃ KJ/m2 Specimen	ISO 180 As the sheet prints it: 23℃ KJ/m2 Specimen ISO 180 tested at 23°C print settings Printing speed 45mm/s; Printing temperature 240 °C; Infill: 100%; 90° raster orientation	in the median
Izod impact strength ZX	6 ± 2 KJ/m2p. 1: (Z-X) Izod Impact Strength of Unnotched ISO 180 23℃ KJ/m2 Specimen	ISO 180 As the sheet prints it: 23℃ KJ/m2 Specimen ISO 180 tested at 23°C print settings Printing speed 45mm/s; Printing temperature 240 °C; Infill: 100%; 90° raster orientation	not in the median: unnotched
Hardness	82.5 Shore (scale not specified by source)p. 1: Shore Hardness ISO 868 23℃ HA/HD	ISO 868 As the sheet prints it: 23℃ HA/HD ISO 868 tested at 23°C	listed under other properties
HDT XY, at 0.45 MPa	55.8 ± 3 ℃p. 1: (X-Y) Heat Distortion (HDT) ISO 75 0.45 MPa ℃	ISO 75 As the sheet prints it: 0.45 MPa ISO 75	in the median
Glass transition temperature	70 ℃p. 1: Glass Transition (Tg) ISO 11357-2 10 ℃/min ℃also in SUNLU, PVB	ISO 11357 As the sheet prints it: ISO 11357-2	in the median
Vicat softening temperature	60 ℃p. 1: Vicat Softening Temp. ISO 306 5kg, 50℃/h ℃also in SUNLU, PVB	ISO 306 As the sheet prints it: 5kg ISO 306
Density	1.08 g/cm3p. 1: Density ISO 1183 23℃ g/cm3also in SUNLU, PVB	specimen not stated, ISO 1183 As the sheet prints it: 23℃ ISO 1183 tested at 23°C
Melt mass-flow rate	14.3 ± 2 g/10 minp. 1: Melt Mass-flow Rate ISO 1133 210℃/2.16 kg g/10 min	ISO 1133 As the sheet prints it: 210℃/2.16 kg ISO 1133 tested at 210°C

SUNLU, PVB9 values
Tensile strength (yield or break not stated) XY	56 MPap. 1: Tensile Strength(X-Y) ISO527/2 50mm/min MPa	ISO 527 As the sheet prints it: 50mm/min ISO527/2	not in the median: another value of this product is in it
Elongation at break XY	25 %p. 1: Elongation at break(X-Y) ISO527/2 50mm/min %	ISO 527 As the sheet prints it: 50mm/min ISO527/2	not in the median: another value of this product is in it
Flexural modulus XY	2164 MPap. 1: Flexural Modulus(X-Y) ISO178 2mm/min MPa	ISO 178 As the sheet prints it: 2mm/min ISO178	not in the median: another value of this product is in it
Flexural strength XY	66 MPap. 1: Flexural Strength(X-Y) ISO178 2mm/min MPa	ISO 178 As the sheet prints it: 2mm/min ISO178	not in the median: another value of this product is in it
Izod impact strength XY	3.7 KJ/m2p. 1: IZOD Impact Notched(X-Y) ISO180 23℃ KJ/m2	ISO 180 As the sheet prints it: 23℃ ISO180 tested at 23°C	not in the median: another value of this product is in it
HDT at 0.45 MPa	54.5 ℃p. 1: Heat Deflection (HDT) ISO75 0.45MPa ℃	ISO 75 As the sheet prints it: 0.45MPa ISO75	not in the median: another value of this product is in it
Decomposition temperature	230 ℃p. 1: @5%Decomposition Temp. ISO11358 20℃/min ℃	ISO 11358
Melt mass-flow rate	15.6 g/10minp. 1: Melt Flow Rate ISO1133 190℃/2.16kg g/10min	ISO 1133 As the sheet prints it: 190℃/2.16kg ISO1133 tested at 190°C
Mould shrinkage orientation not stated	0.5-1.0 %p. 1: Mold Shrinkage ISO294 23℃ %	ISO 294 As the sheet prints it: 23℃ ISO294 tested at 23°C

