Filament Atlas
Open in the selectorSelector

PCTG

8 products from 8 makers. Most documented first. Select a column to sort, a product to see its values, print settings and documents.

Key

How the numbers are worked out

3D-Fuel Pro PCTGData sheet shared with Spectrum pctg, FormFutura AthenaX and 3DJake PCTGStrength XY, MPa53Modulus XY, GPa—Izod notched, kJ/m²93HDT 0.45, °C74HDT 1.8, °C64Price, CAD/kg—Nozzle, °C250–270Bed, °C60–100Chamber, °CnoneDrying, °C, h7524 h

3D-Fuel Pro PCTG3D-Fuel

Data sheet shared with Spectrum pctg, FormFutura AthenaX and 3DJake PCTG: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
3D-Fuel, TECHNICAL DATA SHEET 3D-Fuel Pro PCTG21 valuesUnless a row says otherwise: printed specimen
Tensile yield strength orientation not stated460 Kgf/cm2p. 2: Tensile Strength @ Yield ASTM D638 Kgf/cm2ASTM D638not in the median: another value of this product is in it
Tensile yield strength orientation not stated44 MPap. 3: Tensile Strength @ Yield ISO 527 MPaISO 527not in the median: another value of this product is in it
Tensile break strength orientation not stated540 Kgf/cm2p. 2: Tensile Strength @ Break ASTM D638 Kgf/cm2ASTM D638in the median
Tensile break strength orientation not stated46 MPap. 3: Tensile Strength @ Break ISO 527 MPaISO 527not in the median: another value of this product is in it
Elongation at break orientation not stated340 %p. 2: Elongation @ Break ASTM D638 %ASTM D638in the median
Elongation at break orientation not stated220 %p. 3: Elongation @ Break ISO 527 %ISO 527not in the median: another value of this product is in it
Elongation at yield orientation not stated5.0 %p. 2: Elongation @ Yield ASTM D638 %specimen not stated, ASTM D638listed under other properties
Elongation at yield orientation not stated4.4 %p. 3: Elongation @ Yield ISO 527 %specimen not stated, ISO 527listed under other properties
Flexural modulus orientation not stated18,300 Kgf/cm2p. 2: Flexural Modulus ASTM D790 Kgf/cm2ASTM D790in the median
Flexural modulus orientation not stated1,600 MPap. 3: Flexural Modulus ISO 178 MPaISO 178not in the median: another value of this product is in it
Flexural strength orientation not stated680 Kgf/cm2p. 2: Flexural Strength ASTM D790 Kgf/cm2ASTM D790in the median
Flexural strength orientation not stated60 MPAp. 3: Flexural Strength ISO 178 MPAISO 178not in the median: another value of this product is in it
Izod impact strength860 J/mp. 2: Izod Impact Strength ASTM D256 J/mASTM D256tested at 23 °Cnotchednot in the median: in J/m
Izod impact strength93 KJ/m2p. 3: Izod Impact Strength ISO 180 KJ/m2ISO 180tested at 23 °Cnotchedin the median
Hardness76 Shore Dp. 2: Shore Hardness ASTM D2240 Shore Dspecimen not stated, ASTM D2240in the median
Hardness105 Rockwell Rp. 2: Rockwell Hardness ASTM D785 R-scalespecimen not stated, ASTM D785listed under other properties
HDT at 0.45 MPa74 °Cp. 2: Heat Distortion Temperature ASTM D648 °C
ASTM D648As the sheet prints it: ASTM D648 @0.455 MPa
in the median
HDT at 0.45 MPa76 °Cp. 3: Heat Distortion Temperature ISO 75 °C
ISO 75As the sheet prints it: ISO 75 @0.455 MPa
not in the median: another value of this product is in it
HDT at 1.8 MPa64 °Cp. 2: Heat Distortion Temperature ASTM D648 °C, second value (@ 1.82 MPa)
ASTM D648As the sheet prints it: ASTM D648 @ 1.82 MPa
in the median
HDT at 1.8 MPa64 °Cp. 3: Heat Distortion Temperature ISO 75 °C, second value (@ 1.82 MPa)
ISO 75As the sheet prints it: ISO 75 @ 1.82 MPa
not in the median: another value of this product is in it
Glass transition temperature84 °Cp. 2: Glass Transition Temperature (Tg)specimen not stated, no standard statedin the median