Print settings

Nozzle: 200–230 °Cown data sheet
Bed: 50–60 °Cown data sheet
Heated chamber: not requiredown data sheet
Drying: 50 °Cown data sheet
Hardened nozzle: not stated

Its 2 print profiles, in the documents' words

Nozzle 200-210; 210-230; Bed 50-60℃; Chamber Room Temperature; Drying 50℃SUNLU, TECHNICAL DATA SHEET ISO PVBp. 2: Recommended printing settings; p. 2: Nozzle Temp.
Nozzle 200-210; 210-230; Bed 50-60℃; Chamber Room temperature; Drying 50℃SUNLU, PVBp. 2: Recommended printing settings; p. 2: Nozzle Print Temp.; p. 2: Print Platform Material

Price

Not in the price sample.

Its 3 documents

What the maker says (5)

Surface finishPolishable materialSUNLU, TECHNICAL DATA SHEET ISO PVBp. 1
Supports and removalSupported Material PVASUNLU, TECHNICAL DATA SHEET ISO PVBp. 2
Good forOrnaments, toys, ornaments, handcraftsSUNLU, PVBp. 1
Surface finishMaterial that can be polishedSUNLU, PVBp. 1
Supports and removalSupport Material PVASUNLU, PVBp. 2

Fiberlogy FiberSmoothStrength XY, MPa51Strength Z, MPa—Modulus XY, GPa3.05Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C55Price, CAD/kg—Nozzle, °C215–225Bed, °C75Chamber, °CnoneDrying, °C, h404 h

Fiberlogy FiberSmoothFiberlogy

Published values

Property	As published	Conditions	On the Overview
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy FiberSmooth12 valuesThe same values also in Fiberlogy, FiberSmooth PVB Filament - Fiberlogy.
Tensile modulus orientation not stated	3050 MPap. 1: Tensile Modulus ISO 527 MPa	ISO 527	not in the median: set apart (never used to pass), test bar not described as printed
Tensile break strength orientation not stated	51 MPap. 1: Tensile Strength @ Break ISO 527 MPa	ISO 527	not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated	88 %p. 1: Elongation @ Break @ 10 mm/min ISO 527 %	ISO 527 As the sheet prints it: Break 10 mm/min ISO 527	not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated	2350 MPap. 1: Flexural Modulus ISO 178 MPa	ISO 178	not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated	77 MPap. 1: Flexural Strength ISO 178 MPa	ISO 178	not in the median: set apart (never used to pass), test bar not described as printed
Charpy impact strength orientation not stated	110 kJ/m²p. 1: Charpy Impact Strength (not notched) @ 23°Calso in Fiberlogy, FiberSmooth PVB Filament - Fiberlogy	ISO 180 As the sheet prints it: ISO 180; unnotched tested at 23 °Cunnotched	not in the median: unnotched
HDT at 1.8 MPa	55 °Cp. 1: Heat Distortion Temperature @ 1.8 MPa ISO 75 °C	ISO 75 As the sheet prints it: 1.8 MPa ISO 75	not in the median: set apart (never used to pass), test bar not described as printed
Glass transition temperature	70 °Cp. 1: Glass Transition Temperature Tg ISO 11357-2 °C	ISO 11357 As the sheet prints it: ISO 11357-2	in the median
Vicat softening temperature	70 °Cp. 1: Vicat Softening Temperature ISO 306 °C	ISO 306
Melting temperature	175 °Cp. 1: Melting Temperature Tm DSC °C	DSC
Density	1.1 g/cm3p. 1: Specific Density ISO 1183 g/cm3	ISO 1183
Water absorption	4-6 %p. 1: Water Absorption (24 hr, 20°C, 0.100 mm ) - %	no standard named As the sheet prints it: 24 hr 20°C 0.100 mm - tested at 20°C

Print settings

Nozzle: 215–225 °Cown data sheet
Bed: 75 °Cown data sheet
Heated chamber: not requiredown data sheet
Drying: 40 °C for 4 hown data sheet
Hardened nozzle: not stated

Its 2 print profiles, in the documents' words

Nozzle 215°C - 225°C; Bed 75°CFiberlogy, TECHNICAL DATA SHEET Fiberlogy FiberSmoothp. 1: Recommended printing settings
Nozzle 215–225°C; Bed 75°C; Drying 40°C / 4 hoursFiberlogy, FiberSmooth PVB Filament - Fiberlogyp. 1: Printing temperature; p. 1: Bed temperature; p. 1: Bed material; p. 1: Drying conditions; p. 1: Enclosed chamber

Price

Not in the price sample.