Print settings

Nozzle
250–270 °CSpectrum pctg's data sheet, shared
Bed
60–100 °CSpectrum pctg's data sheet, shared
Heated chamber
not requiredown data sheet
Drying
75 °C for 24 hFormFutura AthenaX's data sheet, shared
Hardened nozzle
not stated
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (3)
3DJake PCTGData sheet shared with Spectrum pctg, 3D-Fuel Pro PCTG and FormFutura AthenaXStrength XY, MPa46Modulus XY, GPa—Izod notched, kJ/m²93HDT 0.45, °C74HDT 1.8, °C64Price, CAD/kg—Nozzle, °C250–270Bed, °C90–110Chamber, °CnoneDrying, °C, h7524 h

3DJake PCTG3DJake

Data sheet shared with Spectrum pctg, 3D-Fuel Pro PCTG and FormFutura AthenaX: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
3DJake, Technical Data Sheet 3DJAKE PCTG7 valuesUnless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated44 MPap. 1: Tensile strength at yieldISO 527not in the median: another value of this product is in it
Tensile break strength orientation not stated46 MPap. 1: Tensile strength at breakISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated220 %p. 1: Elongation at breakISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4,4 %p. 1: Elongation at yieldISO 527listed under other properties
Flexural modulus orientation not stated1600 MPap. 1: Flexural ModulusISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated60 MPap. 1: Flexural StrengthISO 178not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa64 °Cp. 1: Heat Distortion Temp 76 /
ISO 75As the sheet prints it: ISO 75 @1,820 MPa
in the median

Print settings

Nozzle
250–270 °Cown data sheet
Bed
90–110 °Cown data sheet
Heated chamber
not required3D-Fuel Pro PCTG's data sheet, shared
Drying
75 °C for 24 hFormFutura AthenaX's data sheet, shared
Hardened nozzle
not stated
Its 2 print profiles, in the documents' words

Price

Not in the price sample.

Its 3 documents

What the maker says (8)
FormFutura AthenaXData sheet shared with Spectrum pctg, 3D-Fuel Pro PCTG and 3DJake PCTGStrength XY, MPa46Modulus XY, GPa—Izod notched, kJ/m²93HDT 0.45, °C76HDT 1.8, °C64Price, CAD/kg—Nozzle, °C250–270Bed, °C60–100Chamber, °CnoneDrying, °C, h7524 h

FormFutura AthenaXFormFutura

Data sheet shared with Spectrum pctg, 3D-Fuel Pro PCTG and 3DJake PCTG: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
FormFutura, TECHNICAL DATA SHEET AthenaX11 valuesUnless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated44 MPap. 1: Tensile strength at yieldISO 527not in the median: another value of this product is in it
Tensile break strength orientation not stated46 MPap. 1: Tensile strength at breakISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated220 %p. 1: Elongation at BreakISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4.4 %p. 1: Elongation at yieldISO 527listed under other properties
Flexural modulus orientation not stated1600 Mpap. 1: Flexural Modulus (15mm/min)
ISO 178As the sheet prints it: 15mm/min ISO 178
not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated60 Mpap. 1: Flexural Strength (15mm/min)
ISO 178As the sheet prints it: 15mm/min ISO 178
not in the median: set apart (never used to pass), test bar not described as printed
Hardness105 Rockwell Rp. 1: Rockwell Hardness (R-scale)ASTM D785listed under other properties
HDT at 0.45 MPa76 °Cp. 1: HDT (@0.455MPa)
ISO 75As the sheet prints it: 0.455MPa ISO 75
in the median
HDT at 1.8 MPa64 °Cp. 1: HDT (@ 1.820 Mpa)
ISO 75As the sheet prints it: 1.820 Mpa ISO 75
in the median
Vicat softening temperature88 °Cp. 1: Vicat softening temperatureno standard stated
Density1.23 g/cm3p. 1: Specific GravityASTM D792

Print settings

Nozzle
250–270 °CSpectrum pctg's data sheet, shared
Bed
60–100 °CSpectrum pctg's data sheet, shared
Heated chamber
not required3D-Fuel Pro PCTG's data sheet, shared
Drying
75 °C for 24 hown data sheet
Hardened nozzle
not stated
Its print profile, in the documents' words

Price

Not in the price sample.

Its 2 documents

What the maker says (13)
Spectrum pctgData sheet shared with 3D-Fuel Pro PCTG, FormFutura AthenaX and 3DJake PCTGStrength XY, MPa46Modulus XY, GPa—Izod notched, kJ/m²93HDT 0.45, °C76HDT 1.8, °C64Price, CAD/kg48Nozzle, °C250–270Bed, °C60–100Chamber, °CnoneDrying, °C, h7524 h

Spectrum pctgSpectrum

Data sheet shared with 3D-Fuel Pro PCTG, FormFutura AthenaX and 3DJake PCTG: their values are one table, recorded once.

Published values

PropertyAs publishedConditionsOn the Overview
Spectrum, pctg12 valuesUnless a row says otherwise: specimen not stated
Tensile yield strength orientation not stated44 MPap. 1: Tensile Strength at YieldISO 527not in the median: another value of this product is in it
Tensile break strength orientation not stated46 Mpap. 1: Tensile Strength at BreakISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated220%p. 1: Elongation at BreakISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4.4 %p. 1: Elongation at YieldISO 527listed under other properties
Flexural modulus orientation not stated1600 Mpap. 1: Flexural ModulusISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated60 Mpap. 1: Flexural StrengthISO 178not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength orientation not statedheld back: the sheet's unit or table layout is unclearheld backp. 1: Izod Impact Strength Notched @ 23°CISO 180not in the median: held back
Hardness105 R-scale Rockwell Rp. 1: Rockwell HardnessASTM D785listed under other properties
HDT at 0.45 MPa76°Cp. 1: Heat Distortion Temperature @ 0.455MPa
ISO 75As the sheet prints it: ISO 75, 0.455 MPa
in the median
HDT at 1.8 MPa64°Cp. 1: Heat Distortion Temperature @ 1.820 MPa
ISO 75As the sheet prints it: ISO 75, 1.820 MPa
in the median
Vicat softening temperature88°Cp. 1: VICAT Softening TemperatureDSC
Density1.23 g/cm3p. 1: Specific GravityASTM D792

Print settings

Nozzle
250–270 °Cown data sheet
Bed
60–100 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
75 °C for 24 hFormFutura AthenaX's data sheet, shared
Hardened nozzle
not neededown data sheet
Its print profile, in the documents' words
  • Nozzle 250-270°C; Bed 60-100°CSpectrum, pctgRecommended printing settings; p. 1: Nozzle note; p. 1: settings footnote

Price

48 CAD/kgits one regular price in the sample

2 listings: 1 in its price, 1 with no regular price per kilogram recorded
  • 3D Printing Canada: 48 CAD/kgClear - Spectrum Premium PCTG Filament - 1.75mm, 1kg / Default Titlein its price; seen 10 Sep 2026
  • 3D Printing Canada: 35 per kg, sale pricePure Orange - Spectrum Premium PCTG Filament - 1.75mm, 1kg / Default Titlenot used: no regular price per kilogram recorded; seen 10 Sep 2026