Its 3 documents

What the maker says (6)

Good forIt’s ideal for beginners and decorative projects.Fiberlogy, FiberSmooth PVB Filament - Fiberlogyp. 1
Warping and shrinkageLow shrinkage reduces the risk of deformation and delamination from the table.Fiberlogy, FiberSmooth PVB Filament - Fiberlogyp. 1
Precision and toleranceLow shrinkage ensures precise dimensions and better detail reproduction.Fiberlogy, FiberSmooth PVB Filament - Fiberlogyp. 1
Surface finishFiberlogy FiberSmooth is a PVB-based 3D printing filament that produces smooth, porcelain-glossy prints thanks to its easy post-processing with isopropyl alcohol (IPA).Fiberlogy, FiberSmooth PVB Filament - Fiberlogyp. 1
Surface finishThe filament is as easy to print as PLA, hides layer lines, and provides an attractive, elegant finish.Fiberlogy, FiberSmooth PVB Filament - Fiberlogyp. 1
Surface finishThe ability to smooth using isopropyl alcohol (IPA) Wiping or soaking the model in IPA results in a smooth, glossy surface.Fiberlogy, FiberSmooth PVB Filament - Fiberlogyp. 1

Yousu PVBStrength XY, MPa40Strength Z, MPa—Modulus XY, GPa2.31Charpy notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C190–220Bed, °C25–70Chamber, °C—Drying, °C, h—

Yousu PVBYousu

Published values

Property	As published	Conditions	On the Overview
Yousu, Yousu PVB 3D FILMAENT Technical Data Sheet8 values
Tensile modulus orientation not stated	2310 MPap. 1: Tensile Modulus ASTM D638 MPa	ASTM D638	in the median
Tensile break strength orientation not stated	40 MPatranscription correctedp. 1: Tensile Strength MPa	no standard statedtested at 23 ℃	in the median
Tensile break strength orientation not stated	40 MPap. 1: Tensile Strength	ASTM D638 As the sheet prints it: ASTM D638; break tested at 23 ℃	not in the median: another value of this product is in it
Elongation at break orientation not stated	4 %p. 1: Tensile Elongation	ASTM D638 As the sheet prints it: ASTM D638; break	in the median
Flexural strength orientation not stated	70 MPap. 1: Flexural Strength MPa	no standard stated	in the median
Density	1.10 g/cm3p. 1: Density ASTM D792 g/cm3 23 ℃	ASTM D792 As the sheet prints it: 23 ℃ ASTM D792 tested at 23°C
Water absorption	0.15 %p. 1: Water Absorption ASTM D570 % 23 ℃,24hr	ASTM D570 As the sheet prints it: 23 ℃ 24hr ASTM D570 tested at 23°C
Melt mass-flow rate	6.7 g/10minp. 1: Melt Flow Rate g/10min 210 ℃, 2.16Kg	no standard named As the sheet prints it: 210 ℃ 2.16Kg tested at 210°C

Print settings

Nozzle: 190–220 °Cown data sheet
Bed: 25–70 °Cown data sheet
Heated chamber: not stated
Drying: not stated
Hardened nozzle: not stated

Its print profile, in the documents' words

Nozzle 190-220℃; Bed 25-70℃Yousu, Yousu PVB 3D FILMAENT Technical Data Sheetp. 2: Recommended printing settings; p. 2: Bed Temp

Price

Not in the price sample.

Its 2 documents

What the maker says (1)

Surface finishThe surface can be polished with alcohol to achieve layer free models.Yousu, Yousu PVB 3D FILMAENT Technical Data Sheetp. 1

Values are for the colour each sheet tested; pigment can change them.