Its 2 documents

What the maker says (10)
  • BenefitsBelonging to the same material family of copolyesters, PCTG filament offers similar ease of printing as PET-G.Spectrum, pctgp. 1
  • Benefitshigher transparency than standard PET-G (applies to transparent colours)Spectrum, pctgp. 1
  • Benefitsease of printing, processing and finishingSpectrum, pctgp. 1
  • Warping and shrinkageA very important advantage of the Premium PCTG filament is its increased impact strength, high dimensional stability and low shrinkage.Spectrum, pctgp. 1
  • Precision and tolerancehigh dimensional accuracy of the printed elementsSpectrum, pctgp. 1
  • Surface finishexcellent print surfaceSpectrum, pctgp. 1
  • Moisture sensitivityDry box not necessarySpectrum, pctgp. 1
  • Moisture sensitivityhydrophobicSpectrum, pctgp. 1
  • Nozzle wearRuby or hardened nozzle not necessarySpectrum, pctgp. 1
  • Odour and emissionsodourlessSpectrum, pctgp. 1
Fiberlogy PCTGStrength XY, MPa45Modulus XY, GPa2Izod notched, kJ/m²92HDT 0.45, °C76HDT 1.8, °C64Price, CAD/kg—Nozzle, °C250–270Bed, °C90–110Chamber, °CnoneDrying, °C, h604 h

Fiberlogy PCTGFiberlogy

Published values

PropertyAs publishedConditionsOn the Overview
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy PCTG9 valuesUnless a row says otherwise: specimen not stated; its document points to a moulded or resin bar
Tensile yield strength orientation not stated43 MPap. 1: Tensile Strength @ Yield ISO 527 MPaISO 527not in the median: another value of this product is in it
Tensile break strength orientation not stated45 MPap. 1: Tensile Strength @ Break ISO 527 MPaISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated220 %p. 1: Elongation @ Break ISO 527 %ISO 527not in the median: set apart (never used to pass), test bar not described as printed
Elongation at yield orientation not stated4 %p. 1: Elongation @ Yield ISO 527 %specimen not stated, ISO 527listed under other properties
Flexural modulus orientation not stated1600 MPap. 1: Flexular Modulus ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated60 MPap. 1: Flexular Strength ISO 178 MPaISO 178not in the median: set apart (never used to pass), test bar not described as printed
Izod impact strength92 kJ/m2p. 1: Izod Impact Strength (Notched) @ 23°C ISO 180 kJ/m2
ISO 180As the sheet prints it: 23°C ISO 180
tested at 23°C		not in the median: set apart (never used to pass), test bar not described as printed
HDT at 0.45 MPa76 °Cp. 1: Heat Distortion Temperature @ 0.45 MPa ISO 75 °C
ISO 75As the sheet prints it: 0.45 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
HDT at 1.8 MPa64 °Cp. 1: Heat Distortion Temperature @ 1.8 MPa ISO 75 °C
ISO 75As the sheet prints it: 1.8 MPa ISO 75
not in the median: set apart (never used to pass), test bar not described as printed
Fiberlogy, TECHNICAL DATA SHEET Fiberlogy PCTG4 valuesUnless a row says otherwise: specimen not stated
Tensile modulus orientation not stated2000 MPap. 1: Tensile Modulus ISO 527 MPaspecimen not stated; its document points to a moulded or resin bar, ISO 527not in the median: set apart (never used to pass), test bar not described as printed
Glass transition temperature88 °Cp. 1: Glass Transition Temperature Tg DSC °Cno standard statedin the median
Vicat softening temperature81 °Cp. 1: Vicat Softening Temperature ISO 306 °CISO 306
Continuous service temperature50 °Cp. 1: Continuous Use Temperature (UL Yellow Card) UL 746 °C
no standard namedAs the sheet prints it: UL 746
Fiberlogy, PCTG Filament2 values
Izod impact strength orientation not stated92 kJ/m² (ISO 180)p. 1: Izod impact strength (notched) @ 23°C
ISO 180As the sheet prints it: ISO 180; notched
tested at 23 °C		not in the median: another value of this product is in it
Density1.23 g/cm³p. 1: Densityno standard stated

Print settings

Nozzle
250–270 °Cown data sheet
Bed
90–110 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
60 °C for 4 hown data sheet
Hardened nozzle
not stated

Differs in another document of this product, not used in deciding (a data sheet speaks before a product page, a newer edition before an older one): bed in Fiberlogy, PCTG Filament.

Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (2)
  • BenefitsPCTG prints are significantly more resistant to impacts and mechanical stress.Fiberlogy, PCTG Filamentp. 1
  • Pitfalls and limitationsFiberlogy PCTG is BPA-free , fully recyclable , and, in its Pure TR version, approved for food contact* , which further expands its range of applications.Fiberlogy, PCTG Filamentp. 1: exact product paragraph, source text line 50
3DXTECH MAXG PCTGStrength XY, MPa45Modulus XY, GPa1.75Izod notched, kJ/m²8HDT 0.45, °C76HDT 1.8, °C—Price, CAD/kg—Nozzle, °C250–270Bed, °C70–90Chamber, °CnoneDrying, °C, h654 h

3DXTECH MAXG PCTG3DXTECH

Published values

PropertyAs publishedConditionsOn the Overview
3DXTECH, Technical Data Sheet: MAX-G™ PCTG 3D Printing Filament9 valuesUnless a row says otherwise: printed specimen
print settingsPrinted Specimen Conditions Printer: Open Source FDM/FFF Nozzle: 0.4mm Layer Height: 0.25mm Infill: 100%, +/- 45° Extrusion Temp: 275°C Bed Temp: 90°C Specimen Orientation: XY Flat
Tensile modulus XY1755 MPap. 1: Tensile ModulusISO 527in the median
Tensile break strength XY45 MPap. 1: Tensile Strength, BreakISO 527in the median
Elongation at break XY24 %p. 1: Tensile Elongation, BreakISO 527in the median
Flexural modulus XY1600 MPap. 1: Flexural ModulusISO 178in the median
Flexural strength XY72 MPap. 1: Flexural StrengthISO 178in the median
Izod impact strength XY8 kJ/m2transcription correctedp. 1: Izod Impact Stregth
ISO 180As the sheet prints it: ISO 180/A
notched		in the median
HDT at 0.45 MPa76 °Cp. 1: Deflection Temperature at 0.45
ISO 75As the sheet prints it: ISO 75, 0.45 MPa (66 psi)
in the median
Glass transition temperature78 °Cp. 1: Glass Transition Temperature (Tg)DSCin the median
Density1.23 g/ccp. 1: DensityISO 1183

Print settings

Nozzle
250–270 °Cown data sheet
Bed
70–90 °Cown data sheet
Heated chamber
not requiredown data sheet
Drying
65 °C for 4 hown data sheet
Hardened nozzle
not neededown data sheet
Its 3 print profiles, in the documents' words

Price

Not in the price sample.

Its 4 documents

What the maker says (1)
Extrudr PCTGSold as toughened (the maker's statement)Strength XY, MPa46Modulus XY, GPa1.7Izod notched, kJ/m²—HDT 0.45, °C—HDT 1.8, °C64Price, CAD/kg—Nozzle, °C230–270Bed, °C90–110Chamber, °C—Drying, °C, h606 h

Extrudr PCTGExtrudr

Sold as toughened or impact-modified: "engineered for parts that need to survive real impact" (Extrudr, PCTG official maker product page, p. 1). The maker's statement, not a test result.

Published values

PropertyAs publishedConditionsOn the Overview
Extrudr, PCTG official maker product page13 values
Tensile modulus orientation not stated1700 MPap. 1: Tensile modulus (Young's modulus)
ISO 527As the sheet prints it: ISO 527-1
not in the median: set apart (never used to pass), test bar not described as printed
Tensile yield strength orientation not stated44 MPap. 1: Tensile strength at yield
ISO 527As the sheet prints it: ISO 527-1
not in the median: another value of this product is in it
Tensile break strength orientation not stated46 MPap. 1: Tensile stress at break
ISO 527As the sheet prints it: ISO 527-1
not in the median: set apart (never used to pass), test bar not described as printed
Elongation at break orientation not stated220 %p. 1: Elongation at break
ISO 527As the sheet prints it: ISO 527-1
not in the median: set apart (never used to pass), test bar not described as printed
Flexural modulus orientation not stated1600 MPap. 1: Flexural modulusISO 178not in the median: set apart (never used to pass), test bar not described as printed
Flexural strength orientation not stated60 MPap. 1: Flexural strengthISO 178not in the median: set apart (never used to pass), test bar not described as printed
Charpy impact strength orientation not stated50 kJ/m²p. 1: Charpy notched impact strength (-30°C)
ISO 179As the sheet prints it: ISO 179-1eA
tested at -30°C		not in the median: tested below room temperature
Impact strength, test unclear orientation not stated94 kJ/m²p. 1: a notched impact strength of 94 kJ/m²no standard statedWhich test: probably Charpylisted under other properties
HDT at 1.8 MPa64 °Cp. 1: Heat deflection temp. (HDT/A) — 1.8 MPa
ISO 75As the sheet prints it: ISO 75-1; 1.8 MPa
not in the median: set apart (never used to pass), test bar not described as printed
Glass transition temperature~85 °Cp. 1: Glass transition temp. (Tg)
ISO 11357As the sheet prints it: ISO 11357-1 (DSC)
in the median
Vicat softening temperature~84 °Cp. 1: Vicat softening temp. (VST/B50)ISO 306
Decomposition temperature370 °Cp. 1: Thermal decomposition temp.no standard stated
Water absorption~0.5 %p. 1: Water absorption (saturation, 23°C)
no standard namedAs the sheet prints it: state=saturation
tested at 23°C
Extrudr, TECHNICAL DATA SHEET PCTG11 valuesUnless a row says otherwise: moulded bar (resin supplier's value)
Tensile yield strength43 MPap. 1: Tensile strength at yield ISO 527 MPaISO 527not in the median: measured on a moulded bar
Tensile break strength45 MPap. 1: Tensile strength at break ISO 527 MPaISO 527not in the median: measured on a moulded bar
Elongation at break215 %p. 1: Elongation at break ISO 527 %ISO 527not in the median: measured on a moulded bar
Elongation at yield4,3 %p. 1: Elongation at yield ISO 527 %ISO 527listed under other properties
Flexural modulus1650 MPap. 1: Flexural modulus (E-Modulus) ISO 178 MPaISO 178not in the median: measured on a moulded bar
Flexural strength62 MPap. 1: Flexural strength ISO 178 MPaISO 178not in the median: measured on a moulded bar
Izod impact strength94 kj/m²p. 1: Notched impact strength ISO 180 kj/m²ISO 180tested at 23 °Cnot in the median: measured on a moulded bar
Hardness105 Rockwell Rp. 1: Rockwell Hardness ASTM D785 R-SkalaASTM D785listed under other properties
HDT at 0.45 MPa76 °Cp. 1: HDT/B ISO 75 °C
ISO 75As the sheet prints it: HDT B ISO 75
not in the median: measured on a moulded bar
Vicat softening temperature88 °Cp. 1: VICAT (VST) ASTM D1525 °CASTM D1525
Density1,23 g/cm3p. 1: Density ASTM D792 g/cm3ASTM D792
Extrudr, TECHNISCHES DATENBLATT PCTG2 values
Izod impact strength94 @ 23 °C kj/m²p. 1: KerbschlagzähigkeitISO 180tested at 23 °Cnot in the median: measured on a moulded bar
Mould shrinkage orientation not stated0,2-0,5 %p. 1: Schwindung ASTM D955 %ASTM D955

Print settings

Nozzle
230–270 °Cown data sheet
Bed
90–110 °Cown data sheet
Heated chamber
not stated
Drying
60 °C for 6 hown data sheet
Hardened nozzle
not neededown data sheet
Its 3 print profiles, in the documents' words
  • Nozzle 230-270°C; Bed 90-110°CExtrudr, TECHNICAL DATA SHEET PCTGp. 1: Recommended printing settings; p. 1: Hardened Nozzle; p. 1: Recommended settings for printers with a 0.4mm Nozzle
  • Nozzle 230–270 °C; Bed 90–110 °C; Drying Drying temperature 60 °C; Drying time 4–6 hExtrudr, PCTG official maker product pagep. 1: Exact product drying table and own nozzle recommendation; other recipe fields not transcribed in this scoped profile; p. 1: Nozzle temperature; p. 1: Build plate temperature; p. 1: Surface preparation; p. 1: Enclosed chamber required; p. 1: Hardened nozzle required; p. 1: Recommended settings for printers with a 0.4 mm nozzle
  • Nozzle 230-270°C; Bed 90-110°CExtrudr, TECHNISCHES DATENBLATT PCTGp. 1: Düse; p. 1: Heizbett; p. 1: Vorgeschlagene Einstellungen für Drucker mit 0.4 mm Düse

Price

Not in the price sample.

Its 4 documents

What the maker says (6)
Nobufil PCTGStrength XY, MPa50Modulus XY, GPa—Izod notched, kJ/m²4HDT 0.45, °C—HDT 1.8, °C—Price, CAD/kg—Nozzle, °C245–265Bed, °C75–95Chamber, °C—Drying, °C, h603–6 h

Nobufil PCTGNobufil

Published values

PropertyAs publishedConditionsOn the Overview
Nobufil, Technical Datasheet PCTG11 values
Tensile strength (yield or break not stated) orientation not stated50 MPap. 1: Tensile strength, FDM HISO 527
print settingsFDM H column (the sheet does not say what H is)
not in the median: set apart (never used to pass), no stated orientation
Tensile strength (yield or break not stated) orientation not stated48 MPap. 1: Tensile strength, InjectionISO 527
print settingsInjection column
not in the median: measured on a moulded bar
Elongation at break orientation not stated14 %p. 1: Elongation at break, FDM HISO 527
print settingsFDM H column (the sheet does not say what H is)
not in the median: set apart (never used to pass), no stated orientation
Elongation at break orientation not stated74 %p. 1: Elongation at break, InjectionISO 527
print settingsInjection column
not in the median: measured on a moulded bar
Flexural modulus orientation not stated1700 MPap. 1: Flexural modulusISO 178not in the median: measured on a moulded bar
Flexural strength orientation not stated58 MPap. 1: Flexural strengthISO 178not in the median: measured on a moulded bar
Izod impact strength orientation not stated4 kJ/m²p. 1: Izod Impact strength notched, FDM HISO 180
print settingsFDM H column (the sheet does not say what H is)
not in the median: set apart (never used to pass), no stated orientation
Izod impact strength orientation not stated2 kJ/m²p. 1: Izod Impact strength notched, InjectionISO 180
print settingsInjection column
not in the median: measured on a moulded bar
Izod impact strength orientation not stated41 kJ/m²p. 1: Izod Impact strength unnotched, FDM HISO 180
print settingsFDM H column (the sheet does not say what H is)
not in the median: unnotched
HDT at 1.8 MPa65 °Cp. 1: HDT A
ISO 75As the sheet prints it: HDT A ISO 75
not in the median: measured on a moulded bar
Density1,23 g/cm³p. 1: DensityISO 1183

Print settings

Nozzle
245–265 °Cown data sheet
Bed
75–95 °Cown data sheet
Heated chamber
not stated
Drying
60 °C for 3–6 hown data sheet
Hardened nozzle
not stated
Its print profile, in the documents' words
  • Nozzle 255°C ± 10; Bed 85°C ± 10; Drying Pre-dry material for 3-6 hours at 60°C (max.).Nobufil, Technical Datasheet PCTGp. 1: Recommended printing settings; p. 1: Drying note

Price

Not in the price sample.

Its 2 documents

What the maker says (1)

Not published by any product: tensile strength (Z).

Values are for the colour each sheet tested; pigment can change them